aspects of the present invention relate to a process for recovering base metal values from oxide materials , specifically metals found , e . g ., in laterite ores , such as nickel , cobalt and copper . in accordance with aspects of the present invention , oxide materials such as , for example , laterite ores , are mixed with ferric or ferrous chloride to produce an iron , aluminum and magnesium - free solution that carries base metals chlorides , such as nickel , cobalt and copper , through indirect hydrochlorination , as described by equations ( 1 ) to ( 3 ) below . fig1 is an illustration of a method 100 for extracting base metals from laterite ore , according to various aspects of the present invention . as described in more details below with respect to fig1 , the oxide material may be initially crushed or granulated to liberate the oxide base metals prior to mixing with ferric or ferrous chloride , as indicated in step s 101 . the particle reduced oxide material may be mixed with ferric or ferrous chloride and agglomerated with a mineral acid if necessary , as indicated in step s 102 . according to various aspects , the mix of particle - reduced ore and ferric or ferrous chloride is contacted with enough wet air at high temperature to convert base metals into chlorides and iron , and aluminum and magnesium to their respective oxides , as indicated in step s 103 . gibbs free energy behavior for hydrochlorination with using both ferric chloride and ferrous chloride is illustrated in fig2 and 3 . to obtain an iron -, aluminum - and magnesium - free solution , water may be added to the converted ore at a ph of between about 8 and 2 . the ph can be controlled using a mineral acid such as , for example , hydrochloric acid , in order to avoid the newly formed oxides from leaching . in accordance with aspects of the present invention , after solid - liquid separation such as illustrated in step s 104 , the solution becomes therefore iron -, aluminum - and magnesium - free . the solubilized base metals can then be purified into sellable products by various methods known by those skilled in the art . the solid portion of the solid liquid separation , after proper washing of residual solution , may be submitted to a high intensity magnetic separation to separate hematite from other oxides . neutralization may optionally be needed . hematite may then be contacted with hydrochloric acid to produce ferric chloride and water . in order to produce ferrous chloride , a reducing agent , such as , but no limited to , iron may be added to the system . in accordance with aspects of the present invention , ore is extracted from the mine to provide beneficiation plant a run - of - mine . the run of mine may then be prepared to be fed into the extraction plant . for that , it is preferable that the size of the ore is reduced to an appropriate size to liberate base metals oxides for proper indirect hydrochlorination and efficient solubilization . in accordance with aspects of the present invention , ore size may be kept between 2 mm and 0 . 050 mm , and optionally less than 0 . 5 mm . these sizes can be obtained by different conventional unit operations well known and described in the literature , such as , but not limited to , crushing and grinding . ore may be separated in two fractions : a first one that is rich in nickel and having about the sizes described above , and another one that is poor in nickel . the fraction of ore that is poor in nickel may be discarded . it should be noted that the above - discussed fractions and sizes are exemplary , and those skilled in the art may provide more or less fractions of varying sizes . in accordance with aspects of the present invention , after size reduction , the ore is mixed or agglomerated with ferric or ferrous chloride sufficient for total hydrochlorination of payable base metals . ferric or ferrous chloride can be added in the ratio between , for example , 0 . 05 and 1 . 5 times the ore mass , and optionally between 0 . 1 and 0 . 5 times the ore mass . water or a mineral acid may optionally also be added to improve agglomeration . if ferrous chloride is used , an oxidizing agent may also be added to the ore , such as , but not limited to , oxygen , potassium permanganate , ozone or hydrogen peroxide . the oxidizing agent may be added in a similar mass ratio range as ferrous chloride . it should be noted that ferric or ferrous chloride may be obtained by any available source . in accordance with aspects of the present invention , the oxidizing agent reacts with ferrous chloride , forming hematite and hcl , as shown by the reaction below . in accordance with aspects of the present invention , the temperature range needed for this reaction ranges may be between 60 ° c . and 600 ° c ., optionally between about 100 ° c . and about 300 ° c . for kinetics reasons . residence time may range between 0 . 5 hour and 12 hours , optionally between 1 hour and 2 hours . when using ferric chloride , an oxidizing agent may not be necessary . the properly agglomerated ore is taken to a hydrolysis stage , usually but not limited to a kiln , where the ore is submitted to conditions under which ferric and / or ferrous chloride is decomposed , producing stable hematite or other hydrated iron oxide , and hcl . during this step , the agglomerated ore is then submitted to elevated temperature , ranging between 60 ° c . to 600 ° c ., for between a minimum of about 5 minutes and a maximum of about 24 hours . sufficient water may need to be added , but enough water may already be present in ore moisture . the decomposition reaction of the ferric chloride can be described as shown below . the temperature range needed for this second reaction mechanism may ranges between 60 ° c . and 600 ° c ., and optionally around 150 ° c . to 350 ° c . residence time requirements may be the same as the residence time requirements for ferrous chloride . accordingly , it is clear from the reactions expressed by equations ( 1 ) and ( 2 ) that enough water must be provided to the system in order to ensure proper hydrolysis . ore - free moisture may thus be controlled to be between 1 % and 20 % ( m / m ), and water vapor may also be added to the system in order to provide enough water . the