the embodiments of the present invention are explained below with reference to the drawings . in the following description , a substrate having active elements ( e . g . thin - film transistors ) formed thereon is referred to as an active - matrix substrate . when a substrate facing the aforesaid substrate has a color filter , it is referred to also as a color filter substrate . a group of electrodes for driving liquid crystals are explained by taking the case of those formed on an active - matrix substrate in an ips method , though they may be formed on both substrates holding liquid crystals between them . in the present invention , a preferable contrast as a target is more than 500 : 1 and an afterimage disappearance time as a target is preferably 5 minutes or less . the afterimage disappearance time is determined by the method defined in the following embodiments . fig1 is a schematic cross - sectional view of the vicinity of a pixel which illustrates a first embodiment of the liquid crystal display device of the present invention . fig2 is schematic views of an active - matrix substrate for explanation of the structure of the vicinity of a pixel which illustrate the first embodiment of the liquid crystal display device of the present invention . fig2 ( a ) is a plan view , fig2 ( b ) is a sectional view taken along the line a - a ′ in fig2 ( a ), and fig2 ( c ) is a sectional view taken along the line b - b ′ in fig2 ( a ). fig1 corresponds to a part of a section along the line a - a ′ in fig2 ( a ). the sectional views as fig2 ( b ) and fig2 ( c ) are schematic views in which the structure of the main portion is emphasized , and they do not correspond to the sections along the line a - a ′ and the line b - b ′, respectively , in fig2 ( a ) in an one - by - one manner . for example , in fig2 ( b ), a thin - film transistor 115 is not shown , and in fig2 ( c ), only a portion of a through - hole 118 connecting a common electrode 103 to a common wiring 120 is shown as a representative . in the present embodiment , in order to obtain an active - matrix substrate , a scanning wiring ( a gate electrode ) 104 made of cr ( chromium ) and a common wiring ( a common electrode wiring ) 120 are located on a glass substrate 101 , and a gate insulating film 107 made of silicon nitride is formed so as to cover the gate electrode 104 and the common electrode wiring 120 . a semiconductor film 116 made of amorphous silicon or polycrystalline silicon is located on the gate electrode 104 through the gate insulating film 107 so as to function as the active layer of a thin - film transistor ( tft ) 115 as active element . a drain electrode ( a signal wiring ) 106 made of cr · mo ( chromium / molybdenum ) and a source electrode ( a pixel electrode ) 105 are located so as to overlap with a portion of the pattern of the semiconductor film 116 , and a protective film 108 made of silicon nitride is formed so as to cover all of them . as schematically shown in fig2 ( c ), common electrodes 103 connected to the common electrode wiring 120 through a through - hole 118 formed by perforation of the gate insulating film 107 and the protective film 108 are located on an organic insulating film 133 . as can be seen from fig2 ( a ), the common electrodes 103 drawn out from the common electrode wiring 120 through the through - hole 118 are formed so as to face the pixel electrodes 105 in the region of one pixel in a plane . therefore , in the present embodiment , the pixel electrodes 105 are formed under the protective film 108 formed under the organic insulating film 133 , and the common electrodes 103 are located on the organic insulating film 133 . a pixel is formed in a region between a plurality of the pixel electrodes 105 and a plurality of the common electrodes 103 . an alignment film 131 is formed on the surface of the active - matrix substrate having the thus formed unit pixels arranged thereon in the form of a matrix , namely , the surface of the organic insulating film 133 having the common electrodes 103 formed thereon . on the other hand , as shown in fig1 , a color filter layer 111 is located on a glass substrate 102 as opposite substrate so as to be partitioned into sections for the individual pixels by a shade portion ( a black matrix ) 113 , and the color filter 111 and the shade portion 113 are covered with an organic protective film 134 made of a transparent insulating material . in addition , an alignment film 132 is formed also on the organic protective film 134 to constitute a color filter substrate . the alignment films 131 and 132 have an ability to orient liquid crystal molecules which has been imparted by irradiation with linear polarized ultraviolet light taken out from a high - pressure mercury lamp as light source by the use of a pile polarizer obtained by laminating quartz plates . the glass substrate 101 constituting the active - matrix substrate and the glass substrate 102 constituting the color filter substrate are located so as to face each other with respect to the surfaces of the alignment films 131 and 132 , respectively , and a liquid crystal layer ( a liquid crystal composition layer ) 110 ′ composed of liquid crystal molecules 110 is located between the glass substrates , whereby a liquid crystal display device is constructed . polarizing plates 118 and 119 are formed on the outer surfaces , respectively , of the glass substrate 101 constituting the active - matrix substrate and the glass substrate 102 constituting the color filter substrate . thus , an active - matrix type liquid crystal display device using tft 115 ( namely , a tft liquid crystal display device ) is constructed . in this tft liquid crystal display device , when no electric field is applied , the liquid crystal molecules 110 constituting the liquid crystal composition layer 110 ′ are oriented substantially in parallel with the surfaces of the substrates 101 and 102 located so as to face each other , and are homogeneously oriented in an initial direction of orientation determined by photo - alignment treatment . when tft 115 is switched on by applying a voltage to the gate electrode 104 , an electric field 117 is applied to the liquid crystal composition layer 110 ′ owing to the electric potential difference between the pixel electrodes 105 and the common electrodes 103 , and the liquid crystal molecules 110 constituting the liquid crystal composition layer 110 ′ turn in the direction of the electric field owing to the interaction between the dielectric anisotropy of the liquid crystal composition and the electric field . in this case , the light transmittance of the tft liquid crystal display device is varied by the refraction anisotropy of the liquid crystal composition layer 110 ′ and the action of the polarizing plates 118 and 119 , whereby display can be carried out . in the organic insulating films 