the present invention includes two layers , an upper indicia bearing layer and a lower adhesive layer . the upper indicia bearing layer can be formed from a variety of different heat resistant materials which are not destroyed at application temperatures . the upper layer generally remains solid at the softening temperature of the adhesive layer . although a thermoplastic urethane which melts at application temperature but is not destroyed can be used . preferably the upper layer is a thermoplastic urethane , thermoset plastic material , flock , or woven material such as twill edge sewn letters ( with or without a pvc layer ), puff ink and embroideries . a thermoset plastic is a resin which in its final state is substantially infusible and insoluble . thermosetting resins often liquid at some state in their manufacture or process are cured by heat catalysis or other chemical means . after being fully cured , thermosets cannot be resoftened by heat . thermosets include those plastics which are normally thermoplastic but which are made thermosetting by means of cross - linking with other materials such as cross - linked polyolefins . suitable thermoset upper layers include polyamides , thermoset polyurethanes , thermoset polyolefins , thermoset polyepoxides and thermoset polyesters . a preferred thermoset is a thermoset polyurethane ink such as zephrylon pigmented polyurethanes sold by sinclair and valentine chemical coatings group of wheelabrator - frye , inc . of north kansas city , mo . this is disclosed more fully in mahn u . s . pat . no . 4 , 610 , 904 . further the upper indicia bearing layer may be a vinyl plastisol such as disclosed in the liebe jr . u . s . pat . no . 3 , 660 , 212 patent or a flock material such as disclosed in the mahn u . s . pat . no . 4 , 390 , 387 . a suitable thermoplastic polyurethane is disclosed in mahn u . s . pat . no . 4 , 269 , 885 . further the upper indicia bearing layer can be a woven material for example cotton . other non - woven webs can be used as indicia bearing layer presuming they are not destroyed at application temperatures as described below . twill such as edge sewn twill letters can be the upper indicia bearing layer . also embroidered letters are suitable . the adhesive layer is a thermosettable film of a linear saturated polyester polymer which includes a heat activated curing agent . the uncured polyester itself is a linear alkyl unsaturated polyester formed by reacting a glycol with a diacid . the molecular weight of the uncured polyester polymer must be low enough to flow and wet the surface of the nylon at application temperature , i . e ., generally about less than 450 ° f . preferably it should be from about 5 to 30 , 000 and most preferably about 10 to 15 , 000 . the polyester adhesive should include a heat activated curing agent and preferably a heat activated polyisocyanate curing agent . specifically suitable diols include ethylene glycol , propylene glycol , 1 , 3 - propane diol , 1 , 4 - butane diol , 1 , 5 - pentane diol , 1 , 6 - hexane diol , 1 , 8 - octane diol , 1 , 4 - cyclohexanedimethanol , 1 , 3 - cvclohexanedimethanol , diethylene glycol and the like . useful diacids for making these polyesters would include aromatic dicarboxylic acids having no vinyl saturation such as isophthalic acid or anhydride , phthalic acid or anhydride , terphthalic acid or anhydride or aliphatic dicarboxylic acids such as adipic acid , succinic acid , gluteric acid and the like . the heat activated curing agent must act to cure the polyester upon heating . it should be a heat activated curing agent since these ornamentals must have a shelf life of several months . the heat activated curing agent can be an isocyanate curing agent preferably a blocked isocyanate curing agent . suitable such curing agents include phenol blocked methylene bis - 4 - phenylisocyanate such as those disclosed in u . s . pat . no . 3 , 307 , 966 and phenolaldehyde blocked polyisocyanates such as those discussed in u . s . pat . no . 3 , 226 , 276 . other blocked isocyanates include dimerized toluene diisocyanates and methyl - ethyl - ketoxime blocked polyisocyanates . methods of forming such polyesters are well known and are disclosed in u . s . pat . nos . 4 , 350 , 807 , 3 , 898 , 358 , 4 , 606 , 785 and 4 , 215 , 516 . a preferred adhesive for use in the present invention is bostik adhesive 10 - 300 - 3 which is a thermosetting linear saturated polyester adhesive using an isocyanate curing agent and a polyester formed from ethylene glycol and methylterphthalic acid . this is dissolved in methylethyl ketone and methylene chloride and this has a weight average molecular weight of 10 - 15 , 000 . ornamental transfers can be made in various manners as described hereinafter . as shown in fig1 the ornamental transfer 11 will include the lower polyester layer 12 laminated to the upper layer 13 . an optional release layer 14 is included adjacent the polyester layer . to form this transfer , the polyester adhesive dissolved in a solvent is coated onto the release layer 14 and dried at from about 250 °- 325 ° f . ( 121 °- 163 ° c .). the upper layer 13 is then film coated onto the polyester layer 