the principles of the process of the present invention will be explained hereinbelow with reference to the preparation of closed - cage if nanoparticles of tis 2 . however , it should be understood that the discussion is not limited to that specific material but it applies to if metal chalcogenides in general . if nanoparticles of tis 2 were synthesized through the reaction of ticl 4 and h 2 s . the obtained nanoparticles have no or very small hollow core and they consist of 80 - 100 molecular sheets with quite a perfect spherical shape . the if nanoparticles were prepared by two reactor assemblies : a horizontal reactor and a vertical reactor . reference is made to fig1 exemplifying a preferred configuration of an apparatus , generally designated 10 , of the present invention suitable to be used for synthesis of if - nanoparticles with expected superior tribological behavior . the apparatus 10 includes a vertical reaction chamber 12 for mounting into an oven 15 , a separate evaporation chamber 14 , and a control unit 16 . an outlet 17 of the evaporation chamber 14 is connectable to an inlet in 1 of the reaction chamber 12 via a connecting gas - flow pipe ( not shown here ). in the present example , the oven 15 is designed as a two - zone oven , operable to control the temperature profile in the reaction chamber . the reaction chamber 12 has independent inlets in 1 and in 2 at opposite ends of the chamber 12 for inputting two reaction gases ( agents ), respectively , e . g ., ticl 4 and h 2 s , and a gas outlet go . flows of these reaction agents in opposite directions towards a reaction zone in the reaction chamber are assisted by inert gas , n 2 , and a mixture of ticl 4 and h 2 s gases is formed in the reacting zone . the control unit 16 includes , inter alia , a mass flow controller 16 a ( e . g ., tylan model fc260 commercially available from tylan general , usa ) operable for controlling the flow - rate of h 2 s , and a suitable flow controller 16 b for controlling the flow of additional gas to dilute the h 2 s by mixing it with a stream of inert gas or inert gas mixed with a reducing agent . further provided in the apparatus 10 is a filter 18 appropriately configured and accommodated to collect the product ( nanoparticles ). the filter 18 is preferably spatially separated from the inner walls of the reaction chamber 12 . the precursor ( ticl 4 ) vapors were prepared in advance in the separate evaporation chamber 14 . the latter includes a gas - washing bottle 14 a , a temperature source ( not shown here ) appropriately accommodated adjacent to the bottle 14 a and operable to controllably heat the ticl 4 liquid while in the bottle 14 a . valve arrangements 14 b and 14 c are provided to present a bypass for the nitrogen flow . this bypass provides a flow of clean nitrogen instead of one enriched with ticl 4 at certain moments of reaction . this improves the synthetic procedure since it prevents the flow of the highly reactive ticl 4 precursor during the heating up and cooling down steps of the synthesis . to this end , each valve is shiftable ( either by an operator or automatically ) between its position i ( used for flushing the apparatus with pure nitrogen gas ) and its position ii ( used for stopping the flush of the pure nitrogen gas ) during the reaction . the precursor ( ticl 4 ) vapor was carried from the evaporation chamber 14 to the reaction chamber 12 by an auxiliary gas flow . the carrier gas is inert gas , which can be mixed with a reducing agent ( h 2 or / and co ). the control unit 16 is configured for controlling the gas flows and the temperature sources &# 39 ; operation . the preheating temperature was found to be a very significant factor , determining the amount of precursor supplied to the reaction chamber 12 . the flow - rate of nitrogen through the bottle 14 a affects the stream of the titanium tetrachloride precursor as well . this two - chamber design apparatus with the vertical configuration of the reaction chamber considerably improves the size and shape control of the synthesized nanoparticles . the nucleation and growth mechanism established with the vertical reaction chamber ( fig1 ) provide nanoparticles with quite a perfect spherical shape ; small or no hollow core and many layers , which are ideally suited for alleviating friction and wear , as well as other different applications such as ultra strong nanocomposites , very selective and reactive catalysts , photovoltaic solar cells , etc . using