133 and 134 , there may be used thermosetting resins such as acrylic resins , epoxyacrylic resins and polyimide resins , which are excellent in insulating properties and transparency . transparent photo - setting resins and inorganic materials such as polysiloxane resins may also be used in the organic insulating films 133 and 134 . in addition , the organic insulating films 133 and 134 may serve also as the alignment film 132 . as described above , the present embodiment makes it possible to impart uniform orientation all over the display region without local disturbance near the electrodes by adopting a non - contact photo - alignment method , not a rubbing alignment treatment in which the ability to orient liquid crystal molecules of the alignment films 131 and 132 is imparted by direct rubbing with buff . a second embodiment of the liquid crystal display device of the present invention is explained below . fig3 is a schematic cross - sectional view of the vicinity of a pixel which illustrates the second embodiment of the liquid crystal display device of the present invention . fig4 is schematic views of an active - matrix substrate for explanation of the structure of the vicinity of a pixel which illustrates the second embodiment of the liquid crystal display device of the present invention . fig4 ( a ) is a plan view , fig4 ( b ) is a sectional view taken along the line a - a ′ in fig4 ( a ), and fig4 ( c ) is a sectional view taken along the line b - b ′ in fig4 ( a ). fig3 shows a part of a section along the line a - a ′ in fig4 ( a ). the sectional views as fig4 ( b ) and fig4 ( c ) are schematic views in which the structure of the main portion is emphasized , and they do not correspond to the sections along the line a - a ′ and the line b - b ′, respectively , in fig4 ( a ) in an one - by - one manner . for example , in fig4 ( b ), a thin - film transistor 115 is not shown . in the present embodiment , a gate electrode 104 made of cr and a common electrode wiring 120 are located on a glass substrate 101 which constitutes an active - matrix substrate , and a gate insulating film 107 made of silicon nitride is formed so as to cover the gate electrode 104 and the common electrode wiring 120 . a semiconductor film 116 made of amorphous silicon or polycrystalline silicon is located on the gate electrode 104 through the gate insulating film 107 so as to function as the active layer of a thin - film transistor ( tft ) 115 , an active element . a drain electrode 106 made of chromium • molybdenum and a source electrode ( a pixel electrode ) 105 are located so as to overlap with a portion of the pattern of the semiconductor film 116 , and a protective film 108 made of silicon nitride is formed so as to cover all of them . an organic insulating film 133 is located on the protective film 108 . the organic insulating film 133 is made of a transparent material such as an acrylic resin . the pixel electrode 105 is composed of a transparent electrode of ito ( in 2 o 3 : sn ) or the like . common electrodes 103 are connected to the common electrode wiring 120 through a through - hole 118 passing through the gate insulating film 107 , the protective film 108 and the organic insulating film 133 . the common electrodes 103 paired with the pixel electrodes 105 , respectively , when an electric field for driving liquid crystals is applied , are formed so as to surround a pixel in a plane . the common electrodes 103 are located on the organic insulating film 133 . the common electrodes 103 are located so as to hide the drain electrodes 106 , the scanning wiring 104 and the thin - film transistor ( tft ) 115 as active element which are located in lower layers when looked at from above , and they serve also as a shade layer for shading the semiconductor film 116 from light . an alignment film 131 is formed on the surface of the glass substrate 101 constituting the thus constructed active - matrix substrate having unit pixels ( a group of pixels ) arranged thereon in the form of a matrix , namely , it is formed over the organic insulating film 133 and the common electrodes 103 formed thereon . on the other hand , also on a glass substrate 102 that constitutes a color filter substrate , an alignment film 132 is formed on an organic protective film 134 formed on a color filter layer 111 . as in the first embodiment , the alignment films 131 and 132 have an ability to orient liquid crystal molecules which has been imparted by irradiation with linear polarized ultraviolet light taken out from a high - pressure mercury lamp as light source by the use of a pile polarizer obtained by laminating quartz plates . the glass substrate 101 and the opposite glass substrate 102 are located so as to face each other with respect to the planes on which the alignment films 131 and 132 , respectively , have been formed , and a liquid crystal composition layer 110 ′ composed of liquid crystal molecules 110 is located between the glass substrates , whereby a liquid crystal display device is constructed . polarizing plates 118 and 119 are formed on the outer surfaces , respectively , of the glass substrate 101 and the opposite glass substrate 102 . thus , also in the present embodiment , as in the first embodiment described above , the pixel electrodes 105 are located under the organic insulating layer 133 and the protective layer 108 , and the common electrodes 103 are located over the pixel electrodes 105 and the organic insulating film 133 . when the electric resistance of the common electrodes 103 is sufficiently low , the common electrodes 103 can serve also as the common electrode wiring 120 located as the lowest layer . in this case , the formation of the common electrode wiring 120 located as the lowest layer and the fabrication of the through - hole accompanying the aforesaid formation can be omitted . in the present embodiment , as shown in fig4 ( a ), each pixel is formed in a region surrounded by the common electrodes 103 formed in the form of a lattice and is located so as to be divided into four regions , inclusive of the pixel electrode 105 . each pixel has a zigzag crooked structure in which the pixel electrode 105 and the common electrode 103 facing the pixel electrode 105 are located in parallel with each other . each pixel forms two or more sub - pixels . thus , a structure is formed in which a tone change in a plane is compensated for . fig5 is a schematic cross - sectional view of the vicinity of a pixel which illustrates a third embodiment of the liquid crystal display device of the present invention . in fig5 , the same symbols as in the drawings in the embodiments described above correspond to the same functional portions as in these embodiments . as shown in fig5 , in the present embodiment , a pixel electrode 105 located under a protective film 108 is drawn up to the surface of an organic