the following description of the preferred embodiment is provided to understand the features and the structures of the present invention . please refer to fig1 and fig2 , which are views showing devices used and a connection between an electrochemical impedance analyzer and a probe , according to the present invention . as shown in the figures , the present invention is a method for determining an effective diffusivity of a certain substance through porous materials , which comprises the following steps : ( a ) a first compartment [ 1 ] and a second compartment [ 2 ] are obtained . both compartments [ 1 , 2 ] are loaded with a high - permeable solution [ 11 , 21 ], which is methanol or ethanol added with a conductive solution [ 12 , 22 ]. therein , the high - permeable solution [ 11 , 21 ] comprises a concentration between 0 m ( molar , mole per liter ) and 20 m ; and the permeable solution [ 11 ] in the first compartment [ 1 ] comprises a first concentration higher than a second concentration of the permeable solution [ 21 ] in the second compartment [ 2 ]. in addition , the conductive solution [ 12 , 22 ] is a solution added with a salt , an acidity or an alkalinity ; and comprises a concentration between 0 . 1 m and 2 m . ( b ) a material [ 3 ] is obtained , which is a porous material went through a hydrophilic process or a hydrophobic process having an aperture for every pore [ 31 ] between 1 nm and 100 μm . the material [ 3 ] is then immersed in between the first compartment [ 1 ] and the second compartment [ 2 ] to obtain a concentration gradient of the permeable solution between two ends of every pore [ 31 ]. as a result , the permeable solution [ 11 ] having the first concentration is diffused to the second compartment owing to the concentration gradient . ( c ) a probe [ 41 ] is set in the second compartment [ 2 ] and is connected to an electrochemical impedance analyzer [ 4 ]. ( d ) and , concentration changes are happened to the permeable solution [ 21 ] having the second concentration owing to the diffusing of the permeable solution [ 11 ] having the first concentration . the concentration changes is detected by the probe [ 41 ] and the data of the concentration changes is transferred to the electrochemical impedance analyzer [ 4 ] to obtain resistivity changes of the permeable solution [ 21 ] in the second compartment [ 2 ], so that an effective diffusivity coefficient of the material [ 3 ] is figured out . with the above steps , a novel method for determining an effective diffusivity of a certain substance through porous materials is obtained . please further refer to fig3 and fig4 , which are views showing relations between methanol concentrations and resistances under a temperature of 12 . 5 ° c . and under various temperatures , according to the present invention . for obtaining data shown in the figures , experiments are taken . at an end of the material for testing [ 3 ] is a 500 ml ( milliliter ) high - concentration solution of 10 m methanol added with 0 . 5 m sulfuric acid ; and at the other end of the material for testing [ 3 ] is a 100 ml low - concentration solution of 0 m methanol ( i . e . no methanol ) added with 0 . 5 m sulfuric acid . the probe [ 41 ] is made of two platinum flakes which expose 1 cm 2 ( centimeter square ) of surface area in the low - concentration solution for each and comprise a separation of 1 cm in between . when measurements are taken under the above conditions , the electrochemical impedance analyzer [ 4 ] outputs ac ( alternating current ) signals , which in general are sine - wave signals of 10 mv ( millivoltage ), to the solution to detect a phase lead or a phase lag of the signals ( i . e . the current ) to obtain impedance signals . with the signal data obtained to be processed through an equivalent circuit simulation , a thorough understanding to the electrochemistric reactions is acquired . this is the impedance analysis done by the electrochemical impedance analyzer [ 4 ]. thus , useful information are obtained from the measurements and are divided into three parts according to the frequencies of the signals : the solution resistances shown in the areas of high frequency , the electric double layer impedances shown in the areas of middle frequency and low frequency , and the mass transport impedances shown in the areas of extra - low frequency . the electrochemical impedance analyzer [ 4 ] detects an infinitesimal diffusion in the pores [ 31 ] of the material for testing [ 3 ] through electrochemical impedance spectroscopy . an inference for infinitesimal concentration changes is obtained with the infinitesimal changes shown in the high - frequency area ( representing the solution resistance ) of the spectrum due to the diffusing of the high - concentration solution [ 11 ] to the low - concentration solution [ 21 ]. based on an unsteady - state diffusivity equation ( fick &# 39 ; s law ), an inference for effective diffusivity coefficients for the materials for testing [ 3 ] is obtained by using a commercial software ‘ matlab ’. as shown in fig3 , under a temperature of 12 . 5 ° c ., resistances for solutions with various concentrations of methanol are obtained ; and , through linear regression , a linear equation for methanol concentration and resistance under 12 . 5 ° c . is obtained as r = 3 . 1192 + 0 . 