hcl generated as described above in equations ( 1 ) and ( 2 ), inside the agglomerated ore , is used to form value base metal chlorides , as shown below for a generic transition metal m that forms an oxide mo : according to various aspects of the current invention , the newly formed chlorides are soluble in water , but the metal m such as iron , aluminum and magnesium is already in a stable form as an oxide . accordingly , equation ( 3 ) would yield an iron , magnesium and aluminum - free effluent , easily purified by various methods available in the literature and known by those skilled in the art . according to various aspects of the current invention , after hydrochlorination as described before is terminated , the ore could be stacked in a heap and leached with acidified water , with a ph of at least 7 . any mineral acid may be used such as , for example , sulfuric acid , nitric acid or hydrochloric acid . according to various aspects , the acid content may be increased up 100 g / l , but the ph may be kept between about 1 and about 3 . leaching solution could be recycled , with acid make - up , to increase payable metals concentration . another possible way of solubilizing the payable metals is through agitated tanks , keeping ph at the same ranges . residence times may be determined to be between about 5 minutes and about 24 hours , and optionally between 30 minutes and 120 minutes . also , the solution may be heated to increase solubilization kinetics , and the percentage of solids may be kept between about 5 % and about 50 %, depending on how concentrated the solution needs to be . optionally , the percentage of solids may be in the range 15 % and 35 %. it should be noted that any other form of solubilization known by those skilled in the art may also be employed . according to various aspects of the current invention , after proper solubilization and solid - liquid separation , any method of downstream purification may be used . according to various aspects , there is no need of an iron removal stage and an aluminum removal stage , or of effluent treatment for magnesium or manganese removal , because these elements were already stabilized as oxides in the furnace . according to various aspects of the current invention , tailings produced from the solid - liquid separation may be contacted with a high intensity magnetic field , after first been washed to remove residual base metals solution . neutralization may also be needed , but may not be necessary . the magnetic field separates hematite from other oxides . it should be noted that other separation methods , known from those skilled in the art , can be used instead of a magnetic separator . according to various aspects of the current invention , in order to produce ferric or ferrous chloride , hematite may be contacted with hydrochloric acid , producing the chosen iron chloride , as described by equations below : it should be noted that any reducing agent may be used to form ferrous chloride , such as , for example , metal iron ( fe ). ferric chloride may also be produced by contacting metal iron with hydrochloric acid in oxidizing conditions . hydrochloric acid may be produced by reacting a chloride salt , such as sodium chloride , potassium chloride , with an acid , such as sulfuric acid . according to various aspects , potassium chloride may be used as a chloride salt . reacting potassium chloride with sulfuric acid produces dry hydrochloric acid ( e . g ., free of water ) and potassium sulfate , a useful byproduct . according to various aspects of the current invention , one of the advantages of this technology is that hcl is used in a controlled form , reducing the need for expensive equipments , cheaper construction materials and simpler equipments are needed . gas - solid interaction is not a big concern because hcl is generated within the agglomerated ore , diffusing throughout the material . that way , a simple kiln such as , but not limited to , a rotary kiln , can be employed at the hydrolysis stage , thus reducing capital costs . downstream equipments are also simpler because no high chloride solution will be produced . various aspects of the process according to the current invention provide the advantage of base metal extraction with chlorides while reducing one of its drawbacks which is the need of special engineering and materials of construction . further , the following features can also summarize the benefits of various aspects of the present invention : i ) increased extraction of value metal , such as copper , nickel and cobalt ; ii ) better deposit exploitation ; iii ) reduced acid consumption ; iv ) better settling properties of pulp ; v ) reduced consumption of flocculants ; vi ) no need for saprolite / limonite separation ; vii ) controlled hcl usage ; viii ) simple engineering ; ix ) simple operation ; and x ) reduced capital costs . the following examples are illustrative of the experimental process according to various aspects of the current invention : 100 g of a limonite - type ore is mixed with a laterite ore comprising 1 . 03 % ni , 35 . 06 % fe , 12 % si , 4 . 05 % mg , 1 . 94 % al , 0 . 64 % mn and 0 . 065 % cobalt , and with 10 g of ferric chloride hexahydrated for 180 minutes and 400 ° c . extraction results are in table 1 below . a laterite charge is subjected to a 90 minute indirect hydrochlorination at 300 ° c . with wet air injection . the sample contains 2 . 01 % ni , 0 . 073 % co , 49 . 1 % fe , 3 . 07 % mg and 06 % sio 2 . extraction results are show in table 2 below . while this invention has been described in conjunction with the exemplary aspects outlined above , various alternatives , modifications , variations , improvements , and / or substantial equivalents , whether known or that are or may be presently unforeseen , may become apparent to those having at least ordinary skill in the art . accordingly , the exemplary aspects of the invention , as set forth above , are intended to be illustrative , not limiting . various changes may be made without departing from the spirit and scope of the invention . therefore , the invention is intended to embrace all known or later - developed alternatives , modifications , variations , improvements , and / or substantial equivalents .