as shown in fig1 is a flow chart of a typical prior art process for making osb . the flaker 10 forms the flakes , discharging the flakes via a take - away conveyor or drop chute 21 to the “ green ” or “ wet bin ” 20 . the discharge from the “ green ” or “ wet bin ” 20 to the dryer 30 can be via doffing rolls or drop chutes 22 . the dried flakes exiting dryer 30 can be stored in dry bin 40 or fed directly to blender 50 where they are mixed with other compounds , such as an adhesive 11 , wax 12 , catalyst 13 , etc . after mixing , the mixture is discharged to a forming bin 60 , fed by conveyors , such as forming belt 65 to a staging area 70 . from the staging areas 70 mats of particles , adhesive , water , and other components are fed to press 80 where they are treated , under heat and pressure , to consolidate the particles and cure the adhesive , typically a pf resin . we have found that the total application of resin , to the blender 50 as in the prior art , which inherently introduces water , in the form of the aqueous resin component , is deleterious to the formation of building panels for high value uses . after study , we have found that at least a portion of the adhesive can be applied to the lignocellulosic particles before the particles are dried . convenient sites for application are shown in fig2 - 3 . for example , in fig2 the flakes being discharged from flaker 10 can have resin applied as they exit the flaker via a take - away conveyor or drop chute 21 . resin application 14 can be by spray nozzles ( air assisted or non - air assisted ) ( not shown ) or through a conventional spinner disc atomizer ( not shown ). other methods of applying resin such as falling curtain may be employed so long as the choice of application ensures that the desired amount of resin is applied uniformly to the flakes . dilution of the resin optimizes resin distribution . it is typical in the wood industry to run resins from 100 % solids ( powder resole resins ) to 15 % diluted resin solids . there is significant data to show that powder resins provide excellent distribution when compared to the liquid resins . this application rate at resin application 14 can be 0 % ( as in the conventional process ) to about 30 wt %. however , typical resin application of pf resins can result in at least one of several types of deleterious emissions . either formaldehyde , ammonia or no x , or each , can be emitted during such a process during one or both of the drying or pressing steps of the process necessary to transition a mixture of particles and adhesive into a consolidated mat of parties bonded by an adhesive . even when an additional or alternative resin application is performed upon exit of the green flakes from green or wet bin 20 , there can be the deleterious emission of ammonia , or no x gases upon passage through an rto or other emissions burner . the discharge of green or wet bin 20 is usually via doffing rolls and drop chutes 22 . application of a resin 15 can conveniently be applied at this point . the application points in the present invention can be varied based on several factors of the process design , including chute design , wood flow over doffing rolls , distance and space availability for the application hardware , etc . the amount applied at application of resin 15 can be the same or different from that applied at other locations in the process , e . g ., to that applied at 14 . the type of resin applied can also vary , e . g ., powder at 14 , aqueous solution at 15 ( or 11 ). in the alternative embodiment of fig3 resin application may commence as early as in the hot pond 105 , or treatment vat 106 by addition of resin into these areas . alternatively , resin may be applied as the logs are transported from wood yard 107 to flaker 10 , or to hot pond 105 . alternatively , logs can be sent from the wood yard 107 to special treatment vat 106 for resin application before being fed to flaker 10 . in another alternative , after thawing the logs in hot pond 105 , the logs may be sent to treatment vat 106 ( via the route shown in dotted line 108 in fig3 ) for resin application . although we have specifically illustrated resin application at one or more points prior to drying , it would be within the skill of the worker in the art , upon reading the disclosure of the invention , to apply resin prior to , during or after flaking , in the green or wet bin , or in multiple points along the process in order to provide the required resin . still further , it is possible to supplement the present process of resin application after the dryer , by providing additional resin prior to the drier according to the invention . we have found a way in which the emission of free formaldehyde , ammonia and / or no x can be reduced whether the resin , used as an adhesive , is applied prior to the drier , subsequent to the drier , but before the pressing step and / or both prior to the drier and subsequent