the essential components in the composition of the present invention are a chlorinated polyolefin and an optical brightener . the chlorinated polyolefin may be a chlorinated copolymer of ethylene , propylene and copolymers thereof with homopolymers of polypropylene being preferred . typically , the chlorine content of the chlorinated polyolefin will be about 15 to 75 percent by weight based on total weight of the monomer . the chlorinated polyolefins are available industrially as high chlorinated products , that is , 55 to 75 percent by weight chlorine , and as low chlorinated products , that is , 15 to 50 percent by weight chlorine , with the low chlorinated products , particularly those of polypropylene , being preferred . the chlorinated polyolefins are usually prepared by polymerizing the olefin or mixture of olefins in an inert organic diluent in the presence of a low pressure polymerization catalyst . after polymerization , the catalyst is deactivated and the resultant polyolefin reaction mixture is treated with a chlorinating agent to produce the chlorinated polyolefin product . chlorinated polyolefins are available industrially from eastman kodak company as cp - 343 - 1 and cp - 515 - 2 and from toyo kasei kogyo co ., ltd . under the trademark hardlen . the chlorinated polyolefin is usually present in amounts of at least 10 , preferably 20 to 80 percent by weight based on total solids weight of the composition . amounts less than 10 percent by weight are undesirable because of insufficient adhesion promotion . the optical brighteners are compounds that absorb ultraviolet light and convert the energy taken up into the longer wavelength visible portions of the spectrum . this is evidenced by a fluorescence . any optical brightener can be used in the practice of the invention as long as it can be formulated along with the chlorinated polyolefin into a composition which can be applied to the polyolefin substrate as a substantially continuous film . typically , the optical brighteners are aromatic or heterocyclic compounds often with condensed ring structures and with an uninterrupted chain of conjugated double bonds . examples of optical brighteners are derivatives of diaminostilbenedisulfonic acid such as the bistriazinyl derivatives , i . e ., those compounds of the structure : ## str1 ## where x , x &# 39 ; and y and y &# 39 ; can be the same or different and include amino , substituted hydroxyl and chloro . examples of other optical brighteners are bisazoles such as those of the structure : ## str2 ## where r is hydrogen , alkyl and alkoxy and x is an unsaturated radical such as : ## str3 ## bisazoles are preferred in the practice of the invention because of their intense fluorescence upon exposure to uv light , and the compounds 2 , 2 &# 39 ;-( 2 , 5 - thiophenediyl ) bis ( 5 - tert - butylbenzoxazole ), that is , r equals tertiarybutyl and x equals ## str4 ## in the formula above , is especially preferred . the optical brightener is preferably present in the composition in amounts of at least 0 . 1 , usually 0 . 1 to 2 . 5 percent by weight based on total solids weight of the composition . amounts less than 0 . 1 percent by weight do not provide sufficient fluorescence upon exposure to uv light . the upper limit of optical brightener is not known with certainty , however , amounts greater than 2 . 5 percent by weight offer no particular advantage and increase the cost of the composition . however , amounts greater than 2 . 5 percent can be used if desired . the compositions of the present invention also contain an organic diluent to reduce the viscosity of the compositions and to make them suitable for coating applications . the organic diluent should be a material which will disperse or preferably dissolve the chlorinated polyolefin and optical brightener . non - polar solvents such as aromatic hydrocarbons , halogenated hydrocarbons and cycloaliphatic hydrocarbons can be used and are preferred . polar solvents such as alcohols , ketones and esters may be used if used in minor amounts with non - polar solvents but their use is not preferred . examples of suitable solvents include toluene , xylene , methylene chloride and cyclohexane . the organic solvent is usually present in the composition in amounts of about 50 to 98 , preferably 70 to 95 percent by weight based on total weight of the composition . amounts greater than 98 percent by weight are undesirable because of poor film build ; whereas amounts less than 70 percent by weight result in a composition which is very viscous and hard to handle . the composition can contain optional ingredients such as other resinous materials and pigments . other resinous materials are often desirable to assist in the development of a continuous film and to provide for increased adhesion to the subsequent layer of paint . examples of suitable adjuvant resins are vinyl acetate copolymers such as ethylene - vinyl acetate copolymers , alkyd resins , acrylic resins , and graft copolymers of vinyl monomers and alkyd resins . vinyl acetate copolymer resins are preferred because in combination with chlorinated polyolefins , they provide a good combination of film - forming and adhesion - promoting properties . the co - resinous ingredients , if used , are preferably present in the compositions in amounts of up to 89 , preferably 19 to 79 percent by weight based on total solids weight of the composition . the compositions of the invention can optionally be pigmented which provides color and conductivity to the coating . examples of suitable pigments include titanium dioxide and carbon black . when used , the pigments are typically used in a pigment - to - resin weight ratio of about 0 . 01 to 0 . 2 : 1 . as mentioned above , the compositions of the present invention are applied to polyolefin substrates , particularly those substrates used in the fabrication of automobile bodies and trim such as bumpers , front end fascia and filler panels which are located between the bumper and the chassis . usually , these flexible parts are made from thermoplastic polyolefin resins which are made by polymerizing olefins such as ethylene and propylene including copolymers thereof . the polyolefins most often used in the fabrication of automobile body parts and trim are ethylenepropylene copolymers which also contain a small amount of a nonconjugated diene such as dicyclopentadiene . typical polymers are those containing from 50 to 75 percent by weight ethylene , 25 to 45 percent by weight propylene and 2 to 8 percent by weight non - conjugated diene . these polymers are available industrially from republic substrates co . and research polymers co . the compositions of the invention can be applied to the polyolefin substrate in any of the ways commonly used for applying coatings to substrates . the compositions can be applied by brushing , roll coating and spraying as long as a substantially continuous uniform film is formed