in the present invention , the electrostatic chuck is most desirable for the wafer attracting apparatus ; however , a vacuum chuck is also available . as the wafer , a semiconductor wafer requiring high purity is most desirable . however , the present invention is also applicable to the iron wafer and the aluminum wafer . if the present invention is applied to the electrostatic chuck , the shape , etc . of the electrostatic chuck are not limited to specific ones . as a substrate perform of the electrostatic chuck , ordinary substrates to be used for this purpose may be used . that is , the substrate preform may include a ceramic substrate preform prepared by the steps of forming a green molded body preliminarily uniaxially molded in which an electrode is buried and subjecting the green molded body to hp sintering . it is preferable that an electrostatic chuck electrode to be embedded in a ceramic substrate is made of a sheet - shaped bulk metallic material . here , the &# 34 ; sheet - shaped bulk metallic material &# 34 ; means , for example , a linear bulk body , a planar bulk body or the like in the form of a integrally shaped planar member . in this case , an electrode for the electrostatic chuck is preferably made of a high melting point metal , since it is fired together with ceramic powder such as alumina powder or aluminum nitride powder . the high melting point metals includes , for example , tantalum , tungsten , molybdenum , platinum , rhenium , hafnium and their alloys . for the viewpoint of preventing the semiconductor wafer from being contaminated , tantalum , tungsten , molybdenum , platinum and their alloys are preferred . ( 2 ) a sheet - shaped bulk material in which many small void are formed . the bulk material ( 2 ) includes a bulk material made of a planar body having numerous small holes and a net - shaped bulk material . a punched metal may be recited as an example of the planar bulk having numerous small holes . however , if the bulk material is made of a punched metal having a high melting point , it is difficult and highly costly to punch many small holes in the planar high melting point metal because of its high hardness . compared with this , if the bulk material is to be made of a wire net , wires made of a high melting point metal are so easily available that the metal wire net may be produced by knitting the wires . the mesh shape , the wire diameter , etc . of such a metal wire are not limited specifically . however , a 150 - mesh metal wire net having a wire diameter of 0 . 03 mm to a 6 - mesh metal wire net having a wire diameter of 0 . 5 mm were practically usable without causing any problem . in addition , the cross - sectional shape in the width direction of the linear material constituting the metal wire net may be circular , elliptical , rectangular or of variously rolled shapes . &# 34 ; one mesh &# 34 ; means one wire per inch . it is possible to embed a resistive heater and / or a plasma generation electrode as well as an electrostatic chuck electrode in the ceramic substrate constituting the electrostatic chuck . as the ceramic substrate for constituting a wafer attracting apparatus which is the very target of the present invention , alumna , aluminum nitride , silicon nitride , silicon carbide and the like having a porosity of 95 % or more can be recited by way of example . alumina and aluminum nitride are particularly preferable . a method for working the attracting surface in the wafer attracting apparatus according to the present invention should not be limited specifically . preferably , a lapping with abrasive grains made of a hard material , such as diamond , having the average grain diameter or 1 μm or less or preferably 0 . 5 μm or less may be adopted . by this processing , a ductile worked surface having ra = 0 . 01 μm or less can be obtained . the polishing with abrasive grains of silica , cerium oxide or the like having the average grain diameter 2 μm or less in a neutral or alkaline aqueous solution as a processing liquid diameter may be adopted . by this polishing , it is possible to obtain ductile worked surface having ra = 0 . 05 μm or less . it is also possible to adopt lapping and polishing in combination . the same or different high purity cleaning agents may be used for cleaning the ductile worked surface while being rubbed with the cleaning member and ultrasonic cleaning . as the high purity cleaning agent , deionized water having a resistivity of 16 mω or less with the number of fine particles in the water being 10 / ml or less is preferable , however , an aqueous solution of a surface active agent and an alkaline cleaning agent may be used as well . it is particularly preferable that the temperature of the high purity cleaning agent is set in a range from room temperature to 80 ° c . as a cleaning member for cleaning the attracting surface of the substrate of the wafer attracting apparatus , a brushing member is particularly desirable . the material for that brush of the brushing member which directly contacts with the attracting surface of the substrate is preferably polyurethane resin , teflon resin , polyvinyl alcohol resin called &# 34 ; bellclean ( trademark )&# 34 ; ( manufactured by kanebo co ., ltd .) or the like . the frequency of ultrasonic waves in the ultrasonical cleaning is not specifically limited . however , it is noted that if the frequency of the waves is not less than 100 khz but not more than 1000 khz and the output of the ultrasonic waves is 3 . 