insulating film 133 through a through - hole 118 to be located at the same level as that of common electrodes 103 . when this structure is used , a voltage for driving liquid crystals can be further reduced . fig6 is a schematic cross - sectional view of the vicinity of a pixel which illustrates a fourth embodiment of the liquid crystal display device of the present invention . in fig6 , the same symbols as in the drawings in the embodiments described above correspond to the same functional portions as in these embodiments . in the present embodiment , a structure having great level differences due to electrodes and the like is employed . fig7 is a schematic cross - sectional view of the vicinity of a pixel which illustrates a fifth embodiment of the liquid crystal display device of the present invention . in fig7 , the same symbols as in the drawings in the embodiments described above correspond to the same functional portions as in these embodiments . in the present embodiment , pixel electrodes 105 and a common electrode 103 are formed of ito , and the common electrode 103 is composed of a solid electrode covering substantially the whole pixel . owing to such a structure , the portion over the electrodes can be utilized as a transmission portion , so that the aperture ratio can be improved . moreover , the distance between the electrodes can be reduced , so that an electric field can be efficiently applied to liquid crystals . in the thus constructed tft liquid crystal display device , when no electric field is applied , liquid crystal molecules 110 constituting a liquid crystal composition layer 110 ′ become substantially parallel to the surfaces of glass substrates 101 and 102 located so as to face each other , and are homogeneously oriented in an initial direction of orientation determined by photo - alignment treatment . when a thin - film transistor ( tft ) 115 is switched on by applying a voltage to a gate electrode 104 , an electric field 117 is applied to the liquid crystal composition layer 110 ′ owing to the electric potential difference between the pixel electrodes 105 and the common electrode 103 , and the liquid crystal molecules 110 turn in the direction of the electric field owing to the interaction between the dielectric anisotropy of the liquid crystal composition and the electric field . in this case , the light transmittance of the liquid crystal display device is varied by the refraction anisotropy of the liquid crystal composition layer 110 ′ and the action of polarizing plates 118 and 119 , whereby display can be carried out . in each of the embodiments of the present invention described above , two or more groups of display regions consisting of a common electrode ( s ) and a pixel electrode ( s ) in each pixel can be provided . by thus providing the two or more groups , the distance between the pixel electrode and the common electrode can be reduced , so that a voltage to be applied for driving liquid crystals can be reduced . in each of the embodiments of the present invention described above , although a material for a transparent electroconductive film constituting at least one of the pixel electrode and the common electrode is not particularly limited , it is preferable to use a transparent electroconductive film of an ion - doped titanium oxide ( e . g . indium - tin - oxide ( ito )) or an ion - doped zinc oxide , in view of ease of processing , reliability and the like . the following is known : in general , in the ips method , a boundary - surface tilt with respect to the surface of a substrate is unnecessary in principle unlike in a longitudinal electric field method represented by a conventional tn method , and visual characteristics are improved with a decrease of a boundary - surface tilt angle . also in a photo - alignment film , a small boundary - surface tilt angle is preferable , and a boundary - surface tilt angle of 1 degree or less is especially effective . next , the formation of an alignment film using a rubbingless alignment method for a film for controlling the orientation of liquid crystal molecules is explained below as a step in a process for producing the liquid crystal display device of the present invention . the order of steps for forming the alignment film according to the present invention is as described in the following items ( 1 ) to ( 4 ): ( 1 ) the formation of a coating film as alignment film ( a uniform coating film is formed all over a display region ), ( 2 ) calcination for conversion to imide of the alignment film ( the removal of a varnish solvent and conversion to a highly heat - resistant polyimide are accelerated ), ( 3 ) the impartment of an ability to orient liquid crystal molecules by irradiation with polarized light ( an uniform orienting ability is imparted to the display region ), and ( 4 ) the enhancement and stabilization of the orienting ability by ( heating , irradiation with infrared rays , irradiation with far infrared rays , irradiation with electron rays or irradiation with radiation ). the alignment film is formed by a process consisting of the above 4 steps . the order of the steps is not limited to the order of ( 1 ) to ( 4 ) in the process . a larger effect is expected in the following cases ( i ) and ( ii ). ( i ) the above steps ( 3 ) and ( 4 ) are carried out so as to overlap with each other with respect to time , to accelerate the impartment of the ability to orient liquid crystal molecules , and induce crosslinking reaction or the like , whereby more effective formation of the alignment film becomes possible . ( ii ) when the heating , irradiation with infrared rays , irradiation with far infrared rays , or the like in the above step ( 4 ) is employed , the above step ( 4 ) becomes able to serve also as the step ( 2 ), i . e ., the conversion to imide when the above steps ( 2 ), ( 3 ) and ( 4 ) are allowed to overlap with respect to time , whereby it becomes possible to form the alignment film in a short time . specific examples of a process for producing the liquid crystal display device of the present invention are described below . this example corresponds to the liquid crystal display device explained in the first embodiment described above . this example is explained in detail with reference to fig1 and fig2 . in the production of the liquid crystal display device of this example , a glass substrate of 0 . 7 mm in thickness whose surface had been polished was used as each of a glass substrate 101 for forming an active - matrix substrate , and a glass substrate 102 for forming a color filer substrate facing the active - matrix substrate . an acrylic resin organic insulating film 134 of 1 . 