in the practice of the present invention , the wood product is first placed under vacuum for a predetermined period to remove air . as used herein , the term &# 34 ; wood product &# 34 ; refers to products produced from solid wood such as veneers , boards , dowels and similar items shaped from solid wood . preferably , the wood products to be treated have a moisture content below 20 percent by weight . impregnation of the wood product is achieved more readily when the wood is dry , but complete dryness is not essential for the process . as schematically illustrated in fig1 the wood product is subject to a vacuum of from about 5 mm . hg . to about 15 mm . hg . for a period of from about 1 to 30 minutes . the amount of vacuum as well as the period during which the wood product is subjected to the vacuum can , however , be varied above and below these limits . while still under vacuum , the wood product is then immersed in a solution of hexanediol diacrylate ( hdda ) or hexanediol dimethacrylate ( hddma ) monomer and a polymerization initiator alone , or in combination with a flame or fire retardant such as chlorinated wax . a thermally activated polymerization initiator suitable for use in the practice of the present invention is 2 , 2 &# 39 ;- azobis -( 2 - methylbutyronitrile ), commercially available from dupont under the trade designation vazo 67 . additionally , a dye , stain or other colorant can be added to the solution in an amount of 3 to 10 percent by volume . the temperature of the monomer solution can be from 20 degrees up to 60 degrees c . preferably , the wood is immersed in the solution for a period ( soak time ) sufficient to allow the polymer to absorb between about 30 % to about 80 % of monomer solution , based upon the weight of the untreated wood . in the case of veneers the soak time is preferably from about 5 to about 40 minutes . the soak time may , however , be varied above and below these limits depending upon the particular species of wood and the shape of the wood product . finally , the wood product is removed from the monomer solution and then heated under pressure to cure or polymerize the monomer . the temperature of the press can be from 90 to 180 degrees c . the duration of time in the press ( cure time ) for complete polymerization depends primarily on the temperature of the press and typically ranges from about 3 to about 10 minutes in the case of veneers . again , the cure time may vary above and below these limits depending upon the particular species of wood and the shape of the wood product . depending on the type and size of the wood product to be treated , and the total processing to a final product , different process alternatives can be adopted . wood in the form of veneers is a typical wood product amenable to treatment with the process of the present invention . thicker wood materials can also be used in this process if the vacuum and atmospheric soaking times are extended . in some applications , such as multiple layer laminated wood veneers , it may be desirable to further increase resistance to fire . if this is the case , fire retardancy can be further improved by treating the wood product with an aqueous solution of water soluble inorganic fire retardants , such as boric acid , diammonium phosphate , or ammonium borate . as illustrated in fig2 in one embodiment of the present invention , a veneer 1 may be treated with an inorganic fire retardant such as diammonium phosphate prior to treatment with the monomer solution . the veneer may then be laminated to additional layers 2 - 5 of veneer . in another embodiment of the present invention , as illustrated in fig3 a layer of veneer 7 treated with an inorganic fire retardant such as diammonium phosphate may be placed under a top ply 6 that has been treated with the monomer solution . additionally , treatment with a fire retardant such as a chlorinated wax may be combined with the monomer treatment . the treated wood product of the present invention exhibits greatly improved indent resistance as compared to untreated wood of the same type . as used herein , &# 34 ; indent resistance &# 34 ; is measured by the depth of an indentation formed when a wood product is tested with a gardner impact apparatus with a indent force of 50 inch - lbs . thus , lower values reflect higher indent resistance . the present invention is believed to have several advantages over the prior art in treating wood products . the present invention provides : ( 1 ) a harder wood product than is presently used for flooring which may be treated to enhance its fire retardancy ; ( 2 ) a wood product with uniform hardness throughout its surface ; ( 3 ) with the addition of a dye or stain , a uniform color throughout the surface of the wood product ; and ( 4 ) a practical , economical method of hardening a wood product which uses less volatile chemicals and may be accomplished in less time than prior art methods . the invention will be further described with respect to the following examples ; however , the scope of the invention is not to be limited thereby . northern red oak veneers were placed in a vacuum chamber and subjected to a vacuum of 9 mm hg . for 15 minutes . the veneers of this and the following examples ranged from approximately 0 . 10 to 0 . 