according to the present invention such fillers are mixed with organic additives before they are added to the basic resinous substances . these additives bind ionized impurities , for example , by the so - called chelate formation , so that the deleterious influence of the undesirable impurities disposed on the semiconductor surface , in its vicinity , in the fillers or in the resins , is avoided . consequently , impurities contained in the fillers can also not exert any unfavorable influence on the resins or on the semiconductor material so that the necessity of using highly pure and thus very expensive fillers is not necessary . the selection of the chelate forming additive depends on the process temperatures during the production stages and on the temperatures during use of the intended semiconductor system , as well as on the type of impurities encountered which are primarily deposited on the semiconductor surface during the removal , cleansing and contacting processes , or which may be contained in the basic resinous substances and fillers as a result of their manufacturing processes , as well as on the solubility in a solvent or in one of the intended basic substances to produce a desired mixture . the proportion of the chelating additive is determined by the saturation of the quantity of the respective filler and may be as high as 10 percent by weight with reference to the weight of the filler . the proportion can go as low as 0 . 02 %. suitable chelate forming additives are , for example , organic chelating agent , suitable as derivatives of fluorone , e . g . gallein , resorcinbenzein ; derivatives of xanthone , e . g . euxanthone , ravenillin ; derivatives of cumarin , e . g . esculetin , ellagic acid ; derivatives of chromone , e . g . flavones , isoflavones ; derivatives of quinoline , e . g . quinaldinic acid , cuproin ; derivatives of triarylmethane , e . g . phenolphthalein , aurin , eriocromcyanin ; derivatives of quinone , e . g . naphthoquinone , anthraquinone ; derivatives of phenoxazine , e . g . gallocyanine ; derivatives of thiazolidin , e . g . rhodanine ; derivatives of imidazolone ; derivatives of pyrazolone ; derivatives of squaric acid , e . g . 3 - hydroxy - 1 , 2 , 3 - triresorcyl - cyclobutenone -( 4 ), derivatives of porphyrin and of phthalocyanine as well as the azo coloring agents , the azomethine and the azine coloring agents . a further aspect of the present invention consists in employing together with the chelate forming additives , strongly surface - active fillers . thereby the additive as well as impurities are adsorptively bound and undesirable reactions of impurities occurring in the fillers with the basic substances are substantially prevented . moreover , the effect of the surface binding forces of such strongly adsorptive fillers serves to reduce the proportion of chelate forming additives which can be used only in a highly pure form . such strongly surface active fillers include , for example , highly dispersed silicic acids , metal oxides , calcium carbonate , calcium sulfate or calcium silicate . usually the active surface of the various modifications of such fillers is known so that by once adding an additive to a first such filler the required proportion of the same additive for another filler can be determined from the ratio of the surface of the first filler to that of the other filler . to produce the encapsulating materials of the present invention , the chelating additive is initially dissolved in a solvent , such as for example galleine in alcohol . the filler selected for intended admixture is then introduced into this solution , preferably in a surface active form and as finely divided as possible . after adsorption of the additive on the filler particles the filler solution is filtered . the then present quantity of finegrained filler to which is the solvent still adheres and which at least partially covered with the additive is dried by heating to above the boiling point of the solvent or in a vacuum . the processing can now be carried in a known manner in that the thus pretreated filler is mixed with a thin - flowing resin which is available for example in a prepolymerized or precondensed state for the production of molded masses . the thus resulting mass is heated in order to remove gases and then strongly cooled in order to convert it into a vitreous hard state and is then ground into a powder or granulate for the further processing in measured amounts . the encapsulation of semiconductor bodies by means of press molds is then effected , for example , in that the granular encapsulation mass is introduced into a container , is heated therein until it softens or becomes plastic and is then injected into the mold under pressure and in metered quantities , whereupon it hardens in the mold at the appropriate temperature . resins and additives may also be processed in a known manner by the addition of hardening agents and polymerization initiating or accelerating substances to produce casting masses in which the components are embedded by conventional casting techniques . there further exists the possibility of first introducing an additive which is soluble in the selected resinous ingredient into this substance , and then admixing the filler therewith . the chelate forming additive is able by adsorption on the filler , to chelate impurities in the form of ions or atoms which are bound to the filler or , when it is added to the resinous substance , it can form a chelate bond with the impurities contained in the resinous substance . moreover , based on the relatively large quantity of additive compared to the respective proportion of impurities to be bound , a further chelate forming effect with foreign ions is possible , particularly on the semiconductor surface . the additives according to the present invention , which exhibit a high thermal stability , at the temperatures encountered in use of the intended semiconductor devices , as well as high purity , form stable chelates with the impurities which chelates exhibit comparably higher thermal stability , and thus forming no undesirable reaction with the basic substance . the change in the dipole moment and / or the dielectric constant of the encapsulation mass connected with the chelate formation does not have any adverse effect on the electrical behavior of the encapsulation mass . if desired , two or more chelate forming additives may be admixed at the same time , one of which for example , binds the foreign ions disposed on the semiconductor surface , and the other additive or additives forms chelates with the impurities of the filler and / or the resinous substance . thus , all impurities which may occur in the production of the semiconductor bodies and their contact portions as well as in the production