in a first embodiment of the invention , there is provided a printing member with combined functions of a printing plate and a recording film . referring now to fig1 there is shown a cross - sectional representation of a member of a first embodiment of the present invention , comprising substrate film 20 that is substantially transparent to ultra - violet and visible light . film 20 is coated with polymeric layer 21 , preferably based on an amino resin or a nitrocellulose resin , or a combination of the two . the thickness of this layer is less than 3 microns . polymeric layer 21 contains carbon black , an ultra - violet absorbing dye and optionally an infrared absorbing dye . amino resins are generally polycondensation products of carbonyl compounds with nh — functional compounds , an example of which is examples of useful compounds in this group are partially methylated melamine formaldehyde resins with a high content of methylol groups . an example of such a resin is cymel 386 ( dyno - cytec , botleweg 175 , 3197 rotterdam , the netherlands ), which is a proprietary material , described as having a medium degree of alkylation and a high imino functionality . the material is a complex mixture , containing different degrees of hydroxymethylation , alkylation and condensation attached around the melamine structure , as shown below : cymel 3865 is water - soluble and can undergo condensation reactions to form a strong hard film by acid catalysis — for instance using paratoluene sulfonic acid . a similar useful amino resin is sold under the trade name of cymel 373 ( dyno - cytec , botleweg 175 , 3197 rotterdam , the netherlands ), but has a low imino content giving greater flexibility , but lower curing speed . cymel 1170 ( dyno - cytec , botleweg 175 , 3197 rotterdam , the netherlands ) is a butylated glycoluril - formaldehyde amino resin used in this invention in solvent - based systems to cross - link with hydroxyl groups of nitrocellulose resin . examples of carbon blacks are cab - o - jet 200 and 300 . these are specially treated carbon black pigments , sold as aqueous dispersions and are used in this invention in the water - based coatings . mogul l ( cabot corporation , billerca , mass ., usa ) and regal 400r ( cabot corporation , billerca , mass ., usa ) are examples of carbon blacks , which may be used in the invention both in the water - based coatings and the solvent based coatings . if used , they need to be dispersed in the system by , for instance , high - speed cavitation , stirring , triple roller milling or by ball milling . the ultra - violet absorbing dye is usually a yellow one with an absorption peak between 320 and 400nm — what is known as the uva region . this region of the uv is commonly used in the processes of photopolymer plate - making . examples of water - soluble dyes suitable for this application are 4 phenylazo aniline hydrochloride , primulin ( direct yellow 59 ) and thioflavin ( direct yellow 7 ). examples of suitable solvent soluble dyes are 4 - phenyl azoaniline ( solvent yellow 1 ) and phenyl azophenol ( solvent yellow 7 ). fig2 shows the absorption spectrum of primulin by way of example . uppermost layer 22 is a protective surface comprised of a polysiloxane layer , which may contain a uv absorbing dye . the member is imaged by digital writing with an infrared source that ablates layers 21 and 22 , to leave a clean transparent substrate . thus , layer 21 is the infrared absorbent layer and layer 22 is the non - infrared absorbent , ablatable layer . layer 22 , on its own , would not be ablated using the level of energy used in the implementation of this invention . it is only ablated by transference of energy from layer 21 . if necessary , the surface is wiped clean with a dry or damp rag to remove any remnants of ablated material that remains on the surface after imaging . the combined coatings must give a measured optical density of not less than 3 . 0 both in the visible and uv ( all measurements were made with a macbeth td 904 densitometer ); the uppermost layer must protect the material from scratching , solvent and water attack , and other handling damage ; the fully ablated areas of the plate must have an optical transmission density of less than 0 . 