for completing the present invention , a basic experiment was conducted with a refining apparatus similar to one illustrated in fig4 which experiment proved that : ( 1 ) when the molten metal is maintained in a relatively shallow layer , general de - oxidizing - and - sulfurizing refining can be achieved by means of performing a slag refining while blowing an inert gas of low pressure from a porous plug and giving heat to the molten metal by electrode heating . ( 2 ) when the molten metal is maintained in a relatively deep layer , refining of de - oxidation , - sulfurization , - nitrogenation and - hydrogenation can be performed by means of blowing a flux into the molten metal with the aid of an inert gas of high pressure blown from the tuyere . in other words , it is possible , in the course of the first refining process of 20 minutes shown in fig1 to reduce the oxygen content in the molten metal below 50 p . p . m . by means of ( i ) heating of the molten metal with a hollow electrode , ( ii ) making an atmosphere above the molten metal inert by blowing of argon gas on to the surface of the molten metal through a bore of the hollow electrode , and ( iii ) stirring the molten metal by the argon gas blown from the porous plug . and it has been further proved that the oxygen content can be reduced to as low as 15 p . p . m in the course of the second refining process about 10 minutes , wherein reaction between the molten metal and the flux is expedited , by means of blowing the flux such as cao , al 2 o 3 , etc . by the flow of argon gas from the tuyere into the molten metal , and an ingot of extremely low oxygen content can be obtained by pouring the molten metal into an casting mold under the atmosphere of inert gas . through the first and second experimental refining processes the sulfur content in the molten metal was reduced to 0 . 006 % as shown in fig2 ; and the rate of desulfurization reached 77 % an average . it was also proved that only blowing of inert gas in the second refining was sufficient for the treatment of degassification . and the hydrogen content after the finish of the second refining could be reduced to below 2 . 7 cc / 100 g as shown in fig3 because the p h . sbsb . 2 o in the vessel was reduced and the refining of dehydrogenation was carried out by the blowing of large amount of argon , throughout the first and second refining courses . an example of refining process in accordance with this invention , based on the experimental result above - mentioned , is illustrated ranging fig4 through fig7 . a refining vessel 1 of pot type employed there was made of an outer shell of iron and a lining 1b of refractory , and it could be turned to be tilted , as shown in fig4 - 7 , about a shaft 6 ( vessel turning axis ) attached to the side thereof at a substantially central position by means of a rotating device well known such as gears , motor , driving cylinder , etc . ( not shown ). an upper opening 1c of the vessel 1 is for operation of , such as charging of molten metal , putting - in flux , removing slag , or dust collecting . it also may be used as an electrode inserting opening when the electrode heating is carried out . actually three hollow electrodes 8 , having an axial through - bore 8a for passing inert gas into an inner refining chamber 5 of the vessel 1 , are inserted through a main hole 2 formed in a furnace lid 7 made of refractories . the furnace lid 7 is also provided with a sub - hole 2a for charging the flux and / or additional alloy component ( s ) therethrough supplied from a removably disposed reservoir 9 of flux and / or additional alloy component ( s ). furthermore , a tuyere 4 is formed piercing through in the upper - portion of the vessel &# 39 ; s one side wall downwardly slant toward inside , such that the inside opening thereof is positioned above the free surface of the molten metal m , more particularly speaking , the surface of the slag s , for not touching or contacting the molten metal m when the vessel 1 is uprightly postured as in fig4 . the tuyere 4 is for blowing inert gas such as argon or nitrogen and charging along therewith flux , deoxidant ( s ) and additional alloy component ( s ) such as nio , moo 3 , wo 3 , ca powder , mg powder , ca - si alloy , etc . ; so the tuyere 4 is formed steeply ( sharply ) slanted such that even when the vessel 1 is tilted to the extent as in fig5 the inert gas can be effectively blown deep into the lower part of the molten metal m in a slant downward direction . numeral 