in accordance with this invention , the characteristics of bags made from ethylene polymers , particularly from hdpe , lldpe or mixtures thereof can be improved by blending up to about 10 weight percent , preferably up to about 8 weight percent , and most preferably between about 3 and 8 weight percent of a thermoplastic aromatic polymer . the linear ethylene polymers which are suitable for use in this invention are those now commercially prepared by low pressure techniques . but development is active in the preparation of linear copolymers under high pressure with coordination catalysts and the like . such linear polymers are also suitable for use in this invention . many suitable linear ethylene polymers are commercially available . particularly suitable are lldpe resins which are copolymers of ethylene and higher olefins , particularly 1 - butene , 1 - hexene , and 1 - octene . these lldpe copolymers generally have a density of between 0 . 90 and 0 . 94 , preferably between 0 . 9 and 0 . 93 . polystyrene and poly ( para - methylstyrene ) resins are particularly suitable as the aromatic polymer which is blended with the ethylene polymer . polymers in which the aromatic monomer is the predominant constituent , such as high impact polystyrene and styrene copolymers are also suitable . the best tear strength is obtained with blends in which the linear ethylene polymer itself has good tear properties . such blends result in films with good tear and impact properties , and the higher modulus characteristic of a higher density lldpe film . the linear ethylene polymer can be blended with other compatible polymers providing that the linear polymer is the major constituent of the blend . for example , ldpe high pressure polymer is suitable in such blends . compatibilizers can be used in small amounts up to about 2 weight percent of the composition but are not necessary . suitable compatibilizers include block copolymers of styrene - ethylene propylene - styrene ( kraton g ), block copolymers of styrene and ethylene ( shelvis ) and ethylene propylene copolymers ( vistalon 3707 ). for purposes of ease of blending and control on a commercial scale it is preferred that the lldpe and the aromatic polymer be the sole polymeric components . the resin blends and bags are made in the conventional manner . preferably , the bags are made from films obtained by blown film extrusion using conventional techniques to obtain films which are generally from about 0 . 2 l to 5 mils in thickness . this invention finds particular utility in the production of bags having a thin gauge which are commonly dispensed from rolls in supermarket produce sections , for example . it is a common experience to find these bags difficult to open and this difficulty is reduced by using the polymer blends of this invention . but the invention is by no means limited to bags supplied on rolls . it is also advantageous in the production of the larger bags usually having handles and gussetts which are in widespread use at supermarket checkout counters . these bags are commonly supplied in packs of 50 or more bags attached to a tear - off tab fitted to a dispenser device for holding the bag open during loading . bags of this type are disclosed in u . s . pat . no . 4 , 165 , 832 which is incorporated herein by reference . as previously indicated blending of the lldpe resin and the aromatic polymer is done in the conventional manner . blending can be accomplished by melting the polymers into pellets for future extrusion or by feeding a mixture of the two polymers directly to the extruder . the latter may be preferable in commercial operations because the separate operation of melt blending and its attendant expense is eliminated . antiblock agents such as diatomaceous earth ( silica ) are commonly used in bag compositions . these agents often have deleterious effects on the physical properties of bag films . it is an anticipated advantage of this invention that conventional anti - block agent can be reduced or eliminated and replaced in whole or in part with the aromatic polymer . the aromatic polymer , when used in proper amounts has a beneficial effect on important physical propeties such as md tear strength and stiffness , and provides the unexpected improvement in anti - block characteristics contributing to easier opening . in addition to the improvements apparent in the final bags due to the incorporating of aromatic polymer , improvements in processing have been noted . for example , in post - gussetting operations in which a tube blown film is flattened and reblown to introduce gussets difficulty is often encountered in the reblowing step due to blocking of the films causing non - uniform gussets and other problems . these problems are reduced by using the blends of this invention . the following non - limiting examples are illustrative of this invention . unless otherwise noted all parts are by weight . a compounded blend of 95 % lldpe ( ethylene - 1 - hexene copolymer , mi 0 . 7 , density 0 . 922 ) and 5 % polystyrene ( mobil ps 1240 ) was produced by feeding both materials into an intensive mixer ( bolling mill ) at the correct ratio , melting and mixing both polymers together such that an intimate mixture was obtained , then feeding the molten mass to a pelletizer , thus producing pellets . these pellets were cooled and stored several weeks . the pellets were subsequently made into film suitable for producing grocery sacks by the blown film process . similarly produced pellets of the lldpe without polystyrene were also made into film in an identical manner . in a second run pellets of the identical polystyrene were blended with pellets of the lldpe in the blown film extruder hopper in the proper ratio and immediately made into film suitable for grocery sacks . films from both experiments were tested for 1 % secant modulus ( stiffness ) and for tensile impact ( spittiness ). ______________________________________ td tensileexam - blend md 1 % secant impactple film method modulus ( psi ) ( ft - lb ) ______________________________________c - 1 . 100 % lldpe melt 37000 0 . 461 . 95 % lldpe / melt 48500 0 . 52 5 % ps1240 % increase 31 15 ( 1 ) vs ( c - 1 ) c - 2 . 100 % lldpe dry 46200 0 . 272 . 95 % lldpe / dry 55000 0 . 47 5 % ps1240 % increase 19 76 ( 2 ) vs ( c - 2 ) ______________________________________ the bags made in accordance with this invention are demonstrably easier to open than the corresponding bags containing no aromatic polymer . the ease of opening has been associated at least in part to a reduced tendency to block in standard quantitative blocking tests . the increased stiffness of the blends is also believed to contribute to the ease of opening . although the present invention has been described with preferred embodiments , it is to be understood that modifications and variations may be resorted to , without departing from the spirit and scope of this invention , as those skilled in the art will readily understand . such modifications and variations are considered to be within the purview and scope of the appended claims .