in the discussion which follows , it is important to distinguish between graphite “ foams ” and “ solid , porous graphite materials .” a “ foam ” will be defined herein to be a material having a relative density ( rd ) equal to or less than 0 . 3 , i . e ., being at least 70 % porous . using this definition , the artifacts prepared according to the method of the present invention have apparent densities greater than about 0 . 678 g / cc , relative densities greater than 0 . 3 and thus constitute “ porous solids ” rather than foams . at a relative density ( rd ) above about 0 . 3 , there is a transition from a cellular structure ( foam ) to one which is better thought of as a solid containing isolated pores ( porous solid ). rd can be defined as : see : “ cellular solids , structure and properties , second edition , page 2 , lorna j . gibson , dept . of materials science and engineering , mit , cambridge , mass . 021139 , usa , michael f . ashby , dept . of engineering , cambridge , university , cambridge , uk , cambridge university press , 40 w . 20 th street , new york , n . y ., 1988 . for example , a graphite foam with an apparent density of 0 . 50 g / cc would have a rd = 0 . 50 / 2 . 26 = 0 . 22 ( where 0 . 5 g / cc is the density of the cellular material and 2 . 26 g / cc is the density of the graphite in the cell walls ). a sample with an apparent density of 0 . 678 g / cc would have a rd = 0 . 678 / 2 . 26 = 0 . 3 , therefore any material produced that has an apparent density greater than 0 . 678 g / cc will be a “ solid ” containing isolated pores according to the above definition . in the discussion of the invention which follows , reference will be made to both foams and solids , it being understood that the present invention is directed toward porous solids . one problem with previously produced “ foamed ” products was the presence of density variations from the top to the bottom of the production billet . the density variations in the end products were found to occur between the foaming and solidification steps of the prior art process while the foamed pitch was still in the liquid state . the liquid pitch tends to migrate due to gravity , thereby making the bottom of the production billet denser than the top portion of the billet . applicant &# 39 ; s previous application ser . no . 09 / 862 , 560 , concerned the discovery that , by heating the pitch under an increased pressure above 1000 psig , the process temperature can exceed the normal foaming point of the pitch without the pitch actually foaming , i . e ., the thermal foaming point is raised . holding the pitch at such a selected temperature allows the growth of mesophase domains within the pitch , thereby increasing the pitch &# 39 ; s viscosity . higher viscosities at this point in the process reduce the previously described migration problems . the present invention concerns the discovery that the apparent density of artifacts of the above type can be manipulated to produce “ solid ” graphites by processing at final pressures greater than 1000 psi and manipulating the final “ boiling pressure ”. as a result of the higher and variable processing pressures , the apparent densities of the end products have been increased to greater than 0 . 678 g / cc with thermal conductivities which exceed 150 w / mk . [ 0033 ] fig1 shows a graph of thermal conductivity in w / mk versus apparent density in g / cc for several of the poco specialty graphites as compared to the solid , high thermally conductive porous graphite ( htcpg ) of the invention . the thermal conductivity of the sample htcpg in fig1 exceeds 250 w / mk . in the process of the invention , a solid , porous graphite is produced by first placing pitch powder , granules or pellets into a mold or container with the desired final shape of the artifact to be produced . the pitch can be selected from among the mesophase pitches , isotropic pitches and mixtures thereof . the mesophase pitches include , for example , synthetic pitches , coal based pitches and petroleum based pitches . these pitch materials can be solvated if desired . the pitches can be introduced in the granulated , powdered or pelletized form . one example precursor material is the mitsubishi ara - 24 mesophase pitch . a proper mold release agent or film can be applied to the sides of the mold to allow removal of the part . preferably , a suitable liner , such as an aluminum foil liner is utilized . if the mold is made from pure