before proceeding to the detailed description of the preferred embodiment and the preferred manufacturing techniques for making it , several general comments should be made about the materials useful in the present invention . with regard to the thermoplastic polymer , polysulfone materials are preferred , especially amoco p - 1835 polysulfone which has a published glass transition temperature of 190 ° c . other thermoplastic polymers which could be used in the conductive composition of the present invention include polyarylsulfone resins , polyethersulfone resins , polycarbonate resins , polyphenylene oxide resins and cellulose acetate resins . electrically conductive particles useful in the present invention include flakes , spheres , dendrites , regularly shaped particles , whiskers and needles of electrically conductive materials , such as metals ( silver , copper , nickel ), alloys ( silver - gold , copper - nickel ), composites ( silver coated nickel , silver coated graphite ), and electrically conductive non - metals ( carbon blacks , graphite ). these materials are mentioned for purposes of illustration only . a most preferred electrically conductive particle is a silver flake particle having an average particle size of less than 10 microns , such as the silver flake product available from aldrich chemical company , catalog no . 32 , 707 - 7 and from degussa corporation -- metz division , catalog no . sf - 65 . another preferred electrically conductive particle is a chaining carbon black , vulcan xc - 72 , available from cabot corporation that has been deoxidized . finally , with regard to the solvents which may be used , one characteristic is the ability to dissolve the thermoplastic polymer . another is to serve as a carrier for the electrically conductive particles . suitable solvents for polysulfone include butyrophenone , such as that available from aldrich chemical company , catalog no . 12 , 433 - 8 . other solvents which may be used for polysulfone include other alkylphenones , halogenated hydrocarbons such as bromochloromethane and chloroform , and cyclic ketones such as cyclopentanone and cylcohexanone . other solvents may be used for other thermoplastic resins as would , in and of itself , be generally known to those skilled in the art . the present invention can best be understood by proceeding with a detailed description of the method of making an electrically conductive polysulfone - silver ink which constitutes a preferred embodiment of the invention . it should be apparent that proportions and times can be varied . it should also be appreciated that the conductive layers of the aforementioned humidity sensor can also be made using the techniques explained hereafter , substituting the carbon black , for example , for the silver flakes . the preferred procedure for making the composition of the present invention begins by cleaning a glass bottle , preferably a bottle having a cover lined with teflon ®. two foil measuring dishes are then cleaned with a suitable solvent , such as acetone , for subsequent use in the measuring of certain constituents . the glass bottle and its cover are placed on a balance and tared . an initial quantity of butyrophenone is transferred with an automatic volumetric dispenser in a fume hood and the cover is placed on the bottle . the bottle , with contents , is now weighed , and the weight of the solvent is determined . the next step is to weigh the desired amount of silver flake , using one of the aluminum foil dishes , and the silver flake is added to the glass bottle containing the butyrophenone . the second foil dish is balanced and tared and a first predetermined quantity of polysulfone powder is then weighed using the procedures for the other two constituents . the polysulfone powder is then added to the glass bottle containing the butyrophenone and silver flake . the next step in the process constitutes placing the sealed bottle on a ball mill and rotating the bottle on the ball mill for a predetermined amount of time . in my most preferred embodiment , i rotate the bottle on the ball mill for at least twenty - four ( 24 ) hours . after mixing , the bottle is removed from the ball mill and placed back in the fume hood . a third foil dish is cleaned with a solvent , balanced and tared , and the second predetermined amount of polysulfone powder is added to the dish and its weight is recorded . this additional quantity of polysulfone powder is added to the glass bottle and the bottle is sealed . the second mixing step , again for a predetermined time , is undertaken . the speed of rotation on the ball mill used to prepare test samples for the development of the present invention was approximately 15 - 20 rpm . following completion of this step , the viscosity of the polysulfone - silver ink is measured at room temperature , using a brookfield rvt viscometer , with a 13 r small adapter chamber and a no . 27 spindle at 5 rpm . several of the steps , including those which involve handling of butyrophenone and silver flake are conducted carefully to avoid operator contact and are conducted in a fume hood due to potential toxicity problems with these two components . care should be exercised to avoid inhaling or touching the silver flake or inhaling fumes from the butyrophenone . care should also be undertaken to avoid heat around silver dust , as it is a flammable solid and is reactive in air . preferably , it should be stored under nitrogen . it should be noted that in the manufacturing process described above , the polysulfone is added in two steps . the purpose of the first addition is to provide sufficient polysulfone in the solution to keep the conductive particles in suspension . the amount of polysulfone in the first step must also be sufficiently low to maintain a low solution viscosity so the particles can be dispersed uniformly in the polysulfone / butyrophenone solution . a butyrophenone - polysulfone ratio that provides an adequate initial solution viscosity and keeps the particles in suspension during mixing is approximately 16 . 