similar reactions , the nucleation and growth mechanism is likely to provide many other kinds of if nanoparticles with expected superior tribological behavior . fig2 shows another example of an apparatus , generally at 100 . the apparatus 100 includes a horizontal reaction chamber 112 associated with a single - zone oven 115 , and a separate evaporation chamber 14 configured as described above . the reaction chamber 112 has an inlet arrangement in ( for inputting reaction agents ticl 4 and h 2 s ) and an outlet arrangement oa . a control unit 16 is used for controlling the operation of the oven 115 to thereby control the temperature profile in the reaction chamber 112 . the flow - rate of h 2 s , as well as that of n 2 , is appropriately controlled as described above . the ticl 4 vapors were obtained by preheating the liquid ticl 4 in a gas - washing bottle ( evaporation chamber ). the ticl 4 vapor is carried from the evaporation chamber 14 to the reaction chamber 112 by an auxiliary n 2 gas flow . the resulting product ( tis 2 powder ) is collected for analysis on the surface of the reaction chamber . preparation of if - tis 2 nanoparticles in the vertical reactor based apparatus of fig1 in order to maintain a water and oxygen free atmosphere , the reaction chamber 12 was permanently maintained at 500 ° c . and a flow of n 2 gas ( 20 ml / min ) until shortly before the run starts , when it is withdrawn from the oven 15 . at this point , the reaction chamber 12 was opened and cleaned . at the beginning of the process , the reaction chamber 12 was closed hermetically from outside the oven , and the reaction gases , except for precursor ( titanium tetrachloride ), were supplied to the inlets flushing the system for 10 - 15 min . the slight overpressure ( ca . 1 . 1 bars ) was maintained at a constant value by the gas trap in the exit go of the gases from the reaction chamber 12 . this procedure eliminates most of the residual atmospheric gases , like water vapor and oxygen from the reaction chamber . this step is very important for the synthesis , since both the final product ( tis 2 ) and especially the precursor ( ticl 4 ) are very sensitive to moisture . subsequently , the reactor was inserted into the oven 15 . independent inlets in 1 and in 2 for both reaction gases i . e . ticl 4 and h 2 s were used , with the mixture of the reagents being formed in the reaction chamber itself . the flow - rate of h 2 s ( 3 - 20 cc / min ) was controlled by means of a tylan model fc260 mass flow - controller 16 a . the h 2 s was diluted by mixing this gas with a stream of n 2 gas ( 10 - 200 cc / min in this reaction ) using another flow - controller 16 b . the ticl 4 vapors were obtained by preheating the liquid ticl 4 in the gas - washing bottle 14 a of the evaporation chamber 14 . the ticl 4 vapor was carried to the reaction chamber 12 by an auxiliary n 2 gas flow . the temperature of the ticl 4 source was kept usually between 100 and 130 ° c ., which is close to its boiling point of 136 . 5 ° c . as indicated above , the preheating temperature is a significant factor , determining the amount of precursor supplied to the reaction zone . the flow - rate of nitrogen through the bottle 14 a ( 10 - 100 cc / min ) affects the stream of the titanium tetrachloride precursor as well . a small overpressure ( 1 . 1 bar ) was maintained by using a gas trap filled with naoh ( 5 %) solution in the gas outlet of the reactor . the temperature in the reaction chamber zone , where the two gases ( ticl 4 and h 2 s ) mix and react , and near the filter 18 was usually varied between 650 - 750 ° c . this temperature was chosen based on the properties of the ti - s system . several experiments have been run at higher temperatures ( up to 800 ° c .) in the reaction chamber . the reaction started with the flow of ticl 4 vapor for 30 - 60 min and was interrupted by terminating the preheating of the ticl 4 precursor and using the bypass system , which provides continuous n 2 flow for flushing the system . a short annealing period ( 10 - 15 min ) followed , allowing the last portions of the supplied titanium tetrachloride precursor to react completely . afterwards , the reactor was moved down for cooling . the main portion of the synthesized material was collected on the filter . in addition , small portions of the product powder were found sticking to the surfaces of the quartz reactor . preparation of fullerene - like nanostructures of tis 2 in a horizontal reactor