aluminum , typically no mold release agent is necessary since the molten pitch does not wet the aluminum and thus does not stick to the mold . the pitch may be desiccated to assist in removing any residual moisture . following desiccation , the pitch is processed in a substantially oxygen - free environment to avoid oxidation of the pitch materials during heating . preferably , the pitch is placed in a “ hip ” furnace which has been evacuated to less than two torr . the hip vessel is pressurized to a high initial pressure , e . g ., 8000 psig , which increases the boiling point higher than the boiling point at the final processing pressure . the pitch is then heated to a temperature approximately 50 to 100 ° c . above the softening point . for example , where mitsubishi ara - 24 mesophase pitch is used , a temperature of 300 ° c . is sufficient . after holding the pitch at 300 ° c . for one hour , the pitch is heated from 300 to 450 ° c . and held at 450 ° c . for a predetermined amount of time to increase the viscosity of the liquid pitch . the vessel is then depressurized from the initial processing pressure ( 8000 psig ) to the final processing pressure , e . g ., 2000 psig , while maintaining the temperature of the initial processing pressure . this depressurizing causes the liquid pitch to boil and generate porosity . as will be explained in greater detail in the examples which follow , the boiling liquid is then heated to a temperature , e . g ., 500 ° c ., that solidifies the artifact in one or more steps . the temperature of the system can then be raised from 500 ° c . to 600 ° c ., or to a temperature sufficient to coke the pitch ( about 500 - 600 ° c .). this is performed at a rate no greater than about 5 ° c ./ min and preferably about 1 ° c ./ min . the final temperature is held at 600 ° c . for about 2 hours and then the furnace power is turned off and cooled to room temperature . during the cooling cycle , pressure is released gradually to atmospheric conditions . any remaining pressure is released at a rate of about 30 psi per minute . the artifact is then separated from the mold . the artifact can be post heat treated to temperatures above 2000 ° c . for conversion to graphitic structure , depending upon the pitch precursor . in general , mesophase pitch is graphitized significantly easier than isotropic pitches ( coal derived or petroleum derived ). the more graphitic the material , the higher the thermal conductivity of the resulting graphitic foam . the specific steps followed in the process of the invention are summarized below : 1 . a mold is filled with a pellet or powder form of mesophase pitch . 2 . the pitch is then desiccated to assist in removing any residual moisture . 3 . the pitch is placed into a hot isostatic press ( hip ). 5 . the pitch is pressurized to a high initial processing pressure , which increases the boiling point higher than the boiling point at the final processing pressure . 6 . the pitch is heated to a temperature below the solidification point but above the liquid and boiling point which typically occurs if processed at the final processing pressure . 7 . the pitch is depressurized from the initial processing pressure to the final processing pressure while maintaining the temperature which is above the pitch boiling point at the final processing pressure , thus producing a porous artifact . 8 . the artifact is heated to a temperature that solidifies and cokes the porous artifact . 9 . the artifact is cooled to room temperature while allowing natural depressurization during cooling . 10 . the artifact is depressurized of any remaining pressure to atmospheric pressure . 12 . the artifact is then heat - treated to a sufficient temperature to completely carbonize the artifact . 13 . the artifact is then heat - treated to a sufficient temperature to graphitize the artifact . the process of the invention heats the pitch under an “ increased pressure ” which , in effect increases the thermal boiling point . that is , the process temperatures can exceed the “ normal ” boiling point of the pitch without the pitch actually boiling . in the first example which follows , the hip was pressurized to 8000 psi as the “ initial processing pressure .” this increased pressure will be understood to be an arbitrary number which could be anywhere in the range from about 4000 to 30 , 000 psig . in other words , assuming that a doubling of pressure generally increases boiling point by about 10 ° c ., one could roughly estimate the boiling temperature of the pitch to be affected as follows : 1000 psi 425 ° c . 