3 designates a porous plug , through which any necessary gas such as inert gas can be blown into the molten metal m when the arc heating is carried out by the electrodes 8 . numeral 11 designates a sliding nozzle , through which the molten metal m in the vessel 1 can be discharged into a ladle or casting mold when a blockade member is shifted to communicate a pouring gate 10 of the vessel 1 with the outside . refining method applied in the refining of a molten alloyed steel which was carried out in a refining apparatus of the above - mentioned structure will be described next . after having charged the molten steel m into the vessel 1 maintained at the upright position as in fig4 while blowing on the other hand argon gas through the porous plug 3 , so that the vessel inside may be filled with the atmosphere of argon gas , the furnace lid 7 of refractories is fastened . then the flux reservoir 9 is shifted in the direction of the arrow ( solid line in fig4 ), followed by charging through the sub - hole 2a of a basic flux s of , for example , cao -- caf 2 -- al 2 o 3 -- sio 2 series or cao -- al 2 o 3 -- sio 2 series into the molten steel m and blowing of argon gas through the porous plug 3 into the molten steel m . while stirring the molten steel m by the blown argon gas in the direction of the arrow , the arc heating is carried out by the electrodes 8 of graphite to maintain the temperature of the molten steel m at a sufficient level needed for the second refining process . in the course of this process inert gas is blown through the bore 8a of the hollow electrodes 8 , too , thereby reaction between the flux s and molten steel m is also performed right below the electrodes 8 , which experimentally brought about the result of reducing the impure elements in the molten steel m such as sulfur , oxygen , etc . to a trace amount in an extremely short span of time . it is also possible to put in the course of refining a suitable amount of alloy component ( s ) from the reservoir 9 , through the sub - hole 2a , into the molten steel m with the purpose of adjusting the composition of the alloyed molten steel m aimed . when the refining and adjusting of the alloy composition has been finished , the reservoir 9 is shifted in the direction of the dot - lined arrow , followed by removing or lifting of the electrodes 8 . and the vessel 1 is rotated in the arrowed direction as far as the position shown in fig5 . strongly blown inert gas and flux from the tuyere 4 into the molten steel m for stirring the same expedite the reaction with the flux s , which rapidly progresses the de - sulfurizing - and - oxidizing refining . in the meantime foams of the rising - up inert gas allows nitrogen and hydrogen in the molten steel m to diffuse thereinto . upon having finished the above - mentioned refining process the vessel 1 is rotated in the direction of the arrow back to the position illustrated in fig6 . then the molten steel m is poured into a casting mold ( not shown ) through the sliding nozzle 11 . then the vessel 1 is rotated again to be turned to the position in fig7 for exhausting the slag s into a slag ladle 12 . an example of manufacturing the commercially available scm 420 steel [ jis - g - 4108 ( 1979 )] will be explained in accordance with the operational conditions shown in table 1 . table 1__________________________________________________________________________sort of steel c si mn p s cu ni cr mo__________________________________________________________________________scm 420 (%) 0 . 18 0 . 15 0 . 06 & lt ; 0 . 030 & lt ; 0 . 030 & lt ; 0 . 30 & lt ; 0 . 25 0 . 90 0 . 15 - 0 . 23 - 0 . 35 - 0 . 85 - 1 . 20 - 0 . 30__________________________________________________________________________blowing gas ar gas charged material ## str1 ## chargetiming molten first refining second refining discharge steel refer toposition of vessel refer to fig4 refer to fig5 fig6 __________________________________________________________________________ c ## str2 ## ## str3 ## ## str4 ## ## str5 ## si 0 . 020 0 . 30 0 . 30 0 . 30 mn 0 . 055 0 . 75 0 . 75 0 . 75 p 0 . 015 0 . 015 0 . 015 0 . 015ingredients s 0 . 025 0 . 011 0 . 005 0 . 005of the ni 0 . 15 0 . 15 0 . 15 0 . 15molten cr 0 . 95 1 . 10 1 . 10 1 . 10steel mo 0 . 25 0 . 25 0 . 25 0 . 25 (%) o 0 . 022 0 . 0030 0 . 0013 0 . 0013 h 5 . 8 5 . 8 1 . 8 1 . 8 ( ppm ) n 0 . 01 0 . 01 0 . 005 0 . 