based apparatus of fig2 . the reaction chamber 112 was cleaned in a similar manner as described in example 1 above in order to maintain a water and oxygen free atmosphere . subsequently , the reaction chamber was inserted into the oven 115 . the temperature in the horizontal reaction chamber 112 was controlled by means of a single - zone oven 115 . the ticl 4 vapor was prepared in the separate evaporation chamber ( 14 in fig1 ) and supplied to the reaction chamber 112 in the similar way as was done in the above - described example 1 . the temperature of the reaction chamber 112 , where the two gases ( ticl 4 and h 2 s ) mix and react , was varied in the range of 650 - 750 ° c . the resulting tis 2 powder was collected for analysis on the surface of the reactor boat . however , the product collection was impeded as the product was swept by the carrier gas to the trap . preparation of fullerene - like nanostructures of ws 2 in a horizontal reactor based apparatus of fig2 . the reaction chamber 112 was cleaned in a similar manner as described in example 1 above in order to maintain a water and oxygen free atmosphere . subsequently , the reaction chamber was inserted into the oven 115 . the temperature in the horizontal reaction chamber 112 was controlled by means of a single - zone oven 115 . the chosen precursor wo 2 cl 2 was heated up to 270 - 290 ° c . in the separate evaporation chamber ( 14 in fig1 ) and its vapor was supplied to the reaction chamber 112 in the similar way as was done in the above - described example 1 . the temperature of the reaction chamber 112 , where the two gases ( metal - containing precursor and h 2 s ) mix and react , was varied in the range of 700 - 850 ° c . a small overpressure ( 1 . 1 bar ) was maintained by using a gas trap filled with naoh ( 5 %) solution in the gas outlet of the reaction chamber . the resulting ws 2 powder was collected for analysis on the surface of the reactor boat . however , the product collection was impeded as the product was swept by the carrier gas to the trap . the resulting nanoparticles are shown in fig6 . as can be noted , the if - ws 2 obtained in the present example are not so perfect and have hollow core . this can be explained by the inhomegenity of the reaction parameters in the chosen horizontal reactor . in other experiments the forming gas , containing 1 - 10 % of h 2 in n 2 , was used instead of clean nitrogen for either caring the metal - containing precursor or diluting the h 2 s . furthermore , similar series of experiments were carried out using horizontal reactors starting with wbr 5 ( boils at 333 ° c ., preheated at 290 - 330 ° c .). different combinations of carrier gas ( clear nitrogen or hydrogen - enriched nitrogen ) were used . the resulting material consisted from if - nanoparticles together with byproducts ( platelets amorphous materials ), as revealed by tem analysis . different nanoparticles both hollow - core and non - hollow core were observed . preparation of if - ws 2 nanoparticles in the vertical reactor based apparatus of fig1 at the beginning of the process , the reaction chamber 12 was closed hermetically from outside the oven , and the reaction gases , except for precursor ( wbr 5 ), were supplied to the inlets flushing the system for 10 - 15 min . the slight overpressure ( ca . 1 . 1 bars ) was maintained at a constant value by the gas trap in the exit go of the gases from the reaction chamber 12 . subsequently , the reactor was inserted into the oven 15 . independent inlets in 1 and in 2 for both reaction gases i . e . wbr 5 and h 2 s were used , with the mixture of the reagents being formed in the reaction chamber itself . the h 2 s ( 3 - 20 cc / min ) was mixed with a stream of n 2 gas ( 10 - 200 cc / min in this reaction ). the wbr 5 vapors were obtained by preheating the wbr 5 precursor in the gas - washing bottle 14 a of the evaporation chamber 14 and were carried to the reaction chamber 12 by an auxiliary n 2 gas flow . the temperature of the wbr 5 source was kept usually between 290 and 330 ° c ., which is close to its boiling point of 333 ° c . a small overpressure ( 1 . 