2000 psi 435 ° c . 4000 psi 445 ° c . 8000 psi 455 ° c . based upon this theoretical analysis , 8000 psi was selected as an acceptable “ initial processing pressure ” to achieve the desired pressurization induced boiling effect . the final processing pressure is also an arbitrary number which is generally in the range from about 1000 and 30 , 000 psig . as will be evident from the examples which follow the final processing pressure affects both the ultimate thermal conductivity and apparent density of the finished artifact . by employing final processing pressures which are greater than about 1000 psig , apparent densities are increased above 0 . 70 g / cc and thermal conductivities exceed 250 w / mk . the following examples are intended to be illustrative of the process steps of the invention without being limiting : 1 . the mold is filled with a predetermined amount of pitch to give an appropriate foam height . 3 . the hip vessel is evacuated to & lt ; 2 torr with the vacuum being held for 15 minutes . 4 . the vessel is pressurized to 8000 psig with nitrogen gas . 5 . the pitch is heated from room temperature to 300 ° c . at a rate of 3 . 5 ° c . per minute . 6 . the pitch is held at 300 ° c . for 1 hour . 7 . the pitch is heated from 300 to 450 ° c . at a rate of 2 . 0 ° c . per minute . 8 . the pitch is held at 450 ° c . for 1 hour . ( this increases the viscosity of the liquid pitch ). 9 . the vessel is depressurized from 8000 to 2000 psig at a rate of 175 psi per minute while maintaining a temperature of 450 ° c . ( at this stage , the liquid pitch begins to boil and generate porosity .) 10 . the artifact is heated from 450 to 475 ° c . at a rate of 2 . 0 ° c . per minute . 11 . the artifact is held at 475 ° c . for 1 hour . ( this is the point at which the artifact begins to set ). 12 . the artifact is heated from 475 to 500 ° c . at a rate of 0 . 5 ° c . per minute . 13 . the artifact is held at 500 ° c . for 30 minutes . ( at this point , the artifact fully solidifies ). 14 . the artifact is heated from 500 to 600 ° c . at a rate of 1 . 0 ° c . per minute . ( this is the stage at which the artifact begins to coke .) 15 . the artifact is held at 600 ° c . for 2 hours . 16 . the artifact is cooled from 600 ° c . to room temperature at a rate of 2 . 0 ° c . per minute . 17 . the vessel naturally depressurizes during cooldown from 600 ° c . to room temperature . 18 . the remaining vessel pressure is released at a rate approximately 30 psi per minute . 19 . the artifact is removed from the hip and its mold . 20 . the artifact is then heat treated to approximately 1000 ° c . for carbonization . 21 . the artifact is then heat treated to approximately 2800 ° c . for graphitization . results : thermal conductivity ranged from 131 - 207 w / mk . apparent density ranged from 0 . 70 - 0 . 74 g / cc . 9 . the vessel is depressurized from 8000 psi to 3000 psi at a rate of 175 psi per minute while maintaining a temperature of 450 ° c . results : thermal conductivity ranged from 180 - 247 w / mk . apparent density ranged from 0 . 84 - 0 . 85 g / cc . 9 . the vessel pressure is held at 8000 psig while maintaining a temperature of 450 ° c . 8 . the pitch is held at 450 ° c . for 1 . 5 hours . 9 . the vessel is depressurized from 8000 psig to 2800 psig at a rate of 260 psi per minute while maintaining a temperature of 450 ° c . an invention has been provided with several advantages . the process of the invention results in solid , high thermally conductive porous graphites having more uniform density gradient properties . the increased viscosity of the pitch during the processing operation reduces pore / bubble sizes within the ultimate porous artifact . manipulation of the final process temperature allows greater control over pore size . additionally , changing the hold times and temperature along with the various upper and lower pressure limits allows the production of a wider variety of porous graphite products . the porous solid graphites of the invention exhibit thermal conductivities which exceed 70 w / mk , and generally range from about 90 - 300 w / mk with apparent densities ranging from about 0 . 678 g / cc - 1 . 5 g / cc . while the invention has been shown in only one of its forms , it is not thus limited , but is susceptible to various changes and modifications without departing the sprit thereof .