2844 c , where r is the resistance and c is the methanol concentration . as shown in fig4 , resistances for solutions under various temperatures having various concentrations of methanol are obtained . thus , linear equations for methanol concentrations and resistances under various temperatures are obtained through linear regression with the data of the above resistances . those linear equations are as follows : under 12 . 5 ° c . [ 51 ], r = 3 . 1192 + 0 . 2844 c ; under 20 ° c . [ 52 ], r = 3 . 0408 + 0 . 2706 c ; under 30 ° c . [ 53 ], r = 2 . 8302 + 0 . 1817 c ; under 40 ° c . [ 54 ], r = 2 . 6073 + 0 . 3258 c ; and , under 80 ° c . [ 55 ], r = 1 . 8514 + 0 . 3053 c . please refer to fig5 , which is a view showing relations between methanol concentrations and time for a porous carbon fiber went through a hydrophobic process according to the present invention . for obtaining data shown in the figure , porous carbon fibers go through a hydrophobic process with 30 % ptfe ( polytetrafluoroethylene , teflon ) and is coated with a 30 μm microporous layer so that fibers of sgl 31 - ec are obtained . an end of the sgl 31 - ec fiber is immersed in a high - concentration solution of 10 m methanol added with 0 . 5 m sulfuric acid ; and the other end of the fiber is immersed in a low - concentration solution of 0 m methanol ( no methanol ) added with 0 . 5 m sulfuric acid . changes of methanol concentration to time in the low - concentration solution are detected throughout five times of experiments . in the end , by using matlab , an average effective diffusivity coefficient for sgl 31 - ec is obtained as 8 . 05 × 10 − 6 cm2 / s whose standard deviation is 1 . 45 × 10 − 7 cm 2 / s with a precision error below 2 % ( 1 . 8 %). please refer to fig6 through fig1 , which are views showing relations between methanol concentrations and time for porous carbon fibers went through various hydrophobic processes according to the present invention . an experimental environment according to the present invention for obtaining the above figures comprises a material for testing . an end , a first end , of the material for testing is immersed in a high - concentration solution of 10 m methanol added with 0 . 5 m sulfuric acid ; and the other end , a second end , is immersed in a low - concentration solution of 0 m methanol added with 0 . 5 m sulfuric acid . for obtaining data shown in fig6 , five pieces of a porous carbon fiber ( sgl 31 - aa ) are provided to be deposed in the experimental environment as materials for testing while changes of methanol concentration to time are detected at the second end ; for obtaining data shown in fig7 , two pieces of a porous carbon fiber went through a hydrophobic process with 5 % ptfe ( sgl 31 - ba ) are provided ; for fig8 , two pieces of a porous carbon fiber went through a hydrophobic process with 5 % ptfe and coated with a 30 μm microporous layer ( sgl 31 - bc ); for fig9 , two pieces of a porous carbon fiber went through a hydrophobic process with 30 % ptfe and coated with a 30 μm microporous layer ( sgl 31 - ec ); for fig1 , three pieces of a polymeric nano - porous material ( nafion 112 ); and , for fig1 , three pieces of another polymeric nano - porous material ( nafion 117 ). please refer to fig1 , which is a view showing average methanol effective diffusivity coefficients of various porous materials for testing according to the present invention . as shown in the figure , average methanol effective diffusivity coefficients for various porous materials used in fig6 through fig1 are obtained by using matlab with the data in shown in the figures , where the average methanol effective diffusivity coefficient for the porous material used in fig6 [ 61 ] is 1 . 61 × 10 − 4 cm 2 / s ; for the porous material used in fig7 [ 62 ], 3 . 34 × 10 − 5 cm 2 / s ; in fig8 [ 63 ], 9 . 14 × 10 − 6 cm 2 / s ; in fig9 [ 64 ], 9 . 36 × 10 − 6 cm 2 / s ; in fig1 [ 65 ], 9 . 77 × 10 − 7 cm 2 / s ; and , in fig1 [ 66 ], 1 . 28 × 10 − 6 cm 2 / s . please refer to fig1 , which is a view showing a comparison between the effective diffusivity coefficients obtained through the detecting method of the present invention and the effective diffusivity coefficients obtained through gc concentration measurement . as shown in the figure , two effective diffusivity coefficients of the same sgl 31 - bc specimen are obtained : one of 9 . 14 × 10 − 6 cm 2 / s is obtained through the detecting method of the present invention [ 71 ] and the other one of 8 . 93 × 10 − 6 cm 2 / s is obtained through the gc concentration measurement [ 72 ]. by comparing the two effective diffusivity coefficients , a precision error below 2 . 5 % ( 2 . 35 %) is obtained . to sum up , the present invention is a method for determining an effective diffusivity of a certain substance through porous materials , where resistance of a solution is monitored with an electrochemical impedance analyzer to first obtain concentration changes owing to a concentration gradient of the substance in solutions causing the diffusing of the solution through the porous material and then to obtain an inference for an effective diffusivity coefficient of the porous material . the preferred embodiment herein disclosed is not intended to limit the scope of the invention unnecessarily . therefore , simple modifications or variations belonging to the equivalent of the scope of the claims and the instructions disclosed herein for a patent are all within the scope of the present invention .