1 bar ) was maintained by using a gas trap filled with naoh ( 5 %) solution in the gas outlet of the reaction chamber . the temperature in the reaction chamber zone , where the two gases ( wbr 5 and h 2 s ) mix and react , and near the filter 18 was usually varied between 700 - 850 ° c . the main portion of the synthesized material was collected on the filter . in addition , small portions of the product powder were found sticking to the surfaces of the quartz reaction chamber . preparation of if - mos 2 nanoparticles in the vertical reactor based apparatus of fig1 at the beginning of the process , the reaction chamber 12 was closed hermetically from outside the oven , and the reaction gases , except for precursor ( mo ( co ) 5 ), were supplied to the inlets flushing the system for 10 - 15 min . subsequently , the reaction chamber was inserted into the oven 15 . independent inlets in 1 and in 2 for both reaction gases i . e . mo ( co ) 5 and h 2 s were used , with the mixture of the reagents being formed in the reaction chamber itself . the h 2 s ( 3 - 20 cc / min ) was mixed with a stream of n 2 gas ( 10 - 200 cc / min in this reaction ). the mo ( co ) 5 vapors were obtained by preheating the liquid mo ( co ) 5 in the gas - washing bottle 14 a of the evaporation chamber 14 and was carried to the reaction chamber 12 by an auxiliary n 2 gas flow . the temperature of the mo ( co ) 5 source was kept usually between 160 and 200 ° c ., which is over its melting point of 150 ° c . the temperature in the reaction chamber zone , where the two gases ( mo ( co ) 5 and h 2 s ) mix and react , and near the filter 18 was usually varied between 650 - 850 ° c . the main portion of the synthesized material was collected on the filter . in addition , small portions of the product powder were found sticking to the surfaces of the quartz reactor . preparation of if - ws 2 nanoparticles in the vertical reactor based apparatus of fig1 at the beginning of the process , the reaction chamber 12 was closed hermetically from outside the oven , and the reaction gases , except for precursor ( wcl 4 ), were supplied to the inlets flushing the system for 10 - 15 min . the slight overpressure ( ca . 1 . 1 bars ) was maintained at a constant value by the gas trap in the exit go of the gases from the reaction chamber 12 . subsequently , the reactor was inserted into the oven 15 . independent inlets in 1 and in 2 for both reaction gases i . e . wcl 4 and h 2 s were used , with the mixture of the reagents being formed in the reaction chamber itself . the h 2 s ( 3 - 20 cc / min ) was mixed with a stream of n 2 gas ( 10 - 200 cc / min in this reaction ). the wcl 4 vapors were obtained by preheating the precursor in the gas - washing bottle 14 a of the evaporation chamber 14 and were carried to the reaction chamber 12 by an auxiliary n 2 gas flow . the temperature of the wcl 4 source was kept usually between 200 and 400 ° c . in order to provide the necessary amount of precursor supplied to the reaction . a small overpressure ( 1 . 1 bar ) was maintained by using a gas trap filled with naoh ( 5 %) solution in the gas outlet of the reaction chamber . the temperature in the reaction chamber zone , where the two gases ( wcl 4 and h 2 s ) mix and react , and near the filter 18 was usually varied between 700 - 850 ° c . the main portion of the synthesized material was collected on the filter . in addition , small portions of the product powder were found sticking to the surfaces of the quartz reaction chamber . preparation of if - ws 2 nanoparticles in the vertical reactor based apparatus of fig1 at the beginning of the process , the reaction chamber 12 was closed hermetically from outside the oven , and the reaction gases , except for precursor ( wcl 5 ), were supplied to the inlets flushing the system for 10 - 15 min . the slight overpressure ( ca . 1 . 1 bars ) was maintained at a constant value by the gas trap in the exit go of the gases from the reaction chamber 12 . subsequently , the reactor was inserted into the oven 15 . independent inlets in 1 and in 2 for both reaction gases i . e . wcl 5 and h 2 s were used , with the mixture of the reagents being formed in the reaction chamber itself . the h 2 s ( 3 - 20 cc / min ) was mixed with a stream of n 2 gas ( 10 - 200 cc / min in this reaction ). the wcl 5 vapors were obtained by preheating the wcl 5 precursor in the gas - washing bottle 14 a of the evaporation chamber 14 and were carried to the reaction chamber 12 by an auxiliary n 2 gas flow . the temperature of the wcl 5 source was kept usually between 250 and 285 ° c . a small overpressure ( 1 . 