2 ; the imaged member must function as a waterless offset printing plate and produce at least 10 , 000 good printing impressions . with the above stated combination of properties , a graphics arts customer can purchase and stock such a product for multiple uses . it can be used as a recording film mask to image any conventional presensitized offset lithographic printing plates . it is particularly suitable for use with both liquid and solid flexographic members as a contact mask . solid flexographic members have , in general , a slightly sticky surface and contact films are recommended to be matte . the member of this embodiment is shiny , permitting better film - to - plate contact , but at the same time , the silicone surface provides a release layer that prevents any sticking between the flexo surface and the recording film . also , the film can be used with a liquid flexo plate , without the need for an intermediate protective film . before use , the imaged film is treated with an oil or grease , which remains on the imaged areas and provides them with release properties . the resulting method improves the imaging quality by removing the intervening protective layer , which is generally used to protect the film from the liquid polymer . the member can also be used as a computer - to - plate waterless plate . after imaging of such a plate , the plate can be used in proofing processes , which generally use film masks such as those known commercially as chromalin ( du pont ) and matchprint ( kodak ). thus , the proofing is made using the exact image to be printed , avoiding all risks of errors . this is a unique application engendered by the combination of film and plate functions . such plate and film material may be imaged on computer - to - plate setters such as trendsetters and lotems manufactured and sold by creoscitex . it can also be imaged in on - press offset lithographic printing machines such as the heidelberg quickmaster di , wherein it would be supplied as a roll of master material . as intimated above , the film properties have significant advantages over conventional film . the film is handleable in daylight . in the unablated areas of the coating , it has a built - in d max , which does not vary with processing . it does not fog . it has no underexposure memory . it is close to being processless . it does not use environmentally problematic solutions , which have disposal problems as well as stability problems . a second embodiment is depicted in fig3 . substrate 20 is coated with carbon - loaded layer 23 , bonded with an amino resin combined with a cross - linked hydrophilic system , preferably with a uv absorbing dye and optionally with an infrared absorbing dye . layer 23 has a thickness between 0 . 5 and 3 microns . the member must have the following combination of properties : the coating must give a measured optical density of not less than 3 . 0 both in the visible and uv , as measured with a macbeth densitometer ; the uppermost layer must not be susceptible to scratching or other handling damage ; the fully ablated areas of the plate must have an optical transmission density of less than 0 . 2 ; the imaged member must function as a conventional wet offset printing plate and produce at least 10 , 000 good printing impressions . with the above - stated combination of properties , the graphics arts customer can purchase and stock such a product for multiple uses . it can be used as a recording film mask to image any conventional presensitized offset lithographic printing plates . it is particularly suitable for use with solid flexographic members as a contact mask . solid flexographic members have in general a slightly sticky surface and contact films are recommended to be matte . the member of this invention is matte and therefore suitable for use as a film with solid flexographic members . the member can also be used as a computer - to - plate conventional wet offset plate . after imaging of such a plate , the plate can be used in proofing processes where a photomask is used , such as those known commercially as chromalin ( du pont ) and matchprint ( kodak ). thus , the proofing is made using the exact image to be printed , avoiding all risks of errors . this is a unique application engendered by the combination of film and plate functions . such plate and film material may be imaged on computer to plate setters such as trendsetter and lotem machines manufactured by creoscitex . it can also be imaged in on - press systems where a conventional wet plate system is preferred over a waterless system . in its use as a plate , the ablation process of such a one - coat system as described herein removes most , if not all the ablated material by vacuum evacuation , which is usually part of the imaging system . the plate may be offered for printing without any treatment whatsoever , as any small amount of detritus is carried away on the roll - up copies that are wasted at the beginning of any printing run . as mentioned in the previous embodiment , the film properties have significant advantages over