67 mls / gram . the ink compositions listed in table i below have this ratio . the total amount of silver flake added must be kept sufficiently low to maintain an initial low solution viscosity to permit the silver flake dispersion . however , the amount of silver flake must also be sufficiently high to provide a printed and fused polysulfone - silver ink that has good electrical conductivity . the second addition of polysulfone achieves the desired final viscosity for the illustrative polysulfone - silver ink , and during the second mixing step ( after the second addition of polysulfone ) the polysulfone gradually dissolves and the viscosity of the ink increases . the relatively low rotational speed allows the added polysulfone to uniformly mix in the ink as it dissolves . a number of parameters influence the viscosity of the polysulfone - silver ink . these include the silver flake shape and size , the amount of silver flake dispersed in the ink , how well the flake is dispersed , the amount of polysulfone in the solution and the molecular chain length of the polysulfone . since so many parameters influence the final ink viscosity , it is important to measure the ink &# 39 ; s viscosity to verify the quality of the process . the second addition of resin also results in an adjustment of the silver flake to polysulfone ratio and increases the viscosity of the initial polysulfone - silver ink so that the finished ink can be readily screen printed . the amount of polysulfone added influences the electrical conductivity of the printed and fused ink , and greatly affects the strength of the adhesive bond between the fused ink and the polyimide dielectric layer . table ii below shows the electrical properties obtained with six test solutions . good electrical conductivity and a strong bond occur with a silver flake to polysulfone weight ratio of 4 . 5 / 1 . 0 . the electrical resistivity and thickness of the printed and fused polysulfone - silver inks contained in table i are listed in this table ii . an ink viscosity between 20 , 000 - 40 , 000 cps is suitable for screen printing , and an ink viscosity of 25 , 000 ± 5 , 000 cps is desirable so that a relatively thin contact can be used when a 325 mesh stainless steel screen is employed having 0 . 0005 inch emulsion thickness . my preferred solutions of those described in the two tables are those listed as number 5 and 6 , having a viscosity of approximately 24 , 000 cps . the adhesion of the inks prepared according to the above procedures and in the ratios shown in table i was tested by using scotch ® tape pressed over the fused polysulfone - silver inks . after fusion to a upilex ® r polyimide film ( 0 . 0003 inch ) and to polysulfone matrix conductive layers , the fused polysulfone - silver ink layer was not released from the substrate when the scotch ® tape was pulled off the fused ink . set forth below in table i are six ( 6 ) ink solutions prepared according to the techniques of the present invention , all having the 4 . 5 : 1 ratio referred to above . the conductive particle to resin ratio could vary between about 0 . 1 : 1 to about 10 : 1 . also , while the table lists compositions wherein the initial / final resin ratio is from about 0 . 15 : 1 to 0 . 20 : 1 , that ratio could fluctuate from about 0 . 01 : 1 to about 0 . 8 : 1 . table i__________________________________________________________________________polysulfone - silver ink formulations final inkink composition to secondinitially disperse silver flake silver total additionsolutionbutyrophenone silver flake polysulfone flake - polysulfone ratio polysulfone polysulfone__________________________________________________________________________1 25 . 0 mls 42 . 75 g 1 . 5 g 4 . 5 9 . 5 g 8 . 0 g2 25 . 0 mls 39 . 375 g 1 . 5 g 4 . 5 8 . 75 g 7 . 25 g3 25 . 0 mls 36 . 0 g 1 . 5 g 4 . 5 8 . 0 g 6 . 5 g4 25 . 0 mls 33 . 75 g 1 . 5 g 4 . 5 7 . 5 g 6 . 0 g5 50 . 0 mls 67 . 5 g 3 . 0 g 4 . 5 15 . 0 g 12 . 0 g6 50 . 0 mls 67 . 5 g 3 . 0 g 4 . 5 15 . 0 g 12 . 0 g__________________________________________________________________________ set forth in table ii below are the electrical characteristics of the six solutions shown in table 1 and also showing the prior art material ( p2313 ) determined experimentally and as shown in the technical information bulletin . these fused inks were made using a 325 mesh stainless steel screen having a 0 . 0005 inch emulsion thickness , printing a resistor pattern on a 0 . 0003 inch thick polyimide film , and fusing the ink at 250 ° c . for 30 minutes in an oven . table ii______________________________________electrical characteristics electrical electrical resistivity , thickness , resistivity , solution ω /□ inch ω /□/ 0 . 001______________________________________ inch1 0 . 061 0 . 00024 0 . 0152 0 . 062 0 . 00021 0 . 0133 0 . 056 0 . 00022 0 . 0124 0 . 070 0 . 00022 0 . 0155 0 . 062 0 . 00019 0 . 0126 0 . 064 0 . 00021 0 . 013emca - remex 0 . 076 0 . 00018 0 . 013p2313 experimentalemca - remex 0 . 030polymer conductor ( tech . inf . sheet ) p2313______________________________________ while the present invention has been described in detail in connection with certain preferred embodiments , the invention is not to be limited thereby but is to be limited solely by the scope of the claims which follow .