1 bar ) was maintained by using a gas trap filled with naoh ( 5 %) solution in the gas outlet of the reaction chamber . the temperature in the reaction chamber zone , where the two gases ( wcl 5 and h 2 s ) mix and react , and near the filter 18 was usually varied between 700 - 850 ° c . since the formal valence of tungsten in the precursor ( wcl 5 ) differs from the one in the expected product ( ws 2 ), additional reduction of metal was required . the excess of h 2 s in the reaction atmosphere acts as the reduction agent , however in part of the experiments additional flow of h 2 was used for this purpose . the additional flow of hydrogen ( 1 - 10 % of hydrogen within nitrogen instead of pure n 2 ) was supplied either together with precursor or mixed with h 2 s . the main portion of the synthesized material was collected on the filter . in addition , small portions of the product powder were found sticking to the surfaces of the quartz reaction chamber . preparation of if - ws 2 nanoparticles in the vertical reactor based apparatus of fig1 at the beginning of the process , the reaction chamber 12 was closed hermetically from outside the oven , and the reaction gases , except for precursor ( wcl 6 ), were supplied to the inlets flushing the system for 10 - 15 min . the slight overpressure ( ca . 1 . 1 bars ) was maintained at a constant value by the gas trap in the exit go of the gases from the reaction chamber 12 . subsequently , the reactor was inserted into the oven 15 . independent inlets in 1 and in 2 for both reaction gases i . e . wcl 6 and h 2 s were used , with the mixture of the reagents being formed in the reaction chamber itself . the h 2 s ( 3 - 20 cc / min ) was mixed with a stream of n 2 gas ( 10 - 200 cc / in in this reaction ). the wcl 6 vapors were obtained by preheating the wcl 6 precursor in the gas - washing bottle 14 a of the evaporation chamber 14 and were carried to the reaction chamber 12 by an auxiliary n 2 gas flow . the temperature of the wcl 6 source was kept usually between 275 and 345 ° c . a small overpressure ( 1 . 1 bar ) was maintained by using a gas trap filled with naoh ( 5 %) solution in the gas outlet of the reaction chamber . the temperature in the reaction chamber zone , where the two gases ( wcl 6 and h 2 s ) mix and react , and near the filter 18 was usually varied between 700 - 850 ° c . since the formal valence of tungsten in the precursor ( wcl 6 ) differs from the one in the expected product ( ws 2 ), additional reduction of metal was required . the excess of h 2 s in the reaction atmosphere acts as the reduction agent , however in part of the experiments additional flow of h 2 was used for this purpose . the additional flow of hydrogen ( 1 - 10 % of hydrogen within nitrogen instead of pure n 2 ) was supplied either together with precursor or mixed with a h 2 s . the main portion of the synthesized material was collected on the filter . in addition , small portions of the product powder were found sticking to the surfaces of the quartz reaction chamber . preparation of if - mos 2 nanoparticles in the vertical reactor based apparatus of fig1 at the beginning of the process , the reaction chamber 12 was closed hermetically from outside the oven , and the reaction gases , except for precursor ( mocl 5 ), were supplied to the inlets flushing the system for 10 - 15 min . the slight overpressure ( ca . 1 . 1 bars ) was maintained at a constant value by the gas trap in the exit go of the gases from the reaction chamber 12 . subsequently , the reactor was inserted into the oven 15 . independent inlets in 1 and in 2 for both reaction gases i . e . mocl 5 and h 2 s were used , with the mixture of the reagents being formed in the reaction chamber itself . the h 2 s ( 3 - 20 cc / min ) was mixed with a stream of n 2 gas ( 10 - 200 cc / min in this reaction ). the mocl 5 vapors were obtained by preheating the precursor in the gas - washing bottle 14 a of the evaporation chamber 14 and were carried to the reaction chamber 12 by an auxiliary n 2 gas flow . the temperature of the mocl 5 source was kept usually between 200 and 265 ° c . a small overpressure ( 1 . 