referring now to fig1 through 6 , a semiconductor device made in accordance with the present invention is shown in a preliminary fabrication stage in fig1 wherein the first masking and oxide etching stage has been employed to form the desired openings 11 in the silicon oxide layer 12 formed on the n substrate 13 of the body , the p - regions 14 being diffused into the n substrate 13 through said openings in well known manner . after the diffusion of the various p - regions 14 , the silicon oxide layer 12 is stripped from the surface and thereafter a thin silicon oxide gate layer 15 , for example 1 , 000 angstroms , is formed over the entire surface . this layer is then followed by the growth by standard techniques of a thin silicon nitride ( si 3 n 4 ) mask layer 16 on the oxide layer 15 , this silicon nitride layer 16 being about 1000 - 2000 a thick . a second mask is then used to define the p + diffusion regions , i . e ., the p + source and drain regions 17 , 17 &# 39 ; for the p channel devices and the p + guard rings 18 for the n channel regions to be subsequently formed in the p - regions 14 . openings in the silicon nitride layer 16 and the silicon oxide layer 15 are then formed by conventional etching to expose these p + regions . a p + diffusion then takes place to form the p + regions 17 , 17 &# 39 ;, 18 during which diffusion the thick silicon oxide layer 19 is formed over these p + regions ( see fig2 ). thereafter a third masking step , subsequent silicon nitride etch and silicon oxide etch , and n + diffusion are utilized to form the n + diffusion regions 21 , 21 &# 39 ;, 22 in the n substrate 13 . during the diffusion a thick thermal oxide 23 forms over these regions . this stage of fabrication is shown in fig3 . the n + regions 21 , 21 &# 39 ; form the n channel devices in the p - regions 14 and the n + regions 22 form isolation rings around the various p channel regions . it should be understood that the p + and n + guard rings 18 and 22 are not necessary in all cases in the formation of p channel and n channel devices utilizing the present invention . a fourth masking step is then employed to define the contact openings 24 through the thick silicon oxide layers 19 and 22 to the p + and n + source and drain regions 17 , 17 &# 39 ; and 21 , 21 &# 39 ; and a silicon oxide etch follows to remove the oxide at openings 24 ( see fig4 ). a fifth masking step is then provided to protect all areas on the surface except the gate regions of the p channel 17 , 17 &# 39 ; and n channel 21 , 21 &# 39 ; devices . a silicon oxide etch is then used to remove any oxide film that may be on the si 3 n 4 layers at the gate region of the channels . this is followed by etching away the si 3 n 4 layer 16 at the gate regions of the p + channel and n + channel devices ( see fig5 ). a sixth mask is then formed over the surface of the device to define the metal contact 25 for the various source and drain regions and the gate electrodes 26 for the channel regions ( see fig6 ). due to the utilization of the silicon nitride mask layer 16 in the gate regions during the diffusion of the source and drain regions 17 , 17 &# 39 ;, 21 , 21 &# 39 ; in both the n channel devices and the p channel devices , the gate regions are self - aligned with regard to the edges of the diffused source and drain regions 17 , 17 &# 39 ;, 21 , 21 &# 39 ;. thus no parasitic capacitance is formed in these regions due to the fact that the metal of the gate electrode 26 is separated from the sourc and drain diffusion regions 17 , 17 &# 39 ;, 21 , 21 &# 39 ; by a thick oxide layer as opposed to an overlapping thin oxide gate layer as in the conventional cmos devices . also the silicon nitride layer 16 at the outer edges of the p + diffusion regions 17 , 17 &# 39 ; and the n + diffusion regions 21 , 21 &# 39 ; acts as one boundary of the mask for the contact openings 24 to be made in the thick oxide metal films 19 and 23 . thus , although the contact opening mask may extend beyond the edges of the regions 17 , 17 &# 39 ; and 21 , 21 &# 39 ; due to misalignment or the like , the silicon nitride layer 16 acts as an effective etch defining mask for the contact opening . as a result , larger size cmos structures can be limited in their overall area . this novel fabrication technique uses a processing which is compatible with standard metal gate cmos technology . it utilizes the same number of masking steps , but the process steps for the p + and n + diffusions are less critical , and higher density devices are produced . it should be noted that the particular conductivity for the substrate 13 and regions 