005__________________________________________________________________________temperature of 1 , 600 1 , 730 1 , 645 1 , 640molten steel (° c . ) __________________________________________________________________________ in the first refining process , scm 420 molten steel m melted in a separate arc melting furnace is poured into the refining vessel 1 which is held in a position illustrated in fig4 followed by a blowing of inert gas through the bore 8a of the electrodes 8 while heating supplementarily the molten steel m by supplying power of arc heating . then system caco 3 -- caf 2 flux s and additional alloy material which should be charged from the reservoir 9 through the opening 2a are heated for melting . argon gas blown through the porous plug 3 under this circumstance at the rate of 15 l / min . ton brings about the molten steel m continuously to right under the electrodes 8 to raise the temperature of the same . de - oxidizing - and - sulfurizing refining of the molten steel m and the slag s progresses to reduce o content from 0 . 022 % down to 0 . 003 % and s content from 0 . 025 % to 0 . 011 %. thereafter in this experiment the electrodes 8 were removed and the reservoir 9 was moved in the direction of the dot - lined arrow , followed by the tilting rotation of the vessel 1 as far as the position shown in fig5 for preparing the second refining process . in this process system cao -- al 2 o 3 flux was intermittently blown into the molten steel m accompanied by argon gas . soon after that large amount of argon gas ( 500 l / min . ton ) was blown into the molten steel m to carry out the de - oxidizing - and - sulfurizing refining while strongly stirring the same . o content was reduced from 0 . 003 % to 0 . 001 % and s content from 0 . 011 % to 0 . 005 %. and h was reduced from 5 . 8 cc / 100 g to 1 . 8 cc / 100 g and n , too , from 0 . 010 % to 0 . 005 %. this invention showed in this way great characteristic feature , which never could be seen in the prior art , i . e ., refining in the arc melting furnace , through the first and second refining in obtaining the molten steel of low oxygen , sulfur , and hydrogen content . the next step is to turn the vessel 1 to a posture shown in fig6 for being fixed there to pour the molten steel m , by opening the sliding nozzle 11 , through the pouring gate 10 into a mold or a ladle ( not shown ). operation of this sort is preferable to be carried out under the atmosphere of inert gas . afterwards the refining vessel 1 is turned again in the direction of the arrow to be tilted to the position shown in fig9 for exhausting the slag s through a slag exhaust opening 2a to a slag ladle 12 . incidentally it is also possible to carry out this operation of pouring the molten steel only by tilting the vessel 1 , without opening and passing the sliding nozzle 11 . it has further been found , in the further study in respect to the refining operation employing the refining apparatus provided with heating , tilting , and gas blowing means as mentioned above , that the blowing of the inert gas ( es ) in the course of refining could effectively remove harmful metallic contents in the molten steel such as pb , zn , bi , te , etc ., in particular , elements of high vapor pressure . this enabled the removal of harmful metallic substances contained in the molten steel almost completely . an experimental result which was obtained from an argon gas treatment applied on a molten steel of jis - g - 4104 scr 420 containing , as harmful elements , 30 - 40 p . p . m . pb , 15 - 22 p . p . m . zn , 10 p . p . m . or more bi and te , in a secondary refining apparatus of 3 ton capacity with the structure shown in fig8 and 9 is made into graphs of fig1 and 11 . the result in fig1 and 11 are plotted regarding the relation between the time of blowing of the argon gas , which was blown at various rate from the tuyere 4 , and the concentration of pb or zn in the molten steel . fig1 shows the relation between the blowing rate of the inert gas ( argon in this case ) and the rate constant of pb and zn removal computed from the results of fig1 and 11 as follows : ## equ1 ## wherein c : pb or zn concentration as clearly can be seen in fig1 rate constant ( k ) of pb and zn removal rapidly increases in proportion to the blowing speed of the inert gas ( argon ) up to 700 nl / min . ton . but the varying of the rate constant of pb and zn removal in the range exceeding 700 nl / min . ton , begins to dull . under the blowing condition of the inert gas exceeding 700 nl / min . ton the efficiency of pb and zn removal by the blown inert gas is degraded chiefly due to progressing of the