25 inches in thickness . while maintaining the vacuum , monomer was introduced into the chamber to cover the veneers . the vacuum was then released to return the pressure to atmospheric . the veneers were kept in the monomer for 30 minutes before they were removed and cured in a heated press at 100 ° to 120 ° c . and 200 psi for 3 to 4 minutes . the monomers used were hexanediol diacrylate ( hdda ), hexanediol dimethacrylate ( hddma ) and methyl methacrylate ( mma ). each monomer contained 0 . 5 % vazo 67 as a polymerization initiator . specimens were treated separately with each of the monomer solutions and indent resistance of the veneers was determined using a gardner impact apparatus . an indent force of 50 inch - lbs was used to conduct the tests . each test was repeated approximately 25 times . the results of treatment were as follows : table 1______________________________________indentation resistance of oak veneers treated with differentmonomers polymer load average indentationmonomer (%) ( inch ) ______________________________________hdda 46 - 48 0 . 014 - 0 . 018hddma 43 - 45 0 . 015 - 0 . 026mma 13 - 22 0 . 022 - 0 . 026______________________________________ the foregoing example illustrates the superior results obtained through the use of hdda or hddma as compared to mma . as illustrated in example 1 , polymer absorption was approximately twice as great for hdda and hddma as opposed to mma under the same process conditions . indent resistance was also greater for the veneers containing hdda and hddma than for the veneers containing mma . northern red oak veneers were treated separately with hdda and hddma by the method described in example 1 , except the method was varied to obtain a range of polymer loadings . the veneers were tested for indent resistance and the results are shown in table 2 . table 2______________________________________indention resistance of treated oak veneers to different polymerloadingspolymer load average indentation (%) ( inch ) ______________________________________0 0 . 04016 0 . 03033 0 . 02643 0 . 02048 0 . 018______________________________________ the foregoing example demonstrates the relationship between polymer loading and indent resistance . as polymer loading increases , indent resistance also increases . northern red oak veneers were treated separately with hdda and hddma , including 0 . 5 % vazo 67 as a polymerization initiator , by the method described in example 1 to a treatment weight gain of 48 percent . the indentation resistance of earlywood and latewood was measured . the results are shown in table 3 below : table 3______________________________________indentation resistance of earlywood and latewood of oak veneers average indentiontype of wood ( inch ) ______________________________________earlywood 0 . 019 - 0 . 025latewood 0 . 018 - 0 . 022______________________________________ the foregoing example illustrates the uniform degree of hardness imparted to wood products treated in accordance with the present invention . northern red oak veneers were treated separately with hdda and hddma , including 0 . 5 % vazo 67 as a polymerization initiator , as in example 1 , except the vacuum time was varied to determine the effect of vacuum time on polymer loading . the veneers were also allowed to soak for varying periods to determine the effect of soak time on polymer loading . the samples were tested for polymer loading and the results are set forth in table 4 below : table 4______________________________________vacuum time and soak time vs . polymer loadingvacuum time soak time polymer loading ( minutes ) ( minutes ) (%) ______________________________________0 30 165 30 3510 30 4315 30 4815 5 3715 10 4215 15 4215 20 4515 30 5330 15 4830 300 56______________________________________ northern red oak veneers were treated separately with hdda and hddma , including 0 . 5 % vazo 67 as a polymerization initiator , and placed in a heated press at 100 ° c . and 200 psi for varying amounts of time to determine the effect of heating time on the polymerization of the monomer . to determine whether polymerization occurred , a thermocouple was placed in the press with the sample . since the polymerization process is exothermic , a temperature rise above the press temperature indicated that the polymerization reaction was occurring . the results are set forth in table 5 below : table 5______________________________________time required to polymerize monomer in oak veneers . time ( min ) polymerized______________________________________0 no1 no2 no3 no4 yes5 yes______________________________________ northern red oak veneers were placed in a vacuum chamber subjected to a vacuum of 9 mm hg . for 15 minutes . while maintaining the vacuum , monomer was introduced into the chamber to cover the veneers . the vacuum was then released to return the pressure to atmospheric conditions . the veneers were kept in the monomer for 30 minutes before they were removed and cured in a press at 100 to 120 ° c . and 200 psi for 3 to 4 minutes . the monomer solutions used were hdda and hddma with varying amounts of a chlorinated wax . each monomer contained 0 . 5 % vazo 67 as a polymerization initiator . specimens were treated separately with each of the monomer solutions and indent resistance of the veneers was determined using a gardner impact apparatus . an indent force of 50 inch - lbs was used . the test results are set forth in table 6 below : table 6______________________________________indentation resistance of oak veneers treated with solutions ofhdda and hddma with chlorinated waxratio of hdda or hddma average indentationto chlorinated wax ( inches ) ______________________________________85 : 15 0 . 