a vaporization boat 10 of the resistance type require a precise shape to match the resistance circuit . it is usually made long and narrow as is shown in fig1 with a cavity or depression 12 machined into the body 11 on at least one surface 14 . the body 11 is formed from a block of graphite preferably of high density and high strength and is coated with a thin layer of pyrolytic boron nitride 14 . the process for coating boron nitride is conventional and briefly involves introducing vapors of ammonia and a gaseous boron halide in a suitable ratio into a heated furnace reactor containing the graphite body with the furnace maintained at a controlled temperature of between 1800 ° c . to 2200 ° c . the coating 18 of pyrolytic boron nitride which is usually no thicker than 0 . 030 inches fully encapsulates the graphite body except for the ends 15 and 16 where the coating is machined off to expose the graphite for making an electrical connection to a clamp assembly for external connection to a source of power . in accordance with the present invention it has been discovered that the number of flashes that the boat can sustain before failure can be substantially increased thereby improving the performance characteristic of the boat by increasing the density of the surface of the pbn coating in contact with the metal charge to render it less reactive to attack from the aluminum vaporization process . it is hypothesized that a pbn layer having an outer surface of very high density at least equal to 2 . 19 gm / cc and preferably between 2 . 19 gm / cc and 2 . 2 gm / cc . it should be understood that the theoretical maximum density for pbn is essentially 2 . 27 gm / cc and that the density of a conventional vaporization boat is equal to about 2 . 15 gm / cc or less with a density of about 1 . 95 gm / cc being the lower limit for stable operation . hence the total density range between stable operation and theoretical maximum density is from about 1 . 95 gm / cc to 2 . 27 gm / cc . it is believed that the higher density pbn coating of the present invention forms larger crystallites with smaller interlayer spacing and that this results in a less reactive area per unit volume for attack by molten aluminum . subsequent testing has substantiated the improved performance using higher density pbn and has demonstrated that the average life of the boat measured by the number of flashes before failure increased by over 20 %. higher density pbn may be achieved by accurately controlling temperature in the furnace reactor within a narrow temperature range of between 1950 ° c . and 2000 ° c . the higher density pbn coating may be formed as a single coating or a duplex coating of more than one layer in which the outer layer has the increased density . it is also within the purview of the present invention to include an intermediate layer between the pbn layer and the graphite body to adjust the cte mismatch of the materials . this intermediate layer may represent a layer of pyrolytic graphite of a thickness has a thickness in a range of between 0 . 0002 and 0 . 001 inches . the term “ pyrolytic graphite ” is hereby defined to mean a crystalline carbonaceous structure in which there is a high degree of crystallite orientation . crystalline orientation is not found in common graphite material . additionally , pyrolytic graphite exhibits anisotropic physical properties due to its being characterized by oriented slip planes in contrast to isotropic properties of common graphite . pyrolytic graphite may be formed by chemical vapor decomposition of , for example , methane gas at high temperature in a reactor chamber with a suitable inert diluent .