the present invention provides a new agglomerating agent for use in heap leaching of ores . it has been discovered that a moderate or high molecular weight polymer such as an acrylamide / acrylic acid provides effective agglomerating action in mining operations . the polymers of the present invention may be employed singly or in combination with cement or other agglomerating agents . when employed singly , the polymers of the present invention were found to provide effective agglomeration of ores containing excessive quantities of clays and / or fines . the polymer agglomerating agents of the present invention were also found to be effective when employed in combination with cement . to allow comparison of the efficiency of the agglomerating agents of the present invention when applied to different ores , a standardized testing procedure was developed . this procedure allows the efficiency of the various agglomerating agents to be compared . the procedure measures the percolation rate of a predetermined volume of a leachate solution through a column of agglomerated ore . the procedure uses water stability to measure the strength of the agglomerated ores . the procedures take into account the fact that poorly stabilized agglomerates swell , fracture and disintegrate upon contact with water to release a large number of fines . the slime mud which forms as a consequence of agglomerate degradation retards the percolation rate of the leach solution through the agglomerated ore . the - test procedure is designated to take into account effects such as variable surface area that are associated with raw crushed ore . the preferred agglomeration agent of the present invention is an anionic copolymer of acrylamide and acrylic acid . it is believed that comparable or better performance would be achieved if the copolymer solution were applied as a foam wherein copolymer distribution would be improved . it was discovered that with the preferred anionic copolymer agglomerating agent , efficiency was somewhat influenced by the composition of the ore to be treated . a comparison of fig1 and 2 shows that the selection of the most efficient copolymer will be , in part , dependent upon the ore to be treated . fig1 summarizes data relative to the agglomeration effect of prior art cement and acrylamide / acrylic acid copolymers of varying monomer ratio and molecular weights . the data summarized in fig1 relates to a clay containing ore , designated ore a . fig2 summarizes data collected in the testing of prior art cement and acrylamide / acrylic acid copolymers of varying monomer ratio and molecular weight for another clay containing gold ore , designated ore b . as can be seen from fig1 for the ore a , the most effective agglomerating agent , as evidenced by the high percolation rate , is an anionic , high molecular weight , 70 / 30 acrylamide / acrylic acid copolymer . as shown in table 1 , these agglomerating agents are particularly effective when used in combination with cement . table 1______________________________________effect of anionic acrylamide / acrylic acid copolymers on thepercolation rate of cement stabilized ore &# 34 ; a &# 34 ; agglomerates . in these tests , ore &# 34 ; a &# 34 ; agglomerates were stabilized withcement at 5 pounds / ton . application percolation rate rate moleculartreatment ( pounds / ton ) ( ml / min ) weight______________________________________cement 5 119 -- cement 10 217 -- cement 20 500 -- 70 / 30 am / aa * 1 . 0 455 12 - 16 × 10 . sup . 670 / 30 am / aa 1 . 0 455 2 - 4 × 10 . sup . 690 / 10 am / aa 1 . 0 500 12 - 16 × 10 . sup . 6______________________________________ * 70 / 30 am / am refers to a 70 / 30 mole ratio copolymer of acrylamide ( am ) an acrylic acid . 90 / 10 am / aa is a 90 / 10 mole ratio of acrylamide to acrylic acid . from fig2 or ore b , it can be seen that the most effective agglomerating agent was an anionic , high molecular weight , 90 / 10 acrylamide / acrylic acid copolymer . as can be seen from the figures , the efficiency of the agglomerating agent in the present invention can be maximized by varying the ratio of monomers in the copolymer , the molecular weight of the copolymer and the treatment rate . the fact that the copolymer used for ore a did not provide optimum percolation rates for ore b underscores the fact that the copolymer mole ratio and molecular weight selected for a given application will to a large extent depend on the nature of the ore body . fig3 summarize the data relative to the effectiveness of the agglomerating agents of the present invention on ore b when used in combination with cement . the results summarized in tables 2 and 3 further illustrate the effectiveness