0 μm in thickness was formed on the color filter substrate side . a thin - film transistor 115 to be formed on the glass substrate 101 was composed of a source electrode 105 , a drain electrode 106 , a gate electrode 104 and amorphous silicon as semiconductor layer 116 . all of a scanning wiring 104 , a common electrode wiring 120 , a signal wiring 106 and pixel electrodes 105 were formed by patterning a chromium film , and the distance between the pixel electrode 105 and the common electrode 103 was adjusted to 7 μm . for forming the common electrodes 103 and the pixel electrodes 105 , the chromium film was used which had a low resistance and was easily patterned . it is also possible to attain higher luminance characteristics by forming the common electrodes 103 and the pixel electrodes 105 from a transparent electrode obtained by using an ito film . a gate insulating film 107 and a protective insulating film 108 were made of silicon nitride and the thickness of each of these films was adjusted to 0 . 3 μm . an acrylic resin was applied on them and heat - treated at 220 ° c . for 1 hour to form an organic insulating film 133 of 1 . 5 μm in thickness which was transparent and had insulating properties . then , as shown in fig2 ( c ), a through - hole 118 was formed as far as a common electrode wiring 120 by photolithography and etching treatment , and the common electrodes 103 connecting to the common electrode wiring 120 were formed by patterning . as a result , in a unit pixel ( a single pixel ), the pixel electrode 105 was located among three of the common electrodes 103 as shown in fig2 ( a ), whereby there was formed an active - matrix substrate having pixels in a number of 1024 × 3 × 768 , namely , pixels composed of signal wirings 106 in a number of 1024 × 3 ( corresponding to r , g and b ) and 768 scanning wirings 104 . thereafter , a poly ( amic acid ) varnish consisting of a 1 : 1 ( by mole ) mixture of p - phenylenediamine as diamine compound and 1 , 4 - diaminopyridine and 1 , 2 , 3 , 4 - cyclobutanetetracarboxylic dianhydride as acid dianhydride was adjusted so as to have a resin concentration of 5 % by weight , a nmp concentration of 60 % by weight , a y - butyllactone concentration of 20 % by weight and a butyl cellosolve concentration of 15 % by weight , and it was formed by printing on the above - mentioned active - matrix substrate and subjected to conversion to imide by heat treatment at 220 ° c . for 30 minutes . thus , a dense polyimide alignment film 131 of about 80 nm was formed . subsequently , c . i . direct red 81 and c . i . direct yellow 12 were added to a poly ( amic acid ) varnish consisting of a 1 : 1 ( by mole ) mixture of p - phenylenediamine as diamine compound and 1 , 4 - diaminopyridine and 1 , 2 , 3 , 4 - cyclobutanetetracarboxylic dianhydride as acid dianhydride , and the resulting mixture was adjusted so as to have a resin concentration of 5 % by weight , a c . i . direct red 81 concentration of 0 . 7 % by weight , a c . i . direct yellow 12 concentration of 0 . 3 % by weight , a nmp concentration of 60 % by weight , a y - butyllactone concentration of 20 % by weight and a butyl cellosolve concentration of 14 % by weight . this mixture was formed by printing and heat - treated at 220 ° c . for 30 minutes to form an alignment film 132 composed of a dense polyimide film of about 80 nm on the surface of the other glass substrate 102 . the surfaces of the alignment films 131 and 132 were irradiated with polarized uv ( ultraviolet ) light in order to impart an ability to orient liquid crystal molecules and anisotropic absorption . a high - pressure mercury lamp was used as a light source , and uv light in the range of 240 nm to 600 nm was taken out through an interference filter and made into linear polarized light having a polarization ratio of approximately 10 : 1 by the use of a pile polarizer obtained by laminating quartz substrates . the linear polarized light was cast at an irradiation energy of about 5 j / cm 2 . as a result , the direction of orientation of liquid crystal molecules on the surfaces of the alignment films was found to be perpendicular to the direction of polarization of the polarized uv cast . then , the two glass substrates 101 and 102 were located so that their surfaces having the alignment films 131 and 132 , respectively , having an ability to orient liquid crystal molecules might face each other . a spacer composed of dispersed spherical polymer beads was placed between the these surfaces and a sealing compound was applied on the peripheral portion of the resulting assembly to construct a liquid crystal display panel ( referred to also as a cell ) to be made into a liquid crystal display device . the directions of orientation of liquid crystal molecules on the two glass substrates , respectively , were substantially parallel to each other and the angle between these directions and the direction of an applied electric field was adjusted to 75 °. a nematic liquid crystal composition having a positive dielectric anisotropy δε of 10 . 2 ( 1 khz , 20 ° c . ), a refractive index anisotropy δn of 0 . 075 ( wavelength 590 nm , 20 ° c . ), a torsional modulus k 2 of 7 . 0 pn and a nematic - isotropic phase transition temperature t ( n - i ) of about 76 ° c . was injected into the cell in a vacuum , and the cell was sealed with a sealing compound comprising a ultraviolet - setting resin . thus , a liquid crystal panel having a thickness of liquid crystal layer ( a gap ) of 4 . 2 μm was produced . the retardation ( δnd ) of this liquid crystal display panel was about 0 . 31 μm . a liquid crystal display panel having homogeneous orientation was produced by the use of the same alignment films and liquid crystal composition as used in the above - mentioned panel and the pre - tilt angle of the liquid crystals was measured by a crystal rotation method and found to be about 0 . 2 degree . this liquid crystal display panel was held between two polarizing plates 118 and 119 , so that the axis of polarized light transmission of one of the polarizing plates might be substantially parallel to the above - mentioned direction of orientation of liquid crystal molecules and that of the other polarizing plate might be perpendicular thereto . in this case , the axis of absorption of the polarizing plate 119 located on the glass substrate 102 on the observer side was substantially perpendicular to the direction of the axis of absorption of the alignment film 132 formed on the color filter substrate . thereafter , a driving circuit , a backlight as light source and the like were connected to the thus obtained assembly to obtain a module , whereby an active - matrix type liquid crystal display device was obtained . in the present embodiment , normally close characteristics were attained which were such that a dark display is obtained at a low voltage and a light display at a high voltage . then , the display quality of the liquid crystal display device of the present example was evaluated to confirm a high - quality display having a contrast ratio of 520 : 1 and a wide angle of field of view at the time of displaying a color with an intermediate tone . the difference in chromaticity coordinate between white display and black display was measured to find that δu ‘ v ’ was 0 . 