0 to 6 . 0 w / cm 2 , the number of particles can be particularly reduced . a metal wire net made of molybdenum was used as the electrostatic chuck . the wire net is a net obtained by knitting 0 . 12 mm - diameter molybdenum wires at a rate of 50 / inch . aluminum nitride powder was uniaxially press molded into a disc - like preform . at that time , the wire net was embedded into the preform . the preform was installed in a mold and sealed in a carbon foil . the preform was fired by hot pressing at a temperature of 1 , 950 ° c . under pressure of 200 kg / cm 2 for a retention time of two hours , thereby obtaining a sintered body . the relative density of the sintered body was 98 . 0 % or more . the resultant electrostatic chuck was 200 mm in diameter and 8 mm in thickness . the hot pressing firing makes it possible to effectively reduce residual pores and to obtain a sintered body having a relative density of 99 . 8 % or more . an attracting surface of the above - stated electrostatic chuck was lapped . more specifically , the electrostatic chuck was first placed on a copper board ( trade name : hyprez copper manufactured by japan engis , co ., ltd .) and lapped with diamond abrasive grains having the average grain diameter of 6 μm . thereafter , it was lapped by using diamond abrasive grains of 3 μm in the average grain diameter . the center line average surface height ra of the lapped surface was measured to be 0 . 080 μm by a surface roughness meter . the electrostatic chuck was dipped into deionized water inside a class 1000 clean room , and subjected to ultrasonic cleaning at a frequency of 730 khz , an ultrasonic output of 3 . 7 w / cm 2 , and a temperature of 25 ° c . for 5 minutes . next , the electrostatic chuck was dried with hot air at 130 ° c . in a clean oven , and then cooled . a mirror finished surface of a silicon wafer was attracted onto the attracting surface of the electrostatic chuck at 200 ° c . in air , and the attracted state of the wafer to the electrostatic chuck was released . the number of particles , 0 . 2 μm or more in diameter , adhering to the mirror finished surface of the silicon wafer was measured by a light - scattering type particle counter . as a result , the number of the particles attached was 94 , 400 . fig5 is a distribution diagram showing particle distribution measured by the light - scattering type particle counter . furthermore , the elemental analysis was made with respect to the particles on the silicon wafer by means of an energy dispersing type spectral analyzer . fig1 shows the analysis result . a scanning electron microscopic photograph of the ceramic tissue of the attracting surface of the electrostatic chuck is shown in fig3 . as can be seen from fig3 aluminum nitride particles were separated from the attracting surface . this indicates that the working of the attracting surface is a brittle working involving the separation of aluminum nitride particles . as in the case of comparison example 1 , an attracting surface of a electrostatic chuck was lapped . likewise , the attracting surface of the chuck was brushed for 5 minutes in deionized water by using a roll brush made of polyurethane resin inside the class 1000 clean room . thereafter , the electrostatic chuck was dried with hot air at 130 ° c . in the clean oven , and cooled . with respect to the electrostatic chuck , the number of particles attached to a mirror finished surface of a silicon wafer was measured as in the case of comparison example 1 . the measurement result was 80 , 400 . the elemental analysis for the particles on the silicon wafer and the ceramic tissue on the attracting surface were similar to those of comparison example 1 . after manufacturing an electrostatic chuck as described above , the electrostatic chuck was placed on the copper board ( trade name : hyprez copper manufactured by japan engis , co ., ltd .) and lapped with diamond abrasive grains having the average grain diameter of 6 μm . the electrostatic chuck was further lapped with diamond abrasive grains having the average grain diameter of 3 μm . thereafter , the resulting electrostatic chuck was then placed on a pure tin board and lapped with diamond abrasive grains having the average grain diameter of 0 . 5 μm . the ra of the lapped surface was 0 . 008 μm . the electrostatic chuck was dipped into deionized water in the class 1000 clean room , and ultrasonically cleaned at a frequency of 730 khz , an ultrasonic output of 7 w / cm 2 and a temperature of 25 ° c . for 5 minutes . next , the electrostatic chuck was dried with hot air at 130 ° c . in the clean oven , and then cooled . with respect to the electrostatic chuck , the number of particles adhering to a mirror finished surface of a silicon wafer was measured as in the case of comparison example 1 . the number of the particles attached was 24 , 900 . the result of the elemental analysis for the particles on the silicon wafer was the same as that of comparison example 1 . an electrostatic chuck was manufactured as described above , which had a worked surface with the center line average height ra = 0 . 