1 bar ) was maintained by using a gas trap filled with naoh ( 5 %) solution in the gas outlet of the reaction chamber . the temperature in the reaction chamber zone , where the two gases ( mocl 5 and h 2 s ) mix and react , and near the filter 18 was usually varied between 700 - 850 ° c . since the formal valence of tungsten in the precursor ( mocl 5 ) differs from the one in the expected product ( ws 2 ), additional reduction of metal was required . the excess of h 2 s in the reaction atmosphere acts as the reduction agent , however in part of the experiments additional flow of h 2 was used for this purpose . the additional flow of hydrogen ( 1 - 10 % of hydrogen within nitrogen instead of pure n 2 ) was supplied either together with precursor or mixed with a h 2 s . the main portion of the synthesized material was collected on the filter . in addition , small portions of the product powder were found sticking to the surfaces of the quartz reaction chamber . the products were analyzed mainly by means of various electron microscopy techniques . the following microscopes were used : environmental scanning electron microscope ( philips fei - xl30 e - sem ); transmission electron microscope ( philips cm120 tem ), equipped with eds detector ( edax - phoenix microanalyzer ); high resolution transmission electron microscope ( hrtem ) with field emission gun ( fei technai f30 ), equipped with a parallel electron energy loss spectrometer ( gatan imaging filter - gif ( gatan )). simulation of the hrtem micrographs of tis 2 was obtained using the mactempas image - simulation software . complementary analyses were carried out by powder x - ray diffraction ( xrd ). tem examination of the powder obtained in the horizontal set - up ( example 2 ) revealed the presence of closed cage nanostuctures in the product ( fig3 ). the typically observed particle - size was about 100 nm , with nanoparticles ranging in size between 50 and 150 nm . the wide size distribution is a reflection of the inhomogenity of the reaction conditions in this set - up . the yield of the closed - cage nanoparticles in those experiments was up to 30 %, depending on the reaction conditions . the remaining material , as revealed by sem and tem , was made of tis 2 platelets , a few tens of nanometers to 0 . 5 micron in size , each . the product of the vertical set - up ( example 1 ) was found to contain an appreciably larger fraction of the if - tis 2 phase with yields approaching 80 %. furthermore , the size distribution of the synthesized nanoparticles was found to be appreciably narrower in the vertical set - up , as compared to the horizontal reactor . the product of the vertical reactor ended up also to be more spherical ( fig4 ). tilting the sample in different viewing angles did not reveal any significant changes in the shape of the observed nanoparticles . these findings emphasize the advantage of using the vertical set - up for the synthesis of the if - nanophase materials . varying the synthesis time did not seem to have an appreciable influence on the size distribution of the if - tis 2 nanoparticles . the resulting if - nanoparticles were found to consist of a large number of concentric layers displaying relatively smooth curvature . for instance , the nanoparticle shown in fig4 consists of approximately 80 concentric and spherical layers . these layers were continuous with no visible holes or edge dislocations observed . the hollow core , which was observed in the if - ws 2 ( mos 2 ) nanoparticles , did not exist in the present nanoparticles . a careful examination of the synthesized nanoparticles did not reveal a spiral growth mode of the molecular layers of the material . instead , a quasi - epitaxial , layer by layer growth mode could be deciphered . the observed layers are complete and are separated one from the others . in several cases the cores of the observed tis 2 nanoparticles were found to be made of a number of tiny spherical if centers , which are stacked together . as a rule , such nanoparticles were preferably found in the experiments with definitely higher flow rate of ticl 4 precursor ( preheating at 130 - 140 ° c .). for instance several such centers are visible in the tem image of the nanoparticle shown in fig3 . the borders between those nuclei can be clearly distinguished in the core of the nanoparticle , while the peripheral layers envelope the divided core into a single spherical moiety . hrtem image of a part of a closed tis 2 fullerene - like nanoparticle is shown in fig5 a together with its simulated image . a satisfactory agreement between the real and simulated images is indicative of the correct assignment of the nanoparticle &# 39 ; s structure . it should be nonetheless noted , that the simulation refers to the bulk ( lt ) material , which is flat , awhile the if - tis 2 nanoparticles are curved and their structure is not fully commensurate , because the number of atoms is different in each of the concentric nested layers . the interlayer distance obtained from either fourier analysis ( insert of fig4 ), or a direct measurement ( fig5 b ) was found to be 0 . 