038 . next , for the quantitative measurement of image sticking , i . e ., an afterimage in the liquid crystal display device of the present example , evaluation was carried out by the use of an oscilloscope comprising a combination of photodiodes . at first , a window pattern was displayed on the screen at the highest luminance for 30 minutes . then , the whole screen was changed so that a display of a color with an intermediate tone , in which an afterimage was most conspicuous , might be obtained , namely , the luminance might be 10 % of the highest luminance , and a time required for the disappearance of the pattern of the edge portion of the window pattern was measured as afterimage relaxation time . an allowable afterimage relaxation time in this case was 5 minutes or less . as a result , the relaxation time of an afterimage was found to be 3 minutes or less in the working temperature range ( 0 ° c . to 50 ° c .). also in a visual inspection of image quality and afterimage , no display nonuniformity due to image sticking , i . e ., an afterimage was not observed at all , namely , high display characteristics could be attained . it has heretofore been said that photo - alignment permits molecular orientation of liquid crystals but has a lower energy for chaining oriented liquid crystal molecules to the surface of an alignment film than does general rubbing alignment . it is also said that when this anchoring energy is low , the reliability of a liquid crystal display device as product is insufficient . particularly in the case of homogeneous orientation , it is said that anchoring energy in the direction of azimuth angle is more important than anchoring energy in the direction of polar angle . using the same material for alignment film as in the thus obtained liquid crystal display device , a liquid crystal cell was produced by forming an alignment film on each glass substrate and carrying out alignment treatment , by the same process as in the case of the aforesaid liquid crystal display device , followed by encapsulation of the same liquid crystal composition as used in the aforesaid liquid crystal display device . the strength of the torsional bonding of liquid crystal molecules to the surface of the alignment film on the boundary surface between them , i . e ., anchoring energy a 2 in the direction of azimuth angle was measured by a torque balance method ( hasegawa et al . “ collection of preliminary manuscripts for lectures to the forum of the japan liquid crystal society ” 3b12 ( 2001 ), p . 251 ) and found to be 6 . 0 × 10 − 4 n / m . in comparative example 1 , a liquid crystal display device was produced in the same manner as in example 1 except for using as an alignment film 132 the same alignment film as the alignment film 131 in place of the alignment film 132 used in example 1 and containing c . i . direct red 81 and c . i . direct yellow 12 . the display quality of the liquid crystal display device of comparative example 1 was evaluated to find that the contrast ratio was 270 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 072 . then , an afterimage in the liquid crystal display device of comparative example 1 was evaluated in the same manner as in example 1 to find that the afterimage relaxation time was about 3 minutes . the anchoring energy a 2 in the direction of azimuth angle was 4 . 5 × 10 − 4 n / m . in this example , a liquid crystal display device was produced in the same manner as in example 1 except for changing the acrylic resin composition used in the organic insulating film 134 formed on the color filter substrate side . the acrylic resin composition used in the organic insulating film 134 was changed by adding c . i . direct red 81 to a concentration of 0 . 7 % by weight and c . i . direct yellow 12 to a concentration of 0 . 3 % by weight . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 580 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 034 . in this example , a liquid crystal display device was produced in the same manner as in example 1 except for changing an acrylic resin composition used in the organic insulating film 134 formed on the color filter substrate side , a resist material composition used in a color filter 111 and methods for treating them . an acrylic resin composition for forming an organic insulating film 134 was prepared by adding c . i . direct red 81 and c . i . direct yellow 12 to the same acrylic resin composition as used in the organic insulating film 134 in example 1 , to concentrations of 0 . 7 % by weight and 0 . 3 % by weight , respectively . in addition , c . i . direct yellow 44 was added to a resist material for display of a blue color in the color filter layer 111 to a concentration of 1 . 5 % by weight , c . i . direct red 81 was added to a resist material for display of a green color in the color filter layer 111 to a concentration of 1 % by weight , and c . i . direct blue 151 was added to a resist material for display of a red color in the color filter layer 111 to a concentration of 1 % by weight . before forming an alignment film 132 on the color filter substrate side , an organic insulating film 134 formed on the color filter substrate side in this example by the use of the composition prepared above was irradiated with polarized uv ( ultraviolet ) light in order to impart anisotropic absorption to the surface of the organic insulating film 134 . a high - pressure mercury lamp was used as a light source , and uv light in the range of 330 nm to 600 nm was taken out through an interference filter and made into linear polarized light having a polarization ratio of approximately 15 : 1 by the use of a pile polarizer obtained by laminating quartz substrates . the linear polarized light was cast at an irradiation energy of about 5 j / cm 2 . as a result , it was found that the color filter substrate had an axis of absorption in a direction perpendicular to the direction of polarization of the polarized uv cast . in this case , the polarizing plate 119 on the glass substrate 102 can be omitted . thereafter , the alignment film 132 on the color filter substrate side was formed in the same manner as in example 1 . in this case , the axis of polarization of polarized light to be cast on the alignment film 132 was made substantially parallel to the axis of polarization of the polarized light cast on the organic insulating film 134 . