the photodeformable materials of the present invention are prepared from a photoionizable composition selected from the group consisting of n , n , dimethyl - p - phenylenediamine , tetrathiafulvalene , tetraselenafulvalene , ferrocene , tetrathiatetracene and leuco dyes such as leuco methyl violet , and a polymeric backbone selected from the group consisting of polyacrylics , polyglutamate , polyvinyl amine , polyvinyl alcohol , and polystyrene . the donor groups are photoionized to charged species in the presence of halogenated hydrocarbons or acceptor groups . a preferred halogenated hydrocarbon or acceptor can be selected from the group consisting of cbr 4 , ccl 4 , c 2 cl 4 br 2 and ch 2 br 2 . for example , see the publication to ari aviram , entitled &# 34 ; mechanophotochemistry ,&# 34 ; macromolecules , vol . 11 , p . 1275 , dec . 1978 . a typical synthetic path to one of the preferred compositions of the present invention , e . g ., poly - 4 -( n , n - dimethylamino )- n - γ - d glutamanilide , is as follows : ## str1 ## the photoionizable composition can be similarly reacted with other polymer backbone compositions , for example , polyacrylics , polyglutamate , polyvinyl amine , polyvinyl alcohol , polystyrene and the like , to provide other embodiments of the invention . the reaction can be carried out in the following solvents , n , n - dimethylformamide , n , n - dimethylacetamide , hexamethylphosphoric triamide , tetramethylene sulfone , tetramethylene sulfoxide , dimethyl sulfoxide and the like . the resultant polymer is then crosslinked to form about 1 . 0 % to about 5 . 0 % to form a gel . suitable crosslinking agents can be selected from a preferred crosslinking agent which is 2 , 6 - bis -( bromomethyl ) naphthalene . other crosslinking agents may be chosen from among α , ω - dihalogenated compounds ; α , ω - dialcohols ; α , ω - diacids . typically α , ω compounds which can be used in the present invention include those having the general formulae , ## str2 ## where x is selected from a halogen , an alcoholic , an acid and an amine group and n is from 1 to 50 . preferably the resultant polymer is crosslinked at about 1 . 5 %. films of the prepared polymer can be cast onto a substrate from a suitable solvent to which a preferred crosslinking agent has been added . the casted film is permitted to dry slowly so that crosslinking can occur . films having thickness of from about 10 μm to about 1 mm . are prepared . carbon tetrabromide or other halogenated acceptors mentioned above are incorporated into the films . the prepared films can then be irradiated by actinic radiation . sources of actinic radiation can be high pressure mercury lamps with filters such as &# 34 ; calobars &# 34 ; that transmits at 3650 a or xenon lamps , n 2 lasers or cd lasers . in preferred embodiments a source of &# 34 ; black light &# 34 ; rated at 1680μ watts / cm 2 and having a wavelength of 3650 a is used . prior to irradiation the film is swollen with a suitable solvent , such as n , n - dimethylformamide , n , n - dimethylacetamide , hexamethylphosphoric triamide , tetramethylene sulfone , tetramethylene sulfoxide , dimethyl sulfoxide , into which is incorporated a halogenated acceptor , e . g ., cbr 4 , ccl 4 , c 2 cl 4 br 2 or ch 2 br 2 . the foregoing and other objects , features and advantages of the invention will be apparent from the following more particular description of a preferred embodiment of the invention . the following examples are given solely for purposes of illustration and are not to be considered limitations on the invention &# 39 ; s many variations of which are possible without departing from the spirit or scope thereof . about 0 . 5 gm . of poly - d - glutamic acid , having a molecular weight of 12 , 400 , is dissolved in 50 ml dry n , n - dimethylformamide to which 2 gm . of freshly distilled n , n - dimethyl - p - phenylenediamine is added . the solution is cooled to 0 ° c . and 1 gm . dcc is added with stirring . stirring is continued at 0 ° c . for one hour and at room temperature for an additional 24 hours . one ml of dry methanol is added and stirring is continued for an additional hour . the precipitate is filtered off and the filtrate is evaporated to dryness at 0 . 01 mm . 