58 nm . this value represents an expansion of about 1 . 8 % in comparison to the layer to layer separation in bulk lt - tis 2 ( 0 . 57 nm ). the interlayer distance did not seem to vary along the entire volume of the nanoparticle . this result is in a good agreement with xrd experiments , in which the synthesized material was identified as lt - tis 2 . it nevertheless stands in a sharp contrast with the synthesized if - ws 2 and mos 2 nanoparticles , synthesized by reacting h 2 s with the respective oxides , were often large gaps are observed between the molecular sheets . these gaps can be associated with strain - induced brisk changes in the topology of the layers from evenly folded to faceted structure . this topology was found to be typical for nanoparticles which are produced by the reaction of h 2 s with the respective oxide , which starts on the surface of the nanoparticle and progresses inwards consuming the oxide core . at high temperature experiments ( 800 ° c . ), nanoparticles having distorted shape were observed . also , the overall yield of the if - tis 2 at high temperatures was low ( app . 10 %), the main portion being tis 2 platelets . a number of other precursors were tested for their aptitude to obtain fullerene - like materials in similar way . the resulting nanoparticles of both mos 2 and ws 2 ( fig6 - 10 ) were obtained from variety of starting materials . most of the newly - obtained nanoparticles were found to differ from their analogs , obtained by reduction - sulfidization of oxide templates . more specifically , the nanoparticles obtained from the vapors of metal - containing precursors were more spherical , with little amount of defects . moreover , they had a small hollow core , if any , like it was found in the case of tis 2 . a ball on flat tester 1 was used for the present tribological experiments . a load of 50 grams was used in these experiments . the friction coefficient was measured in the end of the 20 cycles run , were steady tribological regime prevailed . to test the efficacy of the if - tis 2 particles produced by the process of the present invention , as a solid lubricant a series of tribological experiments were conducted . it was found that the addition of a small amount ( 1 %) of the if - tis 2 powder decreases significantly ( 10 times ) the friction coefficient of the pure oil - from 0 . 29 to 0 . 03 . a similar test with 1 % bulk powder ( lt - tis 2 ) added to the oil , leads to a friction coefficient of 0 . 07 , i . e . twice that of the if - phase . it must be emphasized here that the portion used for the tribological tests contained no more than 50 % if - tis 2 , the rest being platelets of lt - tis 2 . the collected data suggests that the shape of the if - tis 2 of the invention might play a major role in lowering the friction coefficient . the quite perfectly spherical nanoparticles with sizes ranging in the 30 - 70 nm and up to 100 molecular layers thick obtained with the vertical set - up could provide effective rolling friction and sliding . it is emphasized the important role played by the spherical shape of the nanoparticles in providing rolling friction with a reduced friction coefficient and wear . these nanoparticles are also stable and compliant . comparison between if nanoparticles obtained in the process of the present invention and known if nanoparticles : the if - tis 2 nanoparticles obtained by the process of the present invention in a vertical reactor , typically consist of about hundred layers and are formed fast , over a period of a few minutes or less , only . they are spherical in shape , and their lattice parameter ( c ) is constant along the radial axis of the nanoparticle , which suggests that they suffer from relatively minor strain . table 2 together with fig1 make a concise comparison between the morphology and some of the properties of the if - tis 2 nanoparticles obtained by the process of the present invention and if - ws 2 nanoparticles obtained by processes known in the art . the following table 2 compares the representative characteristics of fullerene - like ws 2 obtained by the known reaction of h 2 s gas with tungsten oxide nanoparticles , and tis 2 nanoparticles obtained from titanium chloride vapor according to the present invention . in contrast to the earlier synthesized if - ws 2 ( mos 2 ) 5 - 7 , the closed - cage nanoparticles of titanium disulfide produced by the process of the present invention have a very small hollow core or do not possess such core . the interlayer distance ( 0 . 