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 630 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 027 . in this example , a liquid crystal display device was produced in the same manner as in example 1 except for using the same alignment film as the film 132 used on the color filter side in example 1 , as an alignment film 131 on the active - matrix substrate side , and using the same alignment film as the film 131 used on the active - matrix substrate side in example 1 , as an alignment film 132 on the color filter side , and changing an acrylic resin composition used in the organic insulating film 133 formed on the active - matrix substrate side and a method for treating the resin composition . at first , an acrylic resin composition for forming an organic insulating film 133 was prepared by adding c . i . direct red 81 and brilliant yellow to the same acrylic resin composition as used in the organic insulating film 133 in example 1 , to concentrations of 0 . 7 % by weight and 0 . 8 % by weight , respectively , and the resulting composition was formed in the same manner as in example 1 . then , before forming an alignment film 131 on the active - matrix substrate side , the organic insulating film 133 formed in this example was irradiated with polarized uv ( ultraviolet ) light in order to impart anisotropic absorption to the surface of the organic insulating film 133 . a high - pressure mercury lamp was used as a light source , and uv light in the range of 330 nm to 600 nm was taken out through an interference filter and made into linear polarized light having a polarization ratio of approximately 15 : 1 by the use of a pile polarizer obtained by laminating quartz substrates . the linear polarized light was cast at an irradiation energy of about 5 j / cm 2 . as a result , it was found that the active - matrix substrate had an axis of absorption in a direction perpendicular to the direction of polarization of the polarized uv cast . in this case , the polarizing plate 118 on the glass substrate 101 can be omitted . thereafter , the alignment film 131 on the active - matrix substrate side was formed in the same manner as in example 1 . in this case , the axis of polarization of polarized light to be cast on the alignment film 131 was made substantially parallel to the axis of polarization of the polarized light cast on organic insulating film 133 . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 550 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 040 . in this example , a liquid crystal display device was produced in the same manner as in example 4 except for using the same alignment film as the film 131 used on the active - matrix substrate side in example 4 , as an alignment film 132 on the color filter side . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 520 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 042 . the structure of a liquid crystal display device as the fifth embodiment of the present invention is specifically explained as example 6 with reference to fig7 . a glass substrate of 0 . 7 mm in thickness whose surface had been polished was used as a substrate 101 . an insulating film 107 for preventing a short circuit between a common electrode 103 and other electrodes was formed on the substrate 101 . in addition , a protective film 108 for protecting a thin - film transistor 115 was formed to obtain a tft substrate . the thin - film transistor 115 was composed of a source electrode , a drain electrode , a gate electrode and amorphous silicon formed among them . a scanning wiring to be connected to the gate electrode was formed by patterning an aluminum film , a signal wiring 106 to be connected to the drain electrode was formed by patterning a chromium film , and the common electrode 103 and pixel electrodes 105 were formed by patterning ito . the insulating film 107 and the protective film 108 were made of silicon nitride and had thickness values of 0 . 2 μm and 0 . 3 μm , respectively . a capacity element was constructed by holding the insulating film 107 and the protective film 108 between the pixel electrodes 105 and the common electrode 103 . the pixel electrodes 105 were located so as to overlap with and exist over the common electrode 103 of solid form . the number of pixels was 1024 × 3 × 768 , namely , the number of pixels composed of signal wirings in a number of 1024 × 3 ( corresponding to r , g and b ) and 768 scanning wirings . a color filter 111 with a black matrix 113 having the same structure as in example 1 was formed on a substrate 102 to obtain a color filter substrate . then , a poly ( amic acid ) varnish consisting of a 3 : 1 ( by mole ) mixture of p - phenylenediamine as diamine compound and 3 , 4 - diaminothiophene and a 1 : 1 ( by mole ) mixture of 1 , 2 , 3 , 4 - cyclobutanetetracarboxylic dianhydride and pyromellitic dianhydride as acid dianhydrides was adjusted so as to have a resin concentration of 5 % by weight , a nmp concentration of 60 % by weight , a y - butyllactone concentration of 20 % by weight and a butyl cellosolve concentration of 15 % by weight , and it was formed by printing on a tft substrate and subjected to conversion to imide by heat treatment at 220 ° c . for 30 minutes . thus , a dense polyimide alignment film 131 of about 110 nm was formed as an alignment film 131 on the tft substrate side . thereafter , c . i . direct yellow 44 was dissolved in the same poly ( amic acid ) varnish as above and the resulting composition was adjusted so as to have a resin concentration of 5 % by weight , a c . i . direct yellow 44 concentration of 1 % by weight , a nmp concentration of 60 % by weight , a γ - butyllactone concentration of 20 % by weight and a butyl cellosolve concentration of 14 % by weight . this composition was formed by printing and heat - treated at 220 ° c . for 30 minutes to form an alignment film 132 composed of a dense polyimide film of about 110 nm , as an alignment film 132 on the color filter substrate side . the surfaces of the alignment films 131 and 132 were irradiated with polarized uv ( ultraviolet ) light while being irradiated with far infrared rays . a high - pressure mercury lamp was used as a light source , and uv light in the range of 240 nm to 600 nm was taken out through an interference filter and made into linear polarized light having a polarization ratio of approximately 10 : 1 by the use of a pile polarizer obtained by laminating quartz substrates . the linear polarized light was cast at an irradiation energy of about 3 j / cm 2 . in this case , the temperature of the alignment films was about 170 ° c . the same alignment film as above was formed on a quartz substrate and a polarized uv spectrum was measured . as a result , it was proved that this alignment film had such anisotropic absorption that it had an axis of absorption in a direction perpendicular to polarized uv light cast . in addition , the direction of orientation of liquid crystal molecules on the surfaces of the alignment film was found to be perpendicular to the direction of polarization of the polarized uv cast . the directions of molecular orientation of the alignment films 131 and 132 on the tft substrate and the color filter substrate , respectively , were made substantially parallel to each other and the angle between these directions and the direction of an applied electric field 117 was adjusted to 15 degrees . polymer beads having an average particle size of 4 μm were dispersed as a spacer between these substrates and liquid crystals were held between the tft substrate and the color filter substrate . as the liquid crystals , a nematic liquid crystal composition having a positive dielectric anisotropy δε of 10 . 