of the encapsulation masses , and which are well known to the person skilled in the art can thus be made ineffective by a chemical bond . the advantages of the present invention are mainly that special measures for the stabilizing surface treatment of semiconductor bodies before their encapsulation are eliminated and the undesirable impurities disposed on the semiconductor surface and in the encapsulation mass are bound , thus removing their influence on the blocking behavior . furthermore , the use of strongly adsorbing fillers permits a reduction in the amounts of the chelate forming additives used . the following examples serve to illustrate several presently preferred embodiments of the invention in the form of particular compositions . the respective resin may exist in a solid or liquid condition which depends on structure and the degree of polymerization or condensation . its mixture with a hardener is stated by the producers and is not object of this invention . the hardener also may be solid or liquid . at production of encapsulation compounds according to this invention and as it is mentionned for example subsequently , at first resin and hardener are moulten seperately , then fillers and additives and finally the hardener are admixed to the liquid resin . for use as molding compound the mixture is kept on a temperature determined by the features of the resin for a longer time and is changed thereby in a gel - like condition , the so - called b - condition , until resin and hardener will have reacted . after that , the mixture is cooled down and e . g . pulverized . for processing as encapsulation compound then it is changed into the molecular final condition under pressure at corresponding temperature and preferentially by means of catalysts . these known procedural steps do not belong to this invention and are not further explained . if such a mixture is used as casting compound so it is processed in a liquid condition after addition of all components at a correspondingly high temperature at which the reaction between resin and hardener must be reached in a very short time . consequently the mixture is to be changed very rapidly from the beginning condition into the molecular final condition . if resin and hardener are liquid at first the different additions and then the liquid hardener are admixed to the liquid resin . for the further processing the above explanations are applicable . the sealing of semiconductor bodies may now follow in the way that these ones are either put into a mold , pressed around with the composition according to invention or arranged in a housing at use of the casting technique and embedded into the composition by means of casting the same into the housing . with the known resins provided according to invention molding or casting masses may be produced while silicone rubber is applicable only as casting mass . bisphenol a - epoxy resin as organic base substance is mixed with calciumcarbonate powder as filler in such quantities that , with regard to the necessary addition of an anhydride hardener mentionned by the resin producer , a mixing ratio of 30 per cent of weight resin with hardener to 67 per cent of weight filler is given . to this mixture 3 per cent of weight of the ellagic acid , a cumarin derivative , are added . epoxynovolake resin as base substance is mixed with silicid acid powder as a first filler and aluminum silicate powder as a second filler in such quantities that , with regard to the necessary addition of an anhydride hardener , a mixing ratio of 30 per cent of weight resin with hardener to 48 per cent of weight of the said first filler and to 20 per cent of weight of the said second filler is given . to this mixture 2 per cent of weight 9 - phenyl - 2 , 3 , 7 - trihydroxy - 6 - fluorone , a derivate of fluorone , are added which is forming chelates especially with metallic impurities of lead , molybdenum , tin and antimony . silicone resin as base substance is mixed with silicid acid powder as filler in such a quantity that , with regard to the necessary quantity of a peroxide hardener , a mixing ratio of 27 per cent of weight resin and hardener to 70 per cent of weight filler is existing . to this mixture 3 per cent of weight 5 -( 4 - dimethylaminobenzalrhodanin ) as a thiazolidin derivative are added which is acting as chelate former e . g . for silver , gold , copper , mercury . bisphenol a - resin and epoxynovolake resin as components of the base substance are added with alumina as filler in such a quantity that , with regard to the necessary quantity of bf 3 - amincomplex as hardener , a mixing ratio of 15 per cent of weight of the first basic substance component to 16 per cent of weight of the second basic substance component to 68 per cent of weight of the filler is existing . to this mixture 1 per cent of weight gallocyanine as a phenoxazine derivative is added . polyimide resin as pre - polymerized base substance is mixed with silicid acid powder as filler in a ratio of 35 to 64 , 5 per cent of weight . to this mixture 0 , 5 per cent of weight of metal - free phthalocyanine are added for chelating especially with iron , copper , nickel , cobalt , platinum . silicone rubber as base substance is mixed with silicid acid powder as filler in such a quantity that , at addition of a corresponding portion of amine hardener , a mixing ratio of 40 per cent of weight rubber with hardener to 59 per cent of weight filler is given . to this mixture 1 per cent of weight 4 , 5 - diphenyl - imidazolon (- 2 ) is admixed . 45 per cent of weight polyamidimide resin as pre - polymerized base substance are mixed with 53 per cent of weight alumina as filler . then , 2 per cent of weight auritricarbon acid are admixed for chelating especially with aluminum and copper . epoxynovolake resin as base substance is mixed with silicid acid powder as filler in such a quantity that , with regard to the necessary quantity of an anhydride hardener , a mixing ratio of 32 per cent of weight resin with hardener to 67 per cent of weight filler is existing . to this mixture 1 per cent of weight 3 - hydroxy - 1 , 2 , 3 - triresorcyl - cyclobutenon -( 4 ), a squaric acid derivative , is admixed . instead of the derivative of squaric acid in the mixture according to example 8 e . g . glyoxal - bis -( 2 - hydroxyanil ) as a derivative of the azomethine coloring agents can be used . the portion of the mentioned chelate formers can be substantially lower as 1 per cent of weight at a respective high portion of the base substance and the filler . it will be understood that the above description of the present invention is susceptible to various modifications , changes and adaptations , and the same are intended to be comprehended within the meaning and range of equivalents of the appended claims .