the method of the present invention will first be generally described in connection with fig1 through 4 . the method will be described in connection with a completed sail 50 shown in fig5 . the completed sail will be typically triangular in shape and will comprise a head 51 , or top corner , a tack 52 , or forward lower corner , and a clew 53 . the three edges of a sail are defined as the luff 54 , or leading edge , the leech 55 or trailing edge , and the foot 56 or bottom edge . the finished sail is a laminate comprising two outer film layers 57 and an inner network of reinforming yarns . yarns 58 generally extend from the top to the bottom of the sail and include yarns converging into the corners . yarns 59 generally extend across the sail and between the bottom two corners . as shown in fig1 - 4 , the sail is fabricated on a roll 10 rotating in a counterclockwise direction as shown in fig1 and 2 . a base layer of perforated film 12 is applied to the roll across the width thereof . the film 12 may be precoated with adhesive , the tape may be eliminated , and adjacent edges of the film may be overlapped . the film may be strips unwound from staggered rolls 14 and 16 and joined together along facing or overlapping edges with adhesive tape supplied from roll 18 , with the joined strips being guided by guide roll 20 under uniform tension . during processing , the base film layer 12 is held onto the roll surface by application of a partial vacuum through the cylindrical wall of roll , as described hereinafter . the roll has a flexible deformable surface in which adjacent surface segments 13 ( fig2 ) across the roll , i . e ., parallel to the axis of rotation , may be deformed into successive convexly curved profiles . the base film layer 12 is first heated by a hot air or radiant heater 22 adjacent the roll to soften the film . in the zone denoted by the arrow at 24 , the roll segment supporting the heated film is deformed to cause the film to be deformed along a narrow contiguous segments across the roll . fig3 and 4 schematically show a roll 10 having an outer flexible surface 26 , with the surface profile being adjusted by means of pistons 28 . fig3 shows the pistons in a neutral position in which the outer surface segment is cylindrical . fig4 shows adjustment of the pistons such that the surface 26 is curved to an airfoil shape . as shown in fig4 and with reference to fig5 the luff 54 or leading edge portion of the base film of the sail would be located on the left side of the drawing and the leech 55 or trailing edge of the sail is located at or near the right edge . since the film is being deformed along a curved profile in the cross direction and is wrapped around the cylinder in the longitudinal or machine direction , the film is being deformed , in a successively varying manner , in three dimensions . in other words , the curvature of the roll around its circumference and the curved profile of the sectors both contribute to the permanent deformation of the film , such that the gaussian curvature of the original sail designed is preserved all points on the surface . when the roll reaches the end of arrow 24 , the pistons 28 are locked to maintain the profile of the film sector until all subsequent processing steps are completed . since the curvature or draft of a sail varies from the head or top to the foot or bottom , the cross curvature of successive profile curvatures change . the shape and dimensions of sails are determined from standard models , and all necessary information can be stored in the form of data in a computer . this information can be converted into signals which cause individual adjustment of each of the pistons 28 in each successive line . using a foresail or jib as an example , the draft or rate of curvature will be greater near the luff 54 and the density or number of the pistons 28 may be greater in this region , as shown in fig4 and 4a . fig4 a illustrates the principle of employing only a portion of the width of the roll to make sails having smaller widths . in such case , the roll would be deformed on the left hand side , with the right hand side remaining undeformed . following heating and deformation , the film is coated with adhesive , such as by a spray head 30 applying adhesive in liquid form and transversing back and forth across the film surface , while moving with the surface to obtain a pass parallel to the axis of the cylinder . in the preferred embodiment , the film is pre - coated with an adhesive . the adhesive is preferably of the thermoplastic or hot melt type . the moving adhesive coated film then passes under a plurality of stations 32 and 34 for applying reinforcing yarn to the film . the stations 32 are spaced to assure adequate coverage of the yarns to the film . the stations comprise fixed transverse support beams 33 having automated yarn dispensers 35 movably mounted thereon wherein the yarn is guided and applied to the film by rollers 37 . the dispensers 32 move back and forth across the moving film and apply yarns 58 which will extend from the top 51 to the bottom 56 of the sail ( fig5 ) or at acute angles thereto . since all modem sails are triangular , the stations 32 will apply yarns extending continuously diverging from the top corner or head 51 into the body of the sail and converging into the two lower corners or the tack 52 and clew 53 . preferably , the yarn is precoated with adhesive . the station 34 serves to apply yarns 59 across the width of the film , such as between the tack 52 and the clew 53 , and across the other yarns 58 between the edges of the sail . all yarns 58 and 59 are preferably applied in a continuous and uninterrupted fashion , from corner to corner , from corner to edge , or from edge to edge . as shown in fig2 the station 34 and the adhesive applicator 30 may be mounted on motorized radial arms 31 and 33 to allow movement of the applicators in the direction of movement of the film . after a sufficient number of yarns have been applied in the desired pattern to complete a single sail , the yarns may be fed continuously from the applicators to an adjacent area of the film to define the next sail . in the alternative , the yarns may be severed and repositioned by the applicators for the start of a new sail . the yarns may be composed of any of the known type used in modern sailmaking . these typically include twisted and untwisted continuous filament yarns composed of polymers such as polyester , aramid , oriented polyethylene and the like , as well as individual monofilament threads . the denier of the yarns can be adjusted to suit the particular weight or type of sail being produced , and the number or density of yarns may be programmed to provide the desired weight . in addition , as described in the baudet u . s . pat . no . 