temperature descending of the molten steel . considering the cost of the expensive inert gas , the cost increase of the heating by the electrodes caused by the increase of heat loss , the minus elements of economical aspect appear conspicuous . lowering of the blowing rate of the inert gas naturally deteriorates , on the other hand , the rate of pb and zn removal , i . e ., brings about an efficiency degradation . assume the lowest limit of this efficiency is 10 minutes , then the blowing rate of the inert gas , required to decrease the pb / zn concentration down to 1 / 2 of the initial concentration within 10 minutes , must be over 200 nl / min . ton or so . it is therefore recommendable to settle the blowing rate of the inert gas ( amount of the blown inert gas every second per 1 ton molten steel ) from the inert gas blowing means such as a tuyere , necessary for performing pb and zn removal effectively , within the range 200 - 700 nl / min . ton . as to other harmful metallic elements such as bi , te similar results were observed . at the blowing speed of 300 nl / min . ton in case of bi , descending of the content ratio from 12 p . p . m . down to 2 p . p . m . was obtained after 10 minutes . in case of te , descending from 16 p . p . m . to 8 p . p . m . in ten minutes was observed . as to the refining apparatus employed in the refining process of molten metals in accordance with this invention , those having the shape shown in fig8 and 9 are also recommendable as desired . the refining vessel 1 shown in fig8 and 9 is , at the molten metal m accommodating portion , of almost spherical and the upper portion above the surface of the molten metal m , when the vessel 1 is postured upright position , is of truncated cone , which largely features this type of vessel . chief merits of this refining vessel reside in ( 1 ) diminishing the space of the refining chamber 5 , which facilitates maintaining the same under non - oxidizing atmosphere ; ( 2 ) consequently diminishing heat diffusion to outside of the furnace with the result of enhancing the effect of heat - refining ; ( 3 ) facilitating exhaust of the slag by tilting the vessel 1 in a manner shown in fig7 . in fig8 and 9 common portions with those in the previous figures the same numerals are alloted for omitting the superfluous explanation . for removing harmful or unnecessary impurities , such as non - metallic or metallic components , in the refining process of molten metals , the amounts of argon or other inert gas blown from the porous nozzle 3 in the first refining is generally preferable to be in the range of 5 - 30 nl / min per 1 ton of the molten metal , and the similar gas from the tuyere 4 in the second refining is recommendable to be in the range of 100 - 700 nl / min per 1 ton of the molten metal . the reducing - refining under the inert atmosphere in accordance with this invention , which is carried out with arc heating while stirring the molten metal strongly , is capable of , as mentioned above in greater detail , performing the manufacture of alloyed metal of high purity , largely contributing to the development of industry . in place of the hollow electrodes of graphite employed in the arc heating in the above embodiment , solid graphite electrodes and plasma arc torches can be utilized . mixing small amount of oxygen gas with the inert gas is good for performing decarburizing refining . it is also permissible to replace partly or entirely the argon gas by nitrogen gas . transportation of the refining vessel 1 by a crane or a trailer , and receiving the molten metal from the blast furnace or pouring the molten metal from the vessel 1 directly into the ladle or the mold by the similar medium is possible . all of those processes are desirable to be carried out under the atmosphere of inert gas . in the previous explanation the electrodes 8 were removed from the vessel 1 in the second refining , but instead they may be lifted to some extent , without being completely taken out , while the vessel 1 is tilted , provided that the electrodes 8 are not contacted with the molten metal m in the vessel 1 . furthermore , the sign nl / min should be understood to indicate a volume ( l ) of the inert gas under normal state , i . e ., n . t . p . per a unit of time ( min ). the present invention is by no means limited to the above - mentioned example ( embodiment ). variations or modifications can be easily made for those skilled in the art without departing from the spirit and scope of the invention .