of the medium and high molecular weight 70 / 30 and 90 / 10 mole percent acrylamide / acrylic acid copolymers relative to cement as agglomerating agents . as shown in table 2 , portland cement was of little value in enhancing the percolation rate of ore c , a high clay content ore . in the case of ore c , cement at 20 #/ ton appeared to have a negative impact on percolation rate . for ore c , lime was not an effective agglomerating agent . when ore c was treated with the acrylamide / acrylic acid copolymers of the prevent invention , significant improvements in the percolation rate values were realized . as shown , the percolation rate of ore c increased from 134 ml / min when treated with cement at 10 #/ ton to 417 ml / min when treated with a high molecular weight 70 / 30 mole percent acrylamide / acrylic acid copolymer at 0 . 5 #/ ton . as shown in table 3 , these polymers may be used in combination with cement . table 2______________________________________effect of anionic acrylamide / acrylic acid copolymerson the percolation rate of ore sample c average application percolation rate rate moleculartreatment ( pounds / ton ) ( ml / min ) weight______________________________________control -- 24 -- cement 5 30 -- cement 10 134 -- cement 20 34 -- lime 5 6 -- lime 10 3 -- lime 20 3 -- 70 / 30 am / aa * 0 . 5 417 12 - 16 × 10 . sup . 6 1 . 0 332 12 - 16 × 10 . sup . 6 2 . 0 401 12 - 16 × 10 . sup . 670 / 30 am / aa * 0 . 5 333 2 - 4 × 10 . sup . 6 1 . 0 361 2 - 4 × 10 . sup . 6 2 . 0 356 2 - 4 × 10 . sup . 690 / 10 am / aa * 0 . 5 385 12 - 16 × 10 . sup . 6 1 . 0 361 12 - 16 × 10 . sup . 6 2 . 0 359 12 - 16 × 10 . sup . 6______________________________________ * 70 / 30 am / aa is a 70 / 30 mole percent acrylamide ( am )/ acrylic acid ( aa ) copolymer . 90 / 10 am / aa is a 90 / 10 mole percent acrylamide / acrylic acid copolymer . table 3______________________________________effect of anionic acrylamide / acrylic acid copolymers on thepercolation rate of cement stabilized ore &# 34 ; c &# 34 ; agglomerates . in these tests ore &# 34 ; c &# 34 ; agglomerates were stabilized withcement at 5 pounds / ton application percolation rate rate moleculartreatment ( pounds / ton ) ( ml / min ) weight______________________________________90 / 10 am / aa 1 . 0 test 1 96 12 - 16 × 10 . sup . 6 2 200 3 119 2 . 0 test 1 333 2 17970 / 30 am / aa 1 . 0 test 1 278 12 - 16 × 10 . sup . 6 2 250 3 385 2 . 0 test 1 385 2 33370 / 30 am / aa 1 . 0 test 1 333 2 - 4 × 10 . sup . 6 2 278 3 333 2 . 0 test 1 294 2 417______________________________________ the anionic medium ( i . e ., about 2 million ) and high ( i . e ., 12 - 16 million ) molecular weight 70 / 30 and 90 / 10 mole percent acrylamide / acrylic acid copolymers reported above are only illustrative of the type of polymer systems necessary for optimum effectiveness . in practice it is believed that 90 / 10 to 60 / 40 mole ratio acrylamide / acrylic acid copolymers with molecular weights between 1 and 16 million would be effective . of course , derivatives of these copolymers could also be effective . the preferred agglomerating agent of the present invention is a copolymer of acrylamide and acrylic acid . the mole ratio of acrylamide to acrylic acid can vary from about 90 to 10 to about 60 to 40 . the preferred copolymer has a moderate to high molecular weight , that is from about one million up to above 8 million . the copolymer is preferably anionic , although it is believed that the presence of some cationic segments in the copolymer would not adversely affect the agglomeration action . the most preferred agglomerating agent of the present invention is an anionic copolymer of acrylamide and acrylic acid with a monomer ratio of about 70 to 30 mole percent and having a molecular weight of above 8 million . typical treatment rates for the anionic / moderate to high molecular weight copolymer of the present invention range from about 0 . 125 up to about 2 . 0 pounds per ton of ore . when used in combination with cement , typical treatment rates are about 1 pound polymer and 5 pounds of cement per ton of ore . typical prior art treatment rates for cement are from 10 to 20 pounds per ton . thus , the copolymer of the present invention provides for effective agglomeration at greatly reduced treatment rates . while the present invention has been described with respect to particular embodiments thereof , it is apparent that numerous other forms and modifications of this invention will be obvious to those skilled in the art . the appended claims and this invention generally should be construed to cover all such obvious forms and modifications which are within the true spirit and scope of the present invention .