02175 : 25 0 . 01770 : 30 0 . 019______________________________________ the foregoing example illustrates that a flame retarding agent , such as a chlorinated wax , may be incorporated into the monomer solution without adversely affecting the ability of the solution to harden wood . northern red oak veneers treated as in examples 1 and 6 were laminated to untreated veneers to form 5 ply boards , the treated veneer being the top veneer . the boards were then tested for flame spread in accordance with astm e162 . the results are set forth in table 7 below : table 7______________________________________flame spread on polymer treated oak veneers . monomertreatment flame spread (%) ______________________________________hdda 118hddma 114hdda or hddma with 9415 % chlorinated waxhddma with 25 % 82chlorinated waxhdda or hddma with 8530 % chlorinated wax______________________________________ northern red oak veneers , treated as in example 6 , were laminated to 4 additional layers of red oak veneer and tested for flame spread . in the first test , the top ply was first treated with diammonium phosphate followed by the monomer treatment . in the second test , the top ply was monomer treated and the second ply was treated with diammonium phosphate . the boards were then tested for flame spread in accordance with astm e162 . the results are set forth in table 8 below : table 8______________________________________flame spread on polymer treated oak veneers . monomertreatment flame spread (%) ______________________________________top veneer treated with 85diammonium phosphatefollowed by treatment withhdda or hddma with30 % chlorinated waxtop veneer treated with 55hdda or hddma with30 % chlorinated wax , second veneer treated withdiammonium phosphate______________________________________ northern red oak veneers were treated separately with mixtures of hdda and hddma with 30 % chlorinated wax as in example 6 . the veneers were then tested for indentation resistance of earlywood and latewood . the results are set forth in table 9 below : table 9______________________________________indentation resistance of earlywood and latewood of oak veneers average indentiontype of wood ( inch ) ______________________________________earlywood 0 . 019 - 0 . 026latewood 0 . 016 - 0 . 022______________________________________ northern red oak veneers were treated separately with hdda and hddma , including 0 . 5 % vazo 67 as a polymerization initiator and 30 % chlorinated wax , using varying vacuum times to determine the effect of vacuum time on polymer loading . the veneers were also allowed to soak for varying periods to determine the effect of soak time on polymer loading . the samples were tested for polymer loading and the results are set forth in table 10 below : table 10______________________________________vacuum time and soak time vs . polymer loadingvacuum time soak time polymer loading ( minutes ) ( minutes ) (%) ______________________________________0 30 175 30 3810 30 4315 30 4815 5 3815 10 4415 15 4415 20 4515 30 57______________________________________ northern red oak veneers were treated separately with hdda and hddma , including 0 . 5 % vazo 67 as a polymerization initiator and 30 % chlorinated wax , and placed in a heated press at 100 ° c . and 200 psi for varying amounts of time to determine the effect of varying heating times on the polymerization of the monomer . to determine whether polymerization occurred , a thermocouple was placed in the press with the sample . since the polymerization process is exothermic , a temperature rise above the press temperature indicated that the polymerization reaction was occurring . alternatively , visual inspection of the surface of the veneer for liquid monomer also indicated whether polymerization had occurred . the test results are set forth in table 11 below : table 11______________________________________time required to polymerize monomer in oak veneers . time ( min ) polymerized______________________________________0 no1 no2 no3 no4 yes5 yes______________________________________ several hardwood and softwood veneers were treated as described in example 1 with and without 30 percent chlorinated wax , with and without a 3 percent addition of a colorant . the monomer solution contained 0 . 5 % vazo 67 as a polymerization initiator . specimens were treated separately and following polymerization , indent resistance of the veneers was determined using a gardner impact apparatus . an indent force of 50 inch - lbs was used . the results are shown in table 12 . table 12______________________________________indentation resistance of different wood treated veneers average polymer indentation untreatedwood load (%) ( inch ) control______________________________________pecan 70 0 . 012 0 . 028ash 65 0 . 014 0 . 030cherry 70 0 . 011 -- maple 60 0 . 010 0 . 025mahogany 70 0 . 014 -- pine 70 0 . 015 0 . 039spruce 70 0 . 017 0 . 039______________________________________ while the particular embodiments of the present invention have been described , it will be apparent to those skilled in the art that various changes and modifications can be made without departing from the spirit and scope of the invention . the following claims are intended to cover all such modifications that are within the scope of the invention .