fig1 is a diagrammatic cross - section of a color filter layer according to the invention . it comprises a layer 1 of a cholesterically ordered material in which the axis of the molecular helix of the cholesteric material extends transversely to the layer . the cholesterically ordered material comprises a polymer network and two dyes . the cholesterically ordered layer is provided on a substrate 2 of , for example , glass or metal , which is provided with an orientation layer 3 of rubbed polyimide . if desired , the substrate may alternatively consist of a flexible material , for example a synthetic material . the color filter layer shown in fig1 was manufactured as follows . the method started from a mixture of two reactive monomers consisting of 50 % by weight of the chiral monoacrylate a and 50 % by weight of the achiral diacrylate b . added to this mixture were : 0 . 7 % by weight of an uv - absorbing dye c ( abs max at 334 nm ), 0 . 25 % by weight of dye d ( abs max at 485 nm ) and 0 . 25 % by weight of of dye e ( abs max at 682 nm ). furthermore , 0 . 6 % by weight of the photoinitiator irgacure 651 ( ciba geigy ) and 40 ppm of the stabilizer p - methoxyphenol were added to the mixture . the chemical structure formulas of said compounds are shown in fig2 . a quantity of the mixture thus manufactured was introduced between two substantially parallel glass substrates spaced apart by approximately 15 μm . the facing surfaces of the substrates were provided with an orientation layer of rubbed polyimide . subsequently , the reactive mixture was polymerized by means of uv light ( 365 nm , i o = 0 . 05 mw / cm 2 ) at room temperature for approximately 10 minutes . during this polymerization , a relatively broadband color filter layer having a three - dimensional polymer network was obtained . finally , one of the two substrates was removed . fig3 shows diagrammatically a combination of the absorption spectrum and the reflection spectrum of the color filter layer described hereinbefore . the reference numerals 1 and 2 denote the absorption spectra of the dyes d and e . they leave open a relatively narrow transmission range between approximately 545 nm and 588 nm . the reference numeral 3 denotes the reflection spectrum of the cholesterically ordered material of the color filter layer for unpolarized light . this was measured perpendicularly to the layer in the absence of the dyes d and e . the reflection spectrum has a bandwidth of approximately 80 nm and ranges from 543 nm to 625 nm . due to the presence of said dyes , the color filter layer actually reflects only light in the range between 545 nm and 588 nm . the visible light outside this range is absorbed by the dyes d and e . the reference numeral 4 denotes the reflection spectrum of the cholesterically ordered material of the color filter layer for unpolarized light . this was measured at an angle of 45 ° under the normal of the layer and in the absence of the dyes d and e . under these circumstances , the entire reflection spectrum has moved to a lower wavelength and now ranges between approximately 525 nm and 608 nm . the bandwidth remains approximately equal ( 80 nm ). due to the presence of said dyes , the color filter layer now actually also reflects only light in the range between 545 nm and 588 nm . the visible light outside this range is absorbed by the dyes d and e . in the absence of the dyes d and e , the viewer would observe a clear color shift if he viewed the color filter layer at different angles . the presence of the dyes and the position of their absorption spectra with respect to the reflection spectrum of the color filter layer have the result that this color shift does not occur . the intensity of the filter also remains equal because there is a considerable overlap between said reflection spectrum and dye e at the edge and at the highest wavelength . fig4 is a diagrammatic cross - section of a liquid crystal color display device of the reflective type according to the invention . it comprises a transparent substrate 11 of , for example glass , a surface of which is provided with a black absorbing layer 12 , for example of a black lacquer . the other surface is provided with a thin orientation layer ( not shown ) on which a pattern of red ( r ), green ( g ) and blue ( b ) color filters is provided . in the relevant case , each filter consists of a layer polymerized to a three - dimensional network having a thickness of approximately 5 μm of cholesterically ordered liquid crystalline material having the wavelength associated with the desired color , and at least one dye . subsequently , a ¼λ retardation layer ( not shown ) of approximately 1 μm thickness is provided on the color filter layer thus formed , dependent on the birefringence of the liquid crystalline material . this retardation layer may be made of a uniaxially nematic liquid crystalline material or of a glass - forming liquid crystalline material . an orientation layer of rubbed polyimide is used for aligning this layer which can be provided by means of spin - coating . an electrode layer 13 of transparent material is provided on the retardation layer . good results are achieved with ito - like materials which can be provided in patterns by means of sputtering . an orientation layer 14 for orienting the layer 15 of liquid crystalline material to be switched is present on this electrode layer . this orientation layer is present between the above - mentioned substrate 11 and a second transparent substrate 17 which may also be made of glass . this substrate is also provided with an electrode layer 18 and an orientation layer 19 . the rows of electrodes of the electrode layers 13 and 18 jointly constitute an electrode array with which small areas ( pixels ) of a layer 15 can be driven via an electric field . the size of these areas approximately corresponds to the size of the smallest dimensions of the patterned color filter layer . the liquid crystal color display device shown in fig4 also comprises a polarizer layer 20 . this layer is provided on the surface of the substrate 17 remote from the substrate 11 . the color filter of the reflective display device according to the invention was manufactured as follows . a thin layer comprising the above - mentioned mixture of reactive acrylates with dyes was provided on the orientation layer on the substrate 11 . the ratio between the two acrylates was chosen to be such that the desired reflection wavelength range was obtained . this is the range between approximately 610 nm and 670 nm for the red pixels , the range between approximately 490 and 540 nm for the green pixels and the range between approximately 435 and 475 nm for the blue pixels . a small quantity ( approximately 0 . 2 % by weight ) of one or two dyes having the desired absorption characteristic was added to these mixtures . in the relevant case , these were the compounds f and g for the red pixels , the compounds f and h for the green pixels and the compounds h and i for the blue pixels . the chemical structure formulas of the compounds f ( abs max at 392 nm ), g ( abs max at 489 nm ), h ( abs max at 590 and 637 nm ) and i ( abs max at 539 nm ) are shown in fig2 . after a first layer was provided for , for example the red pixels , the layer was oriented by means of a matrix which was also provided with an orientation layer . subsequently , pattern exposure took place . after removal of the unpolymerized material with 2 - propanol , a second layer for , for example the green pixels was provided . it was provided with a matrix in the same manner and subjected to a pattern exposure . this method was finally repeated for providing the blue pixels . after the color filter layer has been provided , a thin planarization layer may be provided , if desired , before providing the retardation layer . subsequently , an electrode layer and an orientation layer were consecutively provided on the retardation layer . a display device was manufactured by means of the substrate thus obtained . a second substrate was provided with a polarizer , an electrode layer and an orientation layer as described with reference to fig4 and a cell was formed which was filled with a liquid crystalline material . the extent of color shift was examined by viewing the different pixel colors of the cell , both perpendicularly to the cell and at an angle of 45 °. it has proved to be possible to considerably suppress the color shift , which usually occurs when viewing the device from different angles , with the liquid crystal color display device of the reflective type described hereinbefore .