the instant disclosure sets forth a technique for substantially decreasing the deposition of reactant material on the inner wall surface of a glass tube in an ir heated cvd reactor . however , such description is for the purposes of exposition and not for limitation . for instance , cvd reactors using rf induction heating may advantageously implement the instant technique . fig1 is a schematic representation of a prior art ir heated , horizontal reactor generally designated by the numeral 10 . the reactor 10 is comprised of a quartz tube 12 , having a rectangular cross section , with banks of ir lamps 14 -- 14 located on the outside top surface of the tube in close , spaced relation thereto . a planar graphite susceptor 16 having a plurality of semiconductor wafers 18 -- 18 thereon is shown positioned inside the tube 12 at a predetermined angle α ( approximately 2 to 8 degrees ) to the horizontal . the wafers 18 -- 18 are shown slightly upraised from the surface of the susceptor 16 for purposes of exposition , however , in practice , the upper surface of the wafers 18 -- 18 are substantially coplanar with the surface of the susceptor 16 . in operation , the banks of ir lamps 14 -- 14 are activated to heat the wafers 18 -- 18 and the graphite susceptor 16 radiantly which , in turn , conductively heats the wafers to approximately 1 , 200 ° c . a flow of reactants comprising silicon bearing gaseous compounds ( e . g ., sihcl 3 or sicl 4 ) in a hydrogen ambient are then longitudinally directed into the tube 12 as indicated by the arrow 24 in a velocity range between 200 to 1000 cm / min . the silicon compounds that contact the surface of the heated wafers 18 -- 18 react and dissociate resulting in the desired deposited silicon layer thereon . undeposited reactants are exhausted through the outlet end of the tube 12 . undesirably , a small portion of silicon 26 deposits on the inside surface of the tube 12 which can result in inefficient operation as well as the destruction of the tube as hereinbefore indicated . fig2 shows the relative concentration of the silicon bearing compounds and the velocity thereof at the inlet and the outlet of the tube 12 . the relatively high concentration near the wall surface of the tube 12 , proximate the outlet , may account for the silicon 26 deposition shown in fig1 . fig3 shows the addition of a quartz splitter plate 30 proximate the inlet of the tube 12 . silicon containing compounds , carried in hydrogen gas , are directed longitudinally toward the wafers 18 -- 18 on the susceptor 16 from a silicon source injector 32 located beneath the splitter plate 30 . hydrogen gas , containing no silicon compounds , is simultaneously directed longitudinally along the upper half of the tube 12 at the same velocity as the silicon containing compounds in the lower half , resulting in concentrations and velocity profiles shown shortly after passing through the inlet . as the gases move toward the outlet , the silicon compound concentrations and velocity profiles change as shown . it can be seen that the silicon concentration proximate the wall of the tube 12 has been substantially decreased as compared to the outlet concentration shown in fig2 . the concentration decrease is on the order of about 2 : 1 with a noticeable decrease of undesired silicon deposit 26 ( see fig1 ) on the inside surface of the tube 12 . a further reduction of the silicon deposit 26 on the inner surface of the tube 12 has been accomplished by making the initial velocity of the reactant - free hydrogen ( i . e ., above the splitter plate 30 ) three times greater than that of the reactant - containing gases from the injector 32 at the inlet as shown in fig4 . unexpectedly such a technique reduced the reactant concentration by approximately 90 % at the wall of the tube 12 and substantially eliminated the unwanted silicon deposit 26 . although the mechanism is not fully understood it is believed that the stepped inlet concentration profile , shown in fig3 and 4 , afforded by the splitter plate 30 arrangement requires that the silicon source species diffuse upwards from the lower , high concentration , part of the flow to the wall of the tube 12 before reacting and depositing there . also , the discontinuous inlet velocity undergoes , because of its viscosity , a redistribution of its momentum ; associated with the redistribution is a substantial downward component of velocity which reduces the upward diffusion of the silicon source species . in a particular embodiment the inlet hydrogen flow was approximately 100 to 400 liters per minute while the inlet trichlorosilane ( sihcl 3 ) flow was a maximum of 60 grams per minute . the maximum flow of sihcl 3 was 7 . 3 × 10 23 atoms / min ., while the maximum flow of h 2 was 1 × 10 25 atoms / min . the atom concentration of sihcl 3 in h 2 was in the range between 2 to 8 percent . it is to be understood that the embodiments described herein are merely illustrative of the principles of the invention . various modifications may be made thereto by persons skilled in the art which will embody the principles of the invention and fall within the spirit and scope thereof .