35 ° c . ( bath temperature ). the residue is dissolved in tetrahydrofuran ( thf ) and filtered in a dry box under nitrogen . diethyl ether is added to the solution and the precipitate is filtered and collected under nitrogen . the collected solid is further purified by precipitation from thf with diethyl ether . anal . calculated : c - 62 . 90 , h - 6 . 85 , n - 16 . 93 -- found c - 62 . 69 , h - 7 . 64 , n - 14 . 54 . films of poly - p -( n , n - dimethylamino )- n - γ - d - glutamanilide are prepared by dissolving 120 mgm . of the compound in 400 mgm . of thf . 2 , 6 - bis -( bromomethyl ) naphthalene , 2 . 35 mgm . ( to provide for 1 . 5 m % crosslinking ) in 100 mgm . thf is added and a film is cast on a glass slide . to prevent fast evaporation the film is kept in a chamber saturated with thf vapors . it took about a day to evaporate the solvent . the dry film thickness is 11 . 5 mil . it took about 24 hours for the crosslinking reaction to take place . the so prepared film having an approximate area of 4 mm 2 is swollen in n , n - dimethyl formamide . the excess liquid is replaced in the dark with a 5 % solution of carbontetrabromide in n , n dimethylformamide , and photographed under a microscope , following a five minute waiting period . the film is irradiated at a distance of 1 &# 34 ; with a source of &# 34 ; black light &# 34 ; rated at 1680 μwatts / cm 2 at 3650 a , 18 inches away . during the irradiation the film is freely suspended in the liquid to prevent stress and strain . at the end of the irradiation period ( as specified ) the films were photographed again and the dilations measured from the photographs . additionally , films were exposed to varying exposure times and a plot of observed deformations as indicated in the figure was obtained . about 10 gms . of polyacrylic acid , having a molecular weight of about 250 , 000 is dissolved in 200 ml dry n , n - dimethylformamide to which is added 20 gms freshly distilled n , n - dimethyl - p - phenylenediamine . the solution is cooled under nitrogen to 0 ° c . and 30 gms . dcc are added . the solution is stirred for about two hours at 0 ° c . and for an additional seventy - two hours at room temperature . a precipitate forms after ten minutes that increases in quantity steadily and the solution becomes very viscous . one liter dry solvent is added to permit filtration which could not be affected and therefore the solid was removed by a centrifuge . the liquid is then treated as in example 1 to yield 8 gms of pure product . anal . calculated c - 69 . 47 , h7 . 36 , n14 . 74 -- found c - 67 . 37 , h - 8 . 04 , n - 10 . 36 . films prepared of this material and crosslinked to 1 . 5 % by 2 , 6 - bis ( bromomethyl ) naphthalene exhibited a maximum of 14 % dilation in each dimension after four minutes irradiation with a 3650 a , 1680 μwatts / cm 2 light source . for the purpose of obtaining relief images which strongly adhere to substrates , films are prepared as follows : about 10 g of 3 - chloropropyltriethoxysilane is dissolved in 50 ml of xylene and refluxed under nitrogen . a wafer of silicon 2 . 5 in . in diameter was placed in the vapor area . reflux was continued for 5 hours . the wafer is then rinsed with dry xylene . a solution containing 0 . 6 g of the polymer prepared in example 1 , 7 . 83 mg of 2 , 6 - bis ( bromomethyl ) naphthalene ( predissolved in 0 . 3 g of cyclohexanone ), 0 . 6 g of carbon tetrabromide and 3 g of cyclohexanone is spin coated onto the silicon wafer in the dark . the spin coating is repeated several times to build a film of about 5 μm . the film is left to react in the dark for 72 hours . the films are then irradiated through masks , with a 1680 μw / cm 2 light source and immersed into dmf for 5 minutes . relief images of the patterns exposed are thus obtained . relief images were prepared as in example 3 except the polymeric composition prepared in example 2 was substituted for the polymeric composition used therein . although the invention has been described with respect to various preferred embodiments thereof , it should be recognized that it is not limited thereto but rather various modifications will occur to and be made by those skilled in the art upon a reading of the present disclosure and such changes are within the spirit of the invention and the scope of the claims .