2 ( 1 khz , 20 ° c . ), a refractive index anisotropy δn of 0 . 075 ( wavelength 590 nm , 20 ° c . ), a torsional modulus k 2 of 7 . 0 pn and a nematic - isotropic phase transition temperature t ( n - i ) of about 76 ° c . was injected in a vacuum , and the resulting assembly was sealed with a sealing compound comprising a ultraviolet - setting resin . thus , a liquid crystal panel having a thickness of liquid crystal layer ( a gap ) of 4 . 0 μm was produced . as two polarizing plates 118 and 119 for holding between them the tft substrate and the color filter substrate , those obtained by adding iodine to a poly ( vinyl alcohol ), followed by stretching were used and were located in the manner of crossed nicols . in this case , the axis of absorption of the polarizing plate 119 located on the glass substrate 102 on the observer side was made substantially parallel to the direction of the axis of absorption of the alignment film 132 formed on the color filter substrate . normally close characteristics were employed which were such that a dark state is assumed at a low voltage and a light state at a high voltage . the retardation ( δnd ) of the thus obtained liquid crystal display panel was about 0 . 30 μm . a liquid crystal display panel having homogeneous orientation was produced by the use of the same alignment films and liquid crystal composition as used in the above - mentioned panel and the pre - tilt angle of the liquid crystals was measured by a crystal rotation method and found to be about 0 . 2 degree . a backlight source was located on the glass substrate 101 side of the above - mentioned liquid crystal display panel and other circuits for driving the liquid crystals were provided to produce a liquid crystal display device . then , the display quality of the liquid crystal display device of the present example was evaluated to confirm a high - quality display having a contrast ratio of 620 : 1 and a wide angle of field of view at the time of displaying a color with a intermediate tone . the difference in chromaticity coordinate between white display and black display was measured to find that δu ‘ v ’ was 0 . 034 . in addition , for the quantitative measurement of image sticking , i . e ., an afterimage in the liquid crystal display device of the present example , evaluation was carried out by the use of an oscilloscope comprising a combination of photodiodes . at first , a window pattern was displayed on the screen at the highest luminance for 30 minutes . then , the whole screen was changed so that a display of a color with an intermediate tone , in which an afterimage was most conspicuous , might be obtained , namely , the luminance might be 10 % of the highest luminance , and a time required for the disappearance of the pattern of the edge portion of the window pattern was measured as afterimage relaxation time . an allowable afterimage relaxation time in this case was 5 minutes or less . as a result , the relaxation time of an afterimage was found to be 3 minutes or less in the working temperature range ( 0 ° c . to 50 ° c .). also in a visual inspection of image quality and afterimage , no display nonuniformity due to image sticking , i . e ., an afterimage was not observed at all , namely , high display characteristics could be attained . it has heretofore been said that photo - alignment permits molecular orientation of liquid crystals but has a lower energy for chaining oriented liquid crystal molecules to the surface of an alignment film than does general rubbing alignment . it is also said that when this anchoring energy is low , the reliability of a liquid crystal display device as product is insufficient . particularly in the case of homogeneous orientation , it is said that anchoring energy in the direction of azimuth angle is more important than anchoring energy in the direction of polar angle . using the same material for alignment film as in the thus obtained liquid crystal display device , a liquid crystal cell was produced by forming an alignment film on each glass substrate and carrying out alignment treatment , by the same process as in the case of the aforesaid liquid crystal display device , followed by encapsulation of the same liquid crystal composition as used in the aforesaid liquid crystal display device . the strength of the torsional bonding of liquid crystal molecules to the surface of the alignment film on the boundary surface between them , i . e ., anchoring energy a 2 in the direction of azimuth angle was measured by a torque balance method ( hasegawa et al . “ collection of preliminary manuscripts for lectures to the forum of the japan liquid crystal society ” 3b12 ( 2001 ), p . 251 ) and found to be 7 . 0 × 10 − 4 n / m . in comparative example 2 , a liquid crystal display device was produced in the same manner as in example 6 except for using the same alignment film as the alignment film 131 in place of the alignment film 132 used in example 6 and containing c . i . direct yellow 44 . the display quality of the liquid crystal display device of comparative example 2 was evaluated to find that the contrast ratio was 420 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 065 . then , an afterimage in the liquid crystal display device of comparative example 2 was evaluated in the same manner as in example 6 to find that the afterimage relaxation time was about 5 minutes . the anchoring energy a 2 in the direction of azimuth angle was 5 . 0 × 10 − 4 n / m . in comparative example 3 , a liquid crystal display device was produced in the same manner as in example 6 except for locating the polarizing plate 119 described in example 6 so that the axis of absorption of the polarizing plate 119 might be perpendicular to that of the alignment film 132 , and attaching the polarizing plate 118 and the polarizing plate 119 in the manner of crossed nicols . the display quality of the liquid crystal display device produced in comparative example 3 was evaluated to find that the contrast ratio was 590 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 045 . in this example , a liquid crystal display device was produced in the same manner as in example 6 except for using the same alignment film as the alignment film 132 used in the color filter substrate side in example 6 , also as an alignment film 131 on the active - matrix substrate side . