in fig1 reference numeral 2 indicates generally a furnace assembly in which a heating zone is established within a cylindrical heating chamber 4 . chamber 4 is positioned immediately above a pair of tunnels or tubes 6 supported by base plates 8 . the purpose of the tunnels 6 will be described in great detail later herein . chamber 4 is formed of several layers of insulative material 10 which surround a graphite susceptor 12 and are held thereto by straps on ties 14 . the top of chamber 4 is covered by an insulative disk - shaped cover 16 having an opening therein for receiving a pouring cup 18 while the bottom of chamber 4 is enclosed by an insulative cover 19 having a hole formed through the center thereof . a ceramic shell mold 20 for producing a desired object , such as a turbine blade , is positioned within heating chamber 4 . generally , the mold 20 has a thickness of from about 0 . 10 to 0 . 25 inches or so , and is produced by well known techniques used for the manufacture of shell molds in precision investment castings . mold 20 has an open ended cavity and riser into which molten metal is introduced via pouring cup 18 . the interior of chamber 4 is heated to a high temperature by suitable means such as induction coil 22 although other heating means such as an electrical resistance heating element can be used . it will be seen from fig1 that an insulative blanket material 30 is contained within tunnels 6 and is urged towards the adjacent ends of tunnels 6 by plungers 32 . any suitable electromechanical or mechanical drive means , including spring biasing means , may be coupled to plungers 32 to cause the insulative blanket material 30 to move within tunnels 6 . a sufficient gap is provided between the abutting ends of tunnels 6 to permit the blanket insulative material 30 to exit therefrom . in addition , tunnels 6 have curved portion 24 which together form a curved opening which conforms to the largest radial excursion of mold 20 and is of sufficient size to permit mold 20 to be withdrawn from the heating chamber 4 . in fig2 mold 20 is seen to be positioned on top of a water cooled pull rod 38 , which may be lowered by mechanical or electromechanical means of conventional design and construction . the end of pull rod 38 adjacent mold 20 functions as a chill block for mold 20 . cooling water is introduced into the interior of pull rod 38 via tube 40 and the cooling water flows in the direction of the arrows shown within tube 40 . it is apparent from fig2 that insulative blanket material 30 is pressed up against pull rod 38 and prevents heat from radiating from heating chamber