008 was obtained . the attracting surface of the chuck was brushed in deionized water for 5 minutes with a roll brush of polyurethane resin inside the class 1000 clean room . thereafter , the electrostatic chuck was dried with hot air at 130 ° c . in the clean oven , and then cooled . with respect to the electrostatic chuck , the number of particles attached to a mirror finished surface of a silicon wafer was measured as in the case of comparison example 1 . the number of the particles attached was 19 , 500 . the result of the elemental analysis for particles on the silicon wafer was the same as that of comparison example 1 . after manufacturing an electrostatic chuck as described above , the chuck was placed on the copper board ( trade name : hyprez copper manufactured by japan engis , co ., ltd .) and lapped with diamond abrasive grains having the average particle diameter of 6 μm . the chuck was then lapped with diamond abrasive grains having the average particle diameter of 3 μm . furthermore , the electrostatic chuck was placed on a pure tin board and lapped with diamond abrasive grains of 0 . 5 μm . the ra of the lapped surface was 0 . 008 μm . the ductile worked surface of the chuck was subjected to image analysis , which revealed that no holes having diameters of 0 . 1 μm or more existed in a range of 50 μm × 70 μm although observed at 100 visual fields . the attracting surface of the electrostatic chuck was brushed with a roll brush of polyurethane resin in deionized water for 5 minutes inside the class 1000 clean room . thereafter , the electrostatic chuck was dipped into deionized water and to ultrasonically cleaned at a frequency of 730 khz , an ultrasonic output of 3 . 7 w / cm 2 , a temperature of 25 ° c . for 5 minutes . the electrostatic chuck was then dried with hot air at 130 ° c . in a clean oven , and then cooled . with respect to the electrostatic chuck , the number of particles attached to a mirror finished surface of a silicon wafer was measured as in the case of comparison example 1 . the number of the particles attached was 720 . as can be understood from this , according to the present invention , the number of particles attached to the mirror finished surface of the silicon wafer could be successfully reduced by about 99 % from that of comparison example 1 . fig6 is a distribution diagram showing the particle distribution measured by the light - scattering type particle counter . a scanning electron microscopic photograph of a ceramic tissue of the attracting surface of the electrostatic chuck is shown in fig4 . as is clear from fig4 separation of aluminum nitride grains from the attracting surface was not observed and the ductile surface was seen . the diameters of small holes in the ductile surface were 0 . 07 μm or less . it is noted that the small holes are portions in the vicinity of bottom surfaces of holes at which aluminum nitride grains were separated prior to final lapping . the holes could be made smaller thanks to the final lapping . example 2 was the same as example 1 except that the frequency was 28 khz and the ultrasonic output was 0 . 8 w / cm 2 at the time in ultrasonic cleaning . as in the case of example 1 , holes having diameters greater than 0 . 1 μm did not exist . as a result , the number of particles attached to a mirror finished surface of a silicon wafer was 2 , 900 . moreover , a scanning electron microscopic photograph of a ceramic tissue of the attracting surface of the electrostatic chuck was the same as that of example 1 . example 3 was the same as example 1 except that the temperature of deionized water was 80 ° c . at the time of ultrasonically cleaning . as a result , the number of particles attached to the mirror finished surface of the silicon wafer was 650 . example 4 was the same as example 1 except that an attracting surface of an electrostatic chuck was polished with a solution of cerium oxide abrasive grains having the average grain diameter of 1 . 8 μm in aqueous lubricant ( trade name ) manufactured by nippon engis co . ltd . the ra of the attracting surface of the electrostatic chuck after polishing was 0 . 03 μm . the height difference among ceramic grains at the attracting surface was 0 . 3 μm or less . no small holes in the ductile worked surface were present . as a result , the number of particles attached to a mirror finished surface of a silicon wafer was 860 . as can be seen from the above description , the wafer attracting apparatus according to the present invention , which includes the ceramic substrate , can largely decrease the number of particles attaching to the back surface of the wafer after the wafer has been attracted onto the attracting surface of the substrate .