conventional film . the film is handleable in daylight . the unablated areas provide a built - in d max , which does not vary with processing . it does not fog . it has no underexposure memory . it is close to being processless . it does not use environmentally problematic solutions , which have disposal problems as well as stability problems . because of the multiplicity of functions of the above two embodiments , the same materials can be sold to a wider market and can have the opportunity of reduced costs due to economy of scale . the third embodiment involves the production of a combination of films and plates which are all ablatable and have a commonality of ingredients that reduces the costs of raw materials purchase and of production , but not necessarily with multi - functionality as described in previous embodiments . the three types of members are , by way of example , polyester recording film , wet offset plates , and dry offset plates . the common ingredients are , for example , a polyester substrate , carbon black , uv absorbing dye , amino resin , and a cross - linking catalyst . it is preferable that the substrate and ingredients used in all of the members are identical for optimum cost benefit , but if they are of the same generic type and are from the same supplier , this still provides sufficient advantage . in addition to the above combinations coated on polyester , it is also possible to include coatings on aluminum and the coating formulation mixture itself for plateless application , as described in the u . s . pat . nos . 5 , 713 , 287 and 5 , 996 , 499 to gelbart . example 1 describes the first embodiment as shown in fig1 where the material produced can perform the dual function of a waterless offset printing plate and a recording film that is used as a photomask . the following mixture was made up ( all quantities quoted as parts by weight ). first coat 1 . 98 % thioflavin solution in water 22 . 1 cymel 385 8 . 73 cab - o - jet 200 ( cabot corporation , billerca , 43 . 73 massachusetts , usa ) bayerscript solution ( bayer , phila ., pa usa ) 21 . 85 tegowet kl245 ( tego chemie service , hopewell 1 . 23 va 23860 ) cycat 4040 ( dyno - cytec , botleweg 175 , 2 . 36 3197 rotterdam , the netherlands ) the mixture was well stirred before coating with a wire wound rod onto clear 100 micron polyester and drying and curing at 140 ° c . for 4 minutes to give a dry film of 1 . 8 microns thickness . although this coating had been deposited from water solution , it was water insoluble after curing . the following second coat was mixed and then applied ; second coat alcosil part a 10 parts alcosil part b 5 parts alcosil gum 5 parts ( alcosil products from allcock and sons , ltd ., manchester , england ) the mixture was coated on top of the above coating and dried and cured at 140 ° c . for 4 minutes to give a dry film of 1 . 9 microns . the resulting film was shiny and not easily damaged by handling . it had a d max of 4 . 5 in the visible region and 4 . 0 in the uv region , as measured with a macbeth t0904 densitometer . the blank was imaged on a lotem flexo at 100 lines per millimeter at 600 mj / cm 2 . the image was wiped with a damp cloth and then gave a d min of 0 . 08 in the visible region and 0 . 1 in the uv . the resulting film was then capable of acting as a mask to image printing plates , or of being used as a printing plate , by printing on a water - cooled offset litho machine using waterless printing ink . example 2 describes the second embodiment as depicted in fig2 where the imaged member can be used as a recording film photomask and as a conventional wet offset lithographic printing plate . the following mixture was made up ( all quantities quoted as parts by weight ): 24 % water solution of 99 % hydrolyzed polyvinyl 12 . 92 alcohol kaolin 1 . 12 cab - o - jet 200 26 . 18 cymel 385 1 . 12 ethanol 2 . 2 aerosol ot ( bdh laboratory supplies , poole , 0 . 04 dorset , england ) 1 . 98 % thioflavin solution in water 6 . 46 the mixture was ball milled overnight and then 0 . 22 parts of cycat 4040 and 1 . 29 parts of titanium bis ( ammoniumlactohydroxide ) were added and mixed in . the mixture was coated to a dry thickness of 1 . 8 microns . the resulting film was matte and not easily damaged by handling . it had a d max of 4 . 5 in both the visible region and the uv region . the blank was imaged on a lotem flexo at 100 lines per millimeter at 600 mj / cm 2 . the image was wiped with a damp cloth and then gave a d min of 0 . 05 in the visible region and 0 . 