5 , 097 , 784 , the yarns are preferably applied in a calculated pattern to best accommodate the major stress lines in the sail when the sail is in use , such that the yarns will generally radiate from the corners . other yarns may intersect with the primary yarns to provide support at various sailing angles and to resist tear . the composition of the film may be any of those available and employed in modern sail laminates . typically , stretch resistant films of polyester are employed , but others are known and may be used . following the application of the yarns , a second layer of film 40 is applied to the first layer , which now carries the yarn and the adhesive on its exposed surface . the second film layer 40 is not perforated and may be supplied in the form of strips from rolls 42 joined together by adhesive tape 44 , or if precoated , by edge overlap . the film 40 may be formed on a second separate smaller deformable roll 46 having a heater 48 . the roll 46 also has a continuously adjusting profiled surface such that the film 40 is deformed to match the perforated base film 12 on roll 10 . in the preferred embodiment , the film is not performed but can be fed , in flat form , directly to the primary roll over an idler roll similar to roll 20 upstream of the heater 60 . thus , the second layer of film will be deformed solely by the preliminary roll 10 . the film 40 is fed onto roll 10 to form a layered structure , and such structure is passed beneath and heated by a heater 60 . in the roll position indicated by the arrow 62 , a high degree of vacuum is applied . the vacuum is drawn through the perforated base film 12 , causing the two film layers to be drawn together while being heated to set the adhesive , thereby forming a permanent laminate . the completed laminate 63 is then led off the forming roll and may be wound up on a take - up roll 65 . the sail may be finished by cutting out of the sail from the sheet and performing any finishing operations . the resulting sail , as shown in fig5 is a unitary , seamless and paneless structure . the apparatus of the present invention may be employed to make single successive sails on a continuous basis , as well as sails having portions which overlap within the base film layer . the latter is illustrated in fig6 in which three butted film layers or strips 64a , 64b and 64c are employed . the dimension 66 is equal to one meter , and the dimension 68 is equal to one wrap of film on the roll . it may be seen that portions of successive sails such as outlined at 70 and 72 may overlap , such that portions of two sails are being produced at the same time . the size of the sail is limited to the maximum width of the roll and the film , which in most cases is measured across the foot . fig7 shows the roll in cross section , and fig8 shows a cross section of a piston and roll cover assembly . the roll 10 is mounted on a support frame 74 having inner and outer supports 76 and 78 for the pistons 80 . the outer end of the piston 80 is connected to a flexible batten 82 extending across the width of the roll . the pistons include a locking device 84 ( fig8 ) for locking the piston in an advanced position , and the piston rods are advanced in sequence by an actuator 86 . the piston rods are hollow and are connected to vacuum lines 88 leading through a flexible surface 90 covering the battens 82 . if desired , separate vacuum lines to the surface may be used . the flexible surface may comprise a layer of textured elastomer having vacuum openings , which layer is covered by a permeable fabric to distribute the vacuum evenly over the surface . as shown , a retractable , pneumatic or screw driven actuator 92 engages the rod of the piston 80 and rotates therewith as the piston is moved radially outwardly to the desired position . the lock 84 locks the piston in its extended position , and a second actuator 96 is provided to unlock the piston at the end of the drum rotation cycle and to return the piston to its initial position . the pistons are returned to neutral position in the arc 94 ( fig1 ) after the laminate has been moved from the roll . fig9 - 11 illustrate an alternative and preferred arrangement for providing a deformable framework for the outer surface of the forming and support cylinder 10 . a first plurality of flexible roll 110 are formed into parallel circles with telescoping ends , to define the roll circumference support portion . a second plurality of flexible rods 112 are disposed at right angles to and above the first plurality 110 and extend parallel to the axis of the roll 10 . the rods 110 and 112 are flexibly tied together , for example , by a flexible strip 114 having a plurality of spaced apertures 116 therein arranged along a line . the apertures 116 pass through the rods 112 at spaced locations and are looped upwardly around the circumferential rods 110 to hold the assembly together in a flexible manner . the assembly is covered by one or more elastic sheets as previously discussed to provide a forming surface . the circumferential rods are connected to pistons 118 by eyebolts 120 to selectively radially expand and restrain the assembly in a radial direction . in practice , as a practical example , the main roll will have a diameter of 120 inches and will have a width of greater than 180 inches , in order to accommodate the width of three standard 60 inch wide rolls of film . approximately 1000 pistons will be employed , with each row containing 20 - 30 pistons having an extension of up to 6 inches . it is estimated that production will occur at about 2 inches of surface speed per second , with a single run consuming 3 , 300 meters of film divided among 6 rolls , 215 , 000 meters of warp yarn , 150 , 000 meters of fill yarns , and about 105 pounds of adhesive . preferably , each of the thread applicators are capable of laying down more than one individual yarns at a time , although it is important that the yarns not be tied together transversely such as in the form of a ribbon , in order to allow each individual yarn to follow it on trajectory while being applied to assure a smooth application .