to the drier , but prior to the pressing step . our discovery lies in our recognition that the prior art processes , during curing of the pf resin , produced an ammonia emission , due to the presence of urea , usually added subsequent to formation of the pf resin , as a component of the adhesive which was thought to eliminate free - formaldehyde emissions . the presence of free urea , added to a pf resin , has been found to release ammonia in both the drying step , as well as in the pressing step when used in prior art processes when resin is added after the drying , but before the pressing step ; before the drying step or when resin is added both before and after the drying step . we have found that by adding urea to a pf resin , followed by the addition of formaldehyde , forming methyol urea , which , when used in the present process , is less likely to give ammonia ( or no x if emissions are fed to an rto or other burner ) than a pf resin to which urea alone has been added . the presence of methyol urea , with a pf resin , can then be used as the adhesive which is added before the drying step , after drying , but before pressing , or both , without creating an emission of free - formaldehyde as well as reducing the emission of ammonia ( or no x ) in either the drying or pressing steps . the total amount of resin in the final product includes that added prior to the drier , e . g ., at the hot pond 105 , and / or treatment vat 106 , in the flaker 10 and / or green or wet bin 20 , resin application 14 , application of resin 15 and adhesive 11 , and can be adjusted so that the new building panels made by the process of the invention maintains the current commodity board densities of 37 to 43 lb / ft 3 . however , it is possible to increase the total resin content by the present invention to exceed those densities without introducing excessive moisture into the blended particles or increasing formaldehyde , ammonia or no x emissions . current cure times can be maintained even with higher resin contents so that production rates and volumes are not hampered . while press temperatures between 300 ° and 460 ° f . can be used , desired targets are still between 380 ° and 430 ° f .. the lower press temperatures generally do not allow for good mat consolidation and heat transfer within the mat as it is being pressed . however , it is also possible to combine the prior art steps of preheating the mats before pressing with the resin addition prior to heating of the flakes , which occurs prior to mat formation . generally , temperatures exceeding 430 ° f . present a fire hazard in the current mill environments . in other embodiments according to the invention , the application of the resin prior to the drying makes it possible to eliminate the blending system completely . this is shown by the dotted line in fig2 - 3 . industrialization according to the alternative embodiment could save significant capital and maintenance costs associated with installation and upkeep of the current blending systems . in another alternative , it is also possible to move the blender 50 and its associated adhesive 11 , wax 12 and / or catalyst 13 , to a point upstream of the drier , e . g ., between the flaker 10 and the green or wet bin 20 or , alternatively , after the green or wet bin 20 , but before dryer 30 . it is also possible to eliminate the wax 12 from the process altogether . it is apparent that such elimination would achieve significant savings and , furthermore , board density could be reduced to a lower spectrum of from about 28 to about 32 lb / ft 3 . while we have described the particles as lignocellulosic , we do not envision that the form of particles is limited to strands as it is equally suitable for particles in the form of long or short fibers , flakes , chips and / or combinations thereof with veneers . the methods of the invention are suitable over a wide range of wood species and are suitable for all woods currently in use in the panel making industry . resin optimization could be achieved by changing molecular weight ( wt . avg . mw ), viscosity , and resin solids content . catalysts , both internal and external , can be applied at various times , e . g ., resin can be applied before dryer , but catalyst could be applied at blender and vice versa . suitable adhesives , as substitutes for , or in addition to , the phenol formaldehyde previously mentioned could include other thermosetting resins , so long as reduced ammonia and / or no x emissions are achieved . when the lignocellulose particles are in the form of strands , the strands may be up to 12 inches in length and may be oriented to form oriented strandboard ( osb ). other products which may be manufactured according to the invention include high density fiberboard ( hdf ), medium density fiberboard ( mdf ), chipboard , laminated veneer lumber ( lvl ) and plywood . although we have described a “ flaker ” to process the logs into