12 . if the upper layer is a moisture cure polyurethane , the polyurethane is coated onto the solidified polyester layer 12 . if the upper layer is thermoplastic , it can be formed into a film and laminated onto the polyester layer 12 before it &# 39 ; s solvent completely evaporates . the two films can also be laminated together under slight heat and pressure . as shown in fig3 it is also desirable in certain situations to use an intermediate layer . in this embodiment the polyester layer 15 is coated onto a release layer 16 and the solvent evaporated . a pvc layer 17 can be bonded intermediate the polyester layer 15 and an upper layer 18 which for example can be twill or other cloth or even flock . again , the layers are laminated together under slight heat and pressure . an ornamental decorative can also be made according to the method described in u . s . patent application ser . no . 041 , 866 filed apr . 22 , 1987 wherein the release sheet 21 is coated with the polyester layer 22 where the polyester layer is a continuous layer . a discontinuous indicia bearing layer such as a discrete letter 23 is then coated onto the polyester layer 22 . this is applied to a substrate using blotting paper . in these applications , various coating methods can be used depending on the particular indicia bearing layer . preferably , the polyester adhesive is applied , dissolved in a solvent and allowed to dry at a temperature below its curing temperature to dry off the solvent forming a solid film . the film can also be extruded from solid pellets . the ornamental transfer is then applied to a substrate particularly nylon by placing the polyester layer against the nylon layer , applying heat and pressure against the ornamental transfer , melting the polyester layer and causing it to soak into or migrate towards the nylon . nylon is the generic name for long chain polyamides which have recurring amide groups as an integral part of the main polymer chain . generally nylon fabrics are nylon 6 / 6 which is made by condensing hexamethylenediamine with adipic acid . the application temperature should be above the cure temperature of the polyester ( i . e ., activation temperature of the curing agent ) generally above 325 ° f ., generally at around 350 - 400 ° f . at these temperatures , the polyester film melts and the curing agent is activated . pressure from the heat source forces the molten polyester to flow into the nylon . this is allowed to cool forming a weak bond with the nylon . the curing agent then acts to at least partially cure the polyester forming a firm bond to the polyester . when applied to nylon in this manner the decorative heat transfer remains adhered to the nylon for prolonged periods of time inspite of washing and other normal use . to compare the heat decorative transfer of the present invention with other heat decorative transfers , a heat transfer made according to the present invention was formed having a 3 mil thick film of the bostik - 10 - 300 - 3 adhesive . coated over this was one mil of thermoset polyurethane ink made by zephrylon . this was applied to a piece of nylon fabric at a temperature of 350 ° f . for 5 seconds ( about 5 psi ) and allowed to set over a period of 24 hours . after 24 hours , the peel strength of the transfer onto the nylon fabric was 10 - 14 pounds per square inch . a heat decorative transfer made according to the method disclosed in u . s . pat . no . 4 , 269 , 885 having a polyurethane thermoplastic upper layer and a thermoplastic polyester lower layer was applied to nylon at 350 ° f . at 6 seconds and allowed to set . its peel strength was less than one pound per square inch . in both of these tests , the nylon was substantially the same and can be described as follows : tightly woven nylon , 150 warp and weave , 2 denier which is typically used for outerwear ( windbreakers ). thus , when using a decorative heat transfer according to the present invention , one obtains a very substantial bond between nylon and an indicia bearing layer . the bond strength , 10 - 14 pounds per square inch , is considered excellent . thus , the present invention provides the first heat activated decorative transfer which can be applied to nylon . due to the fact that the polyester adhesive can be laminated to a wide variety of different thermoplastic and thermoset materials as well as woven and nonwoven webs made from a variety of different materials including polyesters , cotton and other natural fabrics and wool , this can be used for a wide variety of different applications and provide substantial cost savings and eliminating the need to sew many indicia bearing transfers onto nylon jackets . heat activated transfer of the present invention can be used for many applications such as nylon including highly sized garments such as lycra brand nylon and even clean room garments which are 100 % polyester having interwoven carbon fibers to prevent static . the preceding has been a description of the preferred embodiment of the present invention along with the best mode of practicing the invention known at this time . however , the present invention is limited only by the pendent claims wherein we claim :