21 , 21 &# 39 ; is chosen as n type and the conductivity for the regions 14 and 17 , 17 &# 39 ; is chosen as p type . devices with the opposite conductivity for these regions may be fabricated by the novel process described above . referring now to fig7 through 11 a novel technique is disclosed wherein the self - aligning gate technique of the present invention is employed for the formation of p channel and n channel gate devices on an insulating substrate , this novel technique employing only five masking steps in the fabrication process . in accordance with standard insulating substrate techniques , a one - half to one micron thick n layer 31 in the form of single crystal silicon is grown on the insulating substrate 32 which may be , for example , sapphire or spinel . a thin silicon oxide gate layer 33 , for example 1000 a thick , is grown on the surface of the n silicon and a thin , for example 1000 - 2000 a thick , silicon nitride layer 34 is grown over the oxide layer . a first masking step followed by a silicon nitride etch and a silicon oxide etch is used to open the surface layers to the p + diffusion regions and the p + regions 35 are formed therein by diffusion . during the diffusion step , a thick silicon oxide layer 36 forms over these regions . the gate regions between the source and drain p + diffusion regions 35 are then protected by a photoresist mask 37 , this mask 37 and the silicon nitride layer 34 over the remainder of the surface of the device protecting the silicon oxide at all regions except where openings 38 are desired in the silicon oxide and in the underlying n silicon layer forming isolation regions between the p channel devices and the n channel devices . thereafter a well known p - ion implantation step is utilized to form p - channel region 39 between the source and drain region areas of the to be formed n channel devices . an oxide etch followed by a silicon etch is then utilized to remove the portion of the silicon oxide layer 36 and the silicon layer 31 in regions 38 . the photoresist 37 protects the p channel devices on the substrate 32 during etching while the silicon nitride layer 34 protects the n channel regions on the substrate 32 . a thermal oxide is then grown over the substrate to cover the edges 41 of the p channel regions and the n channel regions . a third mask is then formed to define the n + diffusion regions 42 and the silicon nitride layer and underlying silicon oxide layer are etched away from these regions , the n + diffusion then taking place to form the n + source and drain regions 42 in the n channel devices ( fig1 ). during this n + diffusion a thick thermal oxide layer 43 is grown over the n + regions . a fourth mask is then formed over the device to define the openings in the thick oxide layers 36 and 43 leading to the various p + and n + source and drain regions and an oxide etch produces these openings . then a silicon nitride etch , such as a hot phosphoric etchant , is used to etch away the silicon nitride layer 34 remaining at the gate regions . the fifth masking step is then employed to define the metallization regions where the metal contacts 44 are formed with the various source and drain regions and the gate electrodes 45 are formed at the gate regions . it is noted that in this embodiment the silicon nitride layer 34 acts as a mask for the self - aligning gate in the p and n channel devices . in addition , a portion of the silicon nitride layer also serves to define the isolation regions 38 made in the grown silicon layer 31 between the n channel devices and the p channel devices . this novel process uses standard cmos fabrication techniques while providing self - aligned gate devices with a five mask process . the standard non - self - aligned cmos technique used to form devices on insulated substrates heretofore utilized seven masking steps in the processing ; thus the present invention contributes a saving in the number of masking steps required . when the process described in fig1 - 6 above is employed , at the end of the process all the undiffused regions are protected with a layer of silicon nitride 16 over thin gate oxide 15 except at the gate regions of the devices . sometimes this is an undesirable configuration , because of the low field inversion voltage of the layer of silicon nitride over gate oxide . this problem can be eliminated by modifying the process flow described above for fig1 - 6 in the following manner as shown in fig1 - 15 . the first operation is the growth of a thin gate oxide layer 15 followed by a silicon nitride deposition layer 16 . with the first mask the silicon