smaller pieces , the use of a “ peeler ” to form discrete layers or plys useful in manufacturing plywood or composite products , such as laminated veneer lumber ( lvl ) can be substituted for flaker 10 and are within the scope of the invention . in all cases , the resin to be applied to the lignocellulose is applied before the lignocellulose is dried , such as before the drier , after , or in , the green or wet bin , between the green or wet bin and flaker or peeler , at the exit of the flaker or peeler , and even in the hot pond , or treatment vat for treating logs ( either debarked or whole ), with a preliminary application of resin . though less effective than applying the resin to lignocellulose whose surface area has already been increased ( e . g ., by flaking or peeling ), the invention is applicable to all phases of board preparation , provided that at least some resin is applied upstream of the drier , or when applied at more than one location is applied at least before the step of applying heat and pressure to a mass of particles and adhesive . the invention has applicability to all known board manufacturing processes , including those using heated press platens , steam injection , catalyst injection , microwave or radio frequency ( rf ), heating and continuous and semi - batch pressing operations . the invention is further explained by reference to the following examples . boards were made according to the specifications of table 1 and tested for properties . the following data demonstrate the effect of post addition of formaldehyde to a pf resin to which urea has been added on the ammonia emissions when the resulting adhesive was subjected to a temperature increase . wherein mr is the “ molar ratio ” and the units of “% xe - 3 ″ are representative of the value , e . g ., 2 . 9 × 10 − 3 or 0 . 0029 %. sample number 5 is a control with no formaldehyde added to the pf resin to which urea has been added . we have also evaluated the effect of delayed pressing on resin applied to lignocellulosic particles . such a delay in pressing can occur due to mechanical breakdown of one or more components of the manufacturing process , e . g ., a breakdown of the conveying system on the press . in such cases , the resin and particles may be in contact for an extended period , e . g ., up to three days , as over a weekend when the breakdown occurred friday and production did not recommence until the following monday . the following examples simulate what may happen if pre - treatment resin was applied to furnish , then dried and the plant shut down for several days before that furnish was utilized . combinations of a pretreat resin and traditional blender resin are also shown . 1 - 23 / 32nd , 38 pcfosb boardwas made per condition using re - humidifed aspen furnish (˜ 35 % mc ). press cycle of 300 seconds , button to button was used on all boards . cascophen ew - 45lv wax emulsion was applied to all surface layers at 1 . 7 % and all core layers at 1 . 0 % based on solids . boards 1 and 2 were pre - treated with an adhesive according to the invention only ( 12 and 8 % respectively ), then dried and allowed to sit for three days in a sealed container . these flakes were then treated with the specified amount of surface and core wax in the blender and then formed and pressed . the remaining boards were subjected to the same as above , with the exception that after the three day waiting period they were treated in the blender with additional resin and wax , then formed and pressed into board . table 3 summaries the treatment . [ 0059 ] table 3 % blender % blender % blender % blender board # % pre - treat face resin core resin face wax core wax 1 12 0 0 1 . 7 1 . 0 2 8 0 0 1 . 7 1 . 0 3 12 4 4 1 . 7 1 . 0 4 8 4 4 1 . 7 1 . 0 5 6 4 4 1 . 7 1 . 0 6 4 5 5 1 . 7 1 . 0 7 6 2 2 1 . 7 1 . 0 8 4 2 2 1 . 7 1 . 0 [ 0060 ] table 4 all data % 24 hr . % pre - treat blender non - oriented % % % board pd - 112 resin resin ib mor moe ei mm wa ts cs 1 12 0 *** *** *** *** *** *** *** *** 2 8 0 2 . 9 1 , 076 341 , 109 125 , 975 1 , 108 36 . 9 23 . 3 18 . 1 3 12 4 42 . 9 4 , 142 596 , 782 211 , 092 4 , 141 27 . 0 5 . 9 3 . 9 4 8 4 46 . 1 3 , 385 515 , 605 192 , 899 3 , 516 27 . 9 8 . 0 4 . 6 5 6 4 40 . 1 3 , 173 543 , 842 185 , 644 3 , 101 26 . 3 6 . 6 3 . 0 6 4 4 21 . 1 3 , 909 622 , 372 215 , 654 3 , 853 32 . 3 9 . 3 5 . 1 7 6 2 32 . 6 3 , 940 558 , 222 195 , 356 3 , 914 38 . 8 13 . 1 5 . 1 8 4 2 22 . 0 2 , 688 478 , 181 178 , 429 2 , 785 72 . 2 31 . 5 28 . 2 as is apparent from the foregoing , the multi - resin addition both prior to and subsequent to drying achieves acceptable quality even if the plant is subject to unanticipated shutdown for three days . although we have described our invention in relation to specific embodiments , it will be apparent that our invention is not limited and may be capable of modification by those skilled in the art without departing from the scope of the appended claims .