1 in the uv . the resulting film was then capable of acting as a mask to image printing plates . it was suitable as a mask for solid flexographic plates . the imaged blank could also be mounted directly on an offset lithographic printing machine without cleaning in any way and was then printed using standard fount and printing ink . the following example demonstrates the third embodiment where there is commonality between all component members . this solution was bar - coated onto the first coat and was dried and cured at 140 ° c . for 4 minutes to a dry thickness of 0 . 7 microns . the resulting product was an infrared ablatable recording film of sensitivity of 600 mj / cm 2 , with a glossy surface that was extremely resistant to any surface scratching , delamination or general damage . it had a d min of 0 . 08 in the visible region and 0 . 1 in the uv . it had a d max of 4 . 5 in the visible region and 4 . 0 in the uv region , as measured with a macbeth t0904 . 24 % water solution of 99 % hydrolyzed polyvinyl alcohol 6 . 46 kaolin 1 . 12 cymel 385 1 . 12 ethanol 2 . 2 aerosol ot 0 . 04 1 . 98 % thioflavin solution in water 6 . 46 this formulation was bar - coated and dried and cured to a thickness of 0 . 7 microns . the product was an infrared ablatable conventional wet offset lithographic printing plate of sensitivity 600mj / cm 2 . dehesive 410e ( wacker chemie gmbh , munich germany ) 68 water 25 cymel 373 11 cycat 4045 2 . 9 v72 ( wacker chemie gmbh , munich germany ) 13 superwetting agent ( dow corp . midland mi , usa ) 3 this was coated onto the first coat and cured to a dry coating thickness of 2 . 5 microns . the resulting member was a processless infrared ablatable wet conventional offset printing plate . the above three members constitute a group of products with a commonality of ingredients . they have the same substrate , the same first coat , and all contain amine resin systems in the top coat . two , out of three , have the same amine resin and catalyst ; the third has an amine and catalyst from a common manufacturing source . the two plate material formulations can also be coated onto an aluminum or anodized aluminum substrate to give more robust plates . the mixture used in example 2 can be sprayed onto a thermally insulative surface of a plate cylinder of an offset lithographic printing press , dried and cured , and then imaged by ablation . the surface will then constitute a printing plate surface and can be used in conventional wet offset printing to produce multiple impressions . at the end of the run , the surface is washed with a material such as ethyl lactate which removes the entire layer and the material is then re - coated onto the drum for use in the next printing job . this is in accordance with the gelbart u . s . pat . no . 5 , 713 , 287 . the following mixture was made up ( all quantities quoted as parts by weight ): methyl ethyl ketone 76 . 99 4 phenylazoaniline 0 . 69 cellulose nitrate 4 . 66 molgul l carbon black . 15 . 64 cymel 1170 1 . 79 this mixture was ball milled over a period of 24 hours and then 0 . 24 parts of cycat 4040 added . it was then coated onto 100 micron polyester and dried and cured at 140 ° c . for 4 minutes to a dry thickness of 2 . 5 microns . this coating was easily scratched . the following mixture was made up ( all quantities quoted as parts by weight ): water 67 . 96 cymel 385 28 . 58 tegowet 245 0 . 88 syloid 7000 ( w . r . grace and co ., cambridge , england ) this mixture was ball milled overnight and 1 . 25 parts of cycat 4040 added . the mixture was gap - coated to a dry thickness of 1 . 5 microns and dried and cured at 140 ° c . for 4 minutes . the resulting film had a matte finish , had a d max of 3 . 8 and after imaging had a d min of 0 . 18 in the visible and d max of 4 . 1 and d min of 0 . 16 in the uv . it was scratch - resistant and fit to use as a photomask for preparing , by way of example , any dry flexographic printing plates . the above - mentioned first coat of this example was coated onto 170 micron polyester and cured and dried as described above . it was then coated with the second coat of example 3 , member 3 , to give a waterless printing plate of similar performance . the above - mentioned first coat of this example was coated onto a 170 - micron polyester and cured and dried as above . it was then coated with the second coat of example 3 , member 2 , to give a conventional , wet offset printing plate of similar performance . having described the invention with regard to certain specific embodiments thereof , it is to be understood that the description is not meant as a limitation , since further modifications may now suggest themselves to those skilled in the art , and it is intended to cover such modifications as fall within the scope of the appended claims .