on the substrate . care should be taken that the correct amount of the composition is applied to the substrate . if the coating is too thick or too thin ( non - uniform ), adhesion failure of the substrate to the paint layer may result . spraying is the preferred method of applying the composition to the substrate because it provides for the greatest control of coating thickness . preferably , the coating thickness is controlled to levels of about 2 to 20 and more preferably from 3 to 15 microns . air or airless spraying can be used . after the coating has been applied to the substrate , it is usually given an air flash to permit the solvents to volatilize . preferably , the coating is then given an exposure to intense uv light such as from a medium pressure mercury arc lamp . such lamps emit radiation over the range of 220 to 1400 nanometers ; emitting principally at 254 , 313 and 365 manometers . exposure of this sort is not for the purpose of detecting coverage but seems to improve the adhesion promoting characteristics of the coating . exposure need not be long but is usually at least 5 seconds , typically 5 seconds to 2 minutes . the coated substrate is then exposed to uv light in the near , that is , about 360 - 370 nanometers , uv visible wavelength region to detect the uniformity of the coverage of the composition over the substrate . light from this source , i . e ., black light , is absorbed by the optical brightener and converted to energy in the visible portion of the spectrum where it appears as a fluorescence . by exposure of the coated substrate to the black uv light source and the resultant fluorescence , one can readily see whether the composition has been applied uniformly across the surface of the substrate . if different portions of the substrate fluoresce with different intensities or do not fluoresce at all , then the composition has not been applied uniformly and adhesion of the substrate to the layer of paint is uncertain . the polyolefin substrate can then be cleaned , recoated with the composition and evaluated again . cleaning is easily accomplished by treating the coated substrate with an aromatic solvent . this is preferable to painting the substrate and finding out that the adhesion is unacceptable . the paint must then be stripped from the substrate or the painted part scrapped , both of which are costly . the layer of paint which is applied to the primed substrate described above is typically an elastromeric paint which is industrially available from many companies supplying the automotive industry . a typical paint is that provided by ppg industries , inc . under the trademark durethane . specific paint products are durethane 700 and durethane 800 . the paint is typically cured at a temperature of 70 °- 120 ° c . for 15 to 40 minutes . the present invention will be more fully understood from the following illustrated examples wherein all quantities , percentages and ratios are on a weight basis unless otherwise indicated . a coating composition containing a chlorinated polyolefin and an optical brightener was prepared by first preparing a pigment paste followed by incorporation of the optical brightener into the pigment paste . the pigment paste was prepared from the following mixture of ingredients : ______________________________________ingredient parts by weight ( in grams ) ______________________________________v + p naphtha 41 . 20cyclohexane 32 . 96toluene 90 . 64elvax 260 . sup . 1 20chlorinated polyolefin . sup . 2 20tio . sub . 2 1 . 2______________________________________ . sup . 1 ethylenevinyl acetate copolymer available from e . i . dupont de nemours and company . . sup . 2 chlorinated polypropylene ( 25 percent chlorine ) available from eastman kodak company as cp 3431 . the v + p naphtha , cyclohexane and toluene were mixed together and heated to about 50 ° c . the elvax 260 and cp 343 - 1 were first dissolved in the heated solvent mixture followed by the addition of the tio 2 . the mixture was then ground in a zircoa mill to a hegman no . 7 grind . the optical brightener was incorporated into this pigment paste to form a sprayable coating composition as follows : ______________________________________ingredient parts by weight ( in grams ) ______________________________________pigment paste 206optical brightener . sup . 1 2cyclohexane 309toluene 309______________________________________ . sup . 1 uvitex ob available from cibageigy used as a 5 percent by weight solution in toluene . the ingredients were mixed together in the order indicated with low shear mixing to form the coating composition containing 0 . 1 percent optical brightener based on weight of total solids . the coating composition was sprayed onto a thermoplastic polyolefin substrate ( eta 3131 available from republic substrates ) to form a substantially continuous film having a thickness of about 10 microns . the film was then given an air flash at ambient temperature and then directly exposed to black uv light which showed a uniform fluorescence over the surface of the substrate indicating uniform coverage of the chlorinated polyolefin . when the substrate was topcoated with a coating composition available from ppg industries , inc . as durethane 700 and heated at 120 ° c . for 30 minutes , excellent adhesion of the topcoat to the substrate was obtained . additional compositions of the adhesion promoters were prepared as generally described above but with the exception that the compositions contained 0 . 5 , 1 . 5 and 2 . 5 percent by weight optical brighteners . in each instance , it was found that when the adhesion promoting compositions were spray applied in a uniform manner over the thermoplastic polyolefin substrate ( as evidenced by a uniform fluorescence when exposed to black uv light ), excellent adhesion of the subsequently applied topcoat ( durethane 700 ) was obtained . in each instance , the film thickness was about 10 microns . a further experiment was conducted with a coating composition as generally described above containing 0 . 1 percent by weight optical brightener but in which the adhesion promoting composition was applied in a non - uniform manner to the thermoplastic polyolefin substrate . the composition was applied heavily in one area and lightly in another . film thickness varied from 0 to 10 microns across the substrate . upon exposure of the coated substrate to black uv light , a non - uniform fluorescence resulted . application and curing of the topcoat durethane 700 as generally described above resulted in very poor adhesion of the topcoat to the substrate . the above examples show that the adhesion promoting compositions containing a chlorinated polyolefin and the optical brighteners of the present invention provide a convenient way to determine whether the adhesion promoter is evenly distributed over a substrate , thereby insuring for good adhesion of the subsequently applied topcoat to the substrate .