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 690 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 035 . then , an afterimage in the liquid crystal display device of this example was evaluated in the same manner as in example 6 to find that the afterimage relaxation time was about 1 minute . the anchoring energy a 2 in the direction of azimuth angle was 1 . 0 × 10 − 3 n / m . in comparative example 4 , a liquid crystal display device was produced in the same manner as in example 7 except for adopting a rubbing alignment method as an alignment treatment method . the display quality of the liquid crystal display device of comparative example 4 was evaluated to find that the contrast ratio was 380 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 098 . then , an afterimage in the liquid crystal display device of comparative example 4 was evaluated in the same manner as in example 6 to find that the afterimage relaxation time was about 2 minutes . the anchoring energy a 2 in the direction of azimuth angle was 9 . 0 × 10 − 4 n / m . in this example , a liquid crystal display device was produced in the same manner as in example 6 except for using the same alignment film as the alignment film 132 used on the color filter substrate side in example 6 , as an alignment film 131 on the active - matrix substrate side , and using the same alignment film as the alignment film 131 used on the tft substrate side in example 6 , as an alignment film 132 on the color filter substrate side . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 610 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 044 . then , an afterimage in the liquid crystal display device of this example was evaluated in the same manner as in example 6 to find that the afterimage relaxation time was about 1 minute . the anchoring energy a 2 in the direction of azimuth angle was 9 . 0 × 10 − 4 n / m . in example 9 , a liquid crystal display device was produced in the same manner as in example 6 except for changing an acrylic resin composition used in the organic insulating film 134 formed on the color filter substrate side , a resist material composition used in the color filter 111 and methods for treating them . at first , an acrylic resin composition for forming an organic insulating film 134 was prepared by adding c . i . direct red 81 and c . i . direct yellow 12 to the same acrylic resin composition as used in the organic insulating film 134 in example 6 , to concentrations of 0 . 7 % by weight and 0 . 3 % by weight . in addition , c . i . direct yellow 44 was added to a resist material for display of a blue color in the color filter layer 111 to a concentration of 1 . 5 % by weight . before forming an alignment film 132 on the color filter substrate side , an organic insulating film 134 formed on the color filter substrate side in this example by the use of the composition prepared above was irradiated with polarized uv ( ultraviolet ) light in order to impart anisotropic absorption to the surface of the organic insulating film 134 . a high - pressure mercury lamp was used as a light source , and uv light in the range of 340 nm to 650 nm was taken out through an interference filter and made into linear polarized light having a polarization ratio of approximately 15 : 1 by the use of a pile polarizer obtained by laminating quartz substrates . the linear polarized light was cast at an irradiation energy of about 5 j / cm 2 . as a result , it was found that the color filter substrate had an axis of absorption in a direction perpendicular to the direction of polarization of the polarized uv cast . thereafter , the alignment film 132 on the color filter substrate side was formed in the same manner as in example 6 . in this case , the axis of polarization of polarized light to be cast on the alignment film 132 was made substantially parallel to the axis of polarization of the polarized light cast on organic insulating film 134 . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 740 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 029 . in this example , a liquid crystal display device was produced in the same manner as in example 6 , except that a composition obtained by adding 0 . 5 % by weight of brilliant yellow , 0 . 1 % by weight of c . i . direct red 28 and 0 . 1 % by weight of c . i . direct blue 1 to the same poly ( amic acid ) varnish as in example 6 was used in an alignment film 132 on the color filter substrate side . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 720 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 031 . in example 11 , a liquid crystal display device corresponding to the fourth embodiment of the present invention was produced . fig6 is a schematic cross - sectional view of the vicinity of a pixel which illustrates this example . in the production of the liquid crystal display device of this example , a glass substrate of 0 . 7 mm in thickness whose surface had been polished was used as each of glass substrates 101 and 102 . a thin - film transistor 115 was composed of a source electrode 105 , a drain electrode 106 , a gate electrode 104 and amorphous silicon 116 . all of the gate electrode ( scanning wiring ) 104 , a common electrode wiring to be connected to a common electrode 103 , the drain electrode ( signal wiring ) 106 , the source electrodes ( pixel electrodes ) 105 and the common electrode 103 were formed by patterning a chromium film , and the distance between the pixel electrode 105 and the common electrode 103 was adjusted to 7 μm . a gate insulating film 107 and a protective film 108 were made of silicon nitride and the thickness of each of them was adjusted to 0 . 3 μm . the same alignment films 131 and 132 as in example 10 were used and they were formed through the same steps as in example 10 . the display quality of the liquid crystal display device produced in this example was evaluated to find that the contrast ratio was 630 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 030 . in comparative example 5 , a liquid crystal display device was produced in the same manner as in example 11 except for adopting rubbing alignment as an alignment treatment method for the alignment films 131 and 132 . the display quality of the liquid crystal display device produced in comparative example 5 was evaluated to find that the contrast ratio was 290 : 1 and that the chromaticity difference δu ‘ v ’ between white display and black display was 0 . 046 . it should be further understood by those skilled in the art that although the foregoing description has been made on embodiments of the invention , the invention is not limited thereto and various changes and modifications may be made without departing from the spirit of the invention and the scope of the appended claims .