nitride 16 and oxide 15 are removed in all the regions where no diffusions are wanted at the end of the process , and are therefore left where source , drain , gate regions and guard rings are wanted ( see fig1 ). during the second masking operation , a negative photoresist 51 is deposited and exposed in such a way that , after development , the photoresist is left only outside the regions when an n channel transistor will be formed . by means of the well known ion implantation process , a controlled amount of boron atoms 52 are introduced into the silicon at the n channel transistor region to form a shallow layer 14 &# 39 ; ( fig1 ); the photoresist 51 where present prevents the boron atoms from reaching the silicon substrate 13 . the implanted boron atoms are then driven in to form the p - region 14 and at the end of this diffusion step a thick thermal oxide 53 is grown selectively in the regions not protected by the silicon nitride layer 16 ( fig1 ). the third masking and etching step removes the silicon nitride 16 and gate oxide 15 from the p channel source and drain regions 17 , 17 &# 39 ; and guard region 18 and the p + diffusion is performed . the fourth masking step opens the n channel source and drain regions 21 , 21 &# 39 ; and guard region 22 after which the n + diffusion is performed ( fig1 ). the silicon nitride 16 is then removed at the gate regions with a selective etch of phosphoric acid . the fifth masking operation is used to form contact openings to the source and drain regions and , after metallization , the sixth mask defines the metal interconnect pattern 25 , 26 ( fig1 ). when this process is used , the self - aligning nature of the formation of the gate regions is retained and also the contact openings to the source and drain regions are limited to the edges of such regions because the initial oxide grown outside the diffused regions can be made easily at least two times thicker than the oxide grown during n + and p + diffusions . it is well known that if a cmos circuit is operated with a low supply voltage ( e . g ., below 5 volts ), the p + and n + guard rings can be used in direct contact to the source - drain diffusion edges and no undiffused spacing has to be left between the guard rings themselves . the present invention can be applied to fabricate such circuits as shown in fig1 - 19 inclusive with the significant advantage that only five masking steps are now needed and the self - aligned nature of the gate formation is retained . as shown in fig1 , after formation of gate oxidation layer 15 and nitride deposition layer 16 , the n + source and drain regions 21 , 21 &# 39 ; are defined with the first masking operation together with the n + guard ring region 22 around the p channel transistor and the silicon nitride etched at these regions . during the second masking operation photoresist 51 is used to mask the thin layer 14 &# 39 ; of implanted boron atoms 52 outside the n channel transistor area and the step of ion implantation is carried out of allowed by resist removal . after drive in of the shallow implanted boron layer to form region 14 , the thin gate oxide 15 is removed wherever it is exposed and the n + diffusion 21 , 21 &# 39 ; and 22 performed ( fig1 ). the third mask is then used to remove the nitride and gate oxide from the p + region 17 , 17 &# 39 ; and 18 . after p + diffusion ( fig1 ), the nitride 16 left on the gate areas in then selectively removed . contact holes to the source - drain regions are opened with the fourth masking operation . metallization takes place and then the fifth mask is then used to define the metal pattern ( fig1 ). again , since the oxide grown after n + diffusion can be made much thicker than the gate oxide , the third mask openings can overlap the already diffused n + regions , but still the p + diffusion will be exactly coincident with the n + diffusion . for the three processes described in fig1 - 6 , 12 - 15 and 16 - 19 , a process variation can be introduced with considerable advantage for the alignment of the contact mask to the diffused regions and the metal mask to the gate regions . instead of defining the p + and n + source - drain regions with two separate masking steps , both regions may be defined with one masking operation in accordance with the well known method of diffusion from a doped oxide . after a layer of oxide heavily doped with phosphorus is deposited on the wafer surface with a subsequent mask , the doped oxide is removed from the p + regions . a p + predeposition is then performed , the doped oxide removed , and thermal oxide grown over the diffused regions .