the abradable seal of the present invention comprises a matrix - forming metal alloy component , a solid lubricant component and a ceramic component , wherein the three components provide a synergism in abradable coatings which have unexpected superior characteristics over prior art materials . the matrix - forming metal alloy is selected from the metals ni , co , cu , fe and al and combinations and alloys thereof , preferably nicral , nicr , cual and alsi . the ceramic component is typified by oxidic ceramics such as ceramics in the group comprising albite , illite and quartz and mixtures thereof and preferably is clad with a metal alloy by a hydrometallurgical process well known in the art prior to blending with particles of a lubricant such as hexagonal boron nitride , graphite , calcium fluoride , lithium fluoride and molybdenum disulphide particles , preferably hexagonal boron nitride . a preferred combination of metal alloy or oxidic ceramic is at least one of or a mixture of albite , illite and quartz clad with a nicral coating on the ceramic . a material found to be satisfactory is commercially available as durabrade ™ 2313 from westaim ambeon . another preferred combination of materials is hexagonal boron nitride and alumina - silica - based ceramics in a total amount of 10 to 50 wt %, the balance nickel alloy . the clad ceramic particles can be blended with particles of hexagonal boron nitride available from commercial suppliers . the ceramic and lubricant components together comprise at least 5 wt % and not more than 60 wt % of the composition , preferably 19 to 60 wt % and more preferably about 25 to 45 wt % of the composition , the balance comprising the matrix metal material . the ratio of solid lubricant to ceramic is 1 : 7 to 20 : 1 , preferably 1 : 6 to 9 : 1 . although the description proceeds herein with reference to a blend of clad ceramic particles and hexagonal boron nitride , it will be understood that the composition may also be prepared in the form of mechanical blends of the three components , homogenously agglomerated particles , mechanically fused particles , agglomerated ceramic and solid lubricant particles clad with metal alloy or mixtures of metal clad ceramic and metal clad solid lubricant , or as a continuous solid or cored wire . the three - phase composition of the invention preferably is applied to a substrate by thermal spray to form an abradable seal . thermal spraying involves the softening or melting of a heat fusible material such as metal or ceramic by heat , and propelling the softened or melted material in particulate form against a surface to be coated . the heated particles strike the surface where they are cooled and bonded thereto . a conventional thermal spray gun may be used for the purpose of the both heating and propelling the particles . a thermal spray gun normally utilizes a combustion or plasma or electric arc to produce the heat for melting of the composition in either powder or wire form . in a powder type combustion thermal spray gun , the carrier gas , which entrains and transports the powder , is typically an inert gas such as argon . in a plasma spray gun , the primary plasma gas is generally argon or nitrogen . hydrogen or helium is usually added to the primary plasma gas , and the carrier gas is generally the same as the primary plasma gas . other thermal spray methods could also be used . a good general description of thermal spraying is provided in u . s . pat . no . 5 , 049 , 450 . the matrix - forming metal alloy powder such as nicral can be dry blended and mixed with the ceramic powder and the lubricant powder , at least one of the ceramic powders and the lubricant powders preferably having a coating of the matrix - forming metal alloy thereon . the matrix metal alloy holds the particles of the ceramic and the solid lubricant in place and adherently bonds the coating to the substrate . the resulting product is a homogenous abradable seal material comprising the continuous metallic matrix phase which provides structural strength to the composition up to at least an operating temperature of 815 ° c . the solid lubricant decreases the hardness and strength of the metallic matrix material due to its uniformly dispersed presence as solid soft lubricant particles to enhance ejection of the particles from the coating when abraded . due to the softness of the lubricant , blade wear is decreased and abradability of the coating is improved . the solid lubricant occupies pore spaces between the metal matrix and ceramic particles to provide a dense structure which will function as a heat sink having enhanced thermal conductivity to conduct heat from the rub zone of the seal . the ceramic component provides enhanced erosion resistance while contributing to the decrease in matrix strength with improved abradability . during the rubbing process by the titanium alloy compressor blades , the seal material abrades readily due to low matrix strength caused by the synergistic effect of the solid lubricant and the ceramic materials . the metal alloy matrix would collapse and compress during the rubbing process without the presence of the ceramic and solid lubricant filler . the coating would become very hard and would glaze with subsequent significantly decreased abradability . coating glazing thus is limiting by facile particle ejection when rubbed by a compressor blade while acceptable erosion resistance is maintained by the addition of the ceramic material . the solid lubricant and ceramic particles are uniformly dispersed throughout the deposited coating . thus any material removal that occurs does not change coating properties of the remaining seal . coatings of the invention prepared by thermal spraying the coating composition onto a substrate have an excellent combination of abradability and erosion resistance as a result of the coating properties including low coating cohesive strength , low porosity , low surface roughness and high thermal conductivity . as a result , the coatings can be effectively used in combination with titanium - alloy blades without danger of titanium fire , coating glazing or excessive blade wear . overall engine efficiency is increased . if it should be desired to increase porosity of the abradable seal , a particulate polymer having a size range of 1 to 200 μm can be blended with the three - phase composition material in an amount of 1 to 30 wt % of the composition prior to thermal spraying . the fugitive polymer is vaporized , burned out or leached to yield a porous and permeable coating . a list of the polymers which can be used is in u . s . pat . no . 4 , 917 , 960 , incorporated herein by reference . the abradable seal of the invention will now be described with reference to the following non - limitative example . commercially available durabrade ™ 2313 powder produced by westaim ambeon having a particle size in the range of − 100 + 200 mesh was blended with 15 wt % of hexagonal boron nitride lubricant having a particle size of − 100 + 200 mesh sold by advanced ceramic corp . under the name ac 6001 . the total of the ceramic and lubricant particles comprised 32 wt % of the powder composition , the balance nicral alloy . the powder blend was flame sprayed ( oxygen - acetylene mixture ) onto a substrate and the resulting coating properties were compared with the co - alloy based seal described in u . s . pat . no . 5 , 434 , 210 and sold as sm 2042 by sulzer metco : applicants &# 39 ; co - based seal seal ( u . s . pat . 5 , 434 , 210 ) density [ g / cm 3 ] 3 . 4 2 . 68 hardness ( hr15y ) 19 40 ambeon erosion 90 ° [ g / min ] 0 . 5 2 . 05 ambeon erosion 90 ° [ mm 3 / min ] 147 765 coating strength [ psi ] 299 788 deposition efficiency [%] 47 n / a thickness [ mm ] 2 2 abradability ( blade wear [ inch ]) 1000 - 0 . 0002 - 0 . 03 * 0 . 001 0 . 003 820 - 0 . 02 - 0 . 03 0 . 008 0 . 026 * abradability was measured using a ti alloy test blade that rubbed against tested seals . test conditions were : 1000 and 820 ft / s blade tip speed , 0 . 0002 and 0 . 02 in / s incursion rate and 0 . 03 inch total incursion . all rub paths of the seal of this invention were smooth with no glazing or discoloration . the particles of the ceramic and the boron nitride were uniformly dispersed throughout the coating . the good properties of the applicants &# 39 ; seal are demonstrated by substantially - improved erosion resistance and abradability performance compared to the co - based seal . it will be understood , of course , that modifications can be made in the embodiments of the invention illustrated and described herein without departing from the scope and purview of the invention as defined by the appended claims .