58 nm ) is preserved along the entire volume of the nanoparticle . the present results are indicative of the fact that the titanium disulfide layers start to grow from a small nuclei , obeying thereby the ubiquitous nucleation and growth mechanism . the present synthesis of if - tis 2 may be envisaged as a homogeneous nucleation of the fullerene - like structures from embryonic clusters formed in the vapor phase , in contrast to the heterogeneous nucleation of if - ws 2 ( mos 2 ) on the surfaces of the respective oxide templates . the vapor of ticl 4 crosses the flux of h 2 s , coming out from an oppositely placed tube at relatively high temperature ( 650 - 750 ° c . ), which provides a high reaction rate . since the tis 2 clusters formed in the gas phase are non - volatile , they condense into small nuclei . it is well established that shrinking the size of the graphene ( or other layered material — like tis 2 ) sheet makes the planar structure unstable resulting in folding and formation of a closed - cage structure . once such closed - cage nuclei of tis 2 are formed in the vapor phase of the reactor further ticl 4 adsorb on its surface and react with the h 2 s gas . this reaction occurs in a highly controlled - quasi - epitaxial fashion , i . e . with a single growth front leading to a layer by layer growth mode . this growth mode entails minimal geometrical constraints , and hence the nanoparticles are appreciably more spherical than the previously reported if nanoparticles . the spherical morphologies with relatively smooth curvature exhibited by these nanoparticles suggest that the bending of the molecular sheets results in continuously distributed dislocations or defects , in contrast to the more facetted structures , observed in the previously synthesized if - ws 2 , where the defects are localized in grain boundaries . the rather large number of layers observed in the if - tis 2 nanoparticles undergoing van der waals interactions may compensate for the bending and dislocation energies and add to the stability of such spherical nanoparticles . the small crystallites , formed during the initial stages of the gas - phase reaction collide in the vapor phase . when the kinetic energy of the collision is not sufficiently large to separate the colliding nanoparticles , they aggregate forming multi - nuclei cores . these aggregated nanoparticles serve as a template , which are subsequently enfolded by additional tis 2 layers on their surface . a fullerene - like nanoparticle with multi - core is thus obtained ( see fig3 ). the fairly narrow size distribution of the if - tis 2 nanoparticles in the vertical set - up is particularly notable . presently , two possible explanations for this effect can be invoked . once the nanoparticles reach a critical size , which coincides with their thermodynamic stability , their growth rate slows down appreciably , while the smaller nuclei continue to grow fast until they reach a similar size . a further possible reason for the narrow size distribution is that the larger nanoparticles can not float in the vapor and they fall on the filter , where they are rapidly buried under the next layer of nanoparticles , and their growth slows down . the constancy of the distance between the layers ( c ) in the radial direction , and their quite perfectly spherical shape indicate that the present if nanoparticles suffer little strain , only . this phenomenon is the result of the nucleation and growth mechanism accomplished in the present invention , and it has a favorable impact on the tribological behavior of such nanoparticles . other if metal chalcogenides , e . g . if - ws 2 and mos 2 nanoparticles , synthesized by a similar process as the above - exemplified one for tis 2 , provide similar spherical nanoparticles consisting of many layers ( fig6 - 10 ). it appears that the nanoparticles obtained from the vapors of metal - containing precursor follow the same growth mechanism ( nucleation and growth ). this topology favors rolling and sliding of the nanoparticles , providing improved tribological behavior for the if solid lubricant . since if - ws 2 and mos 2 are the materials of choice for such applications , the improved control of the nanoparticles morphology , as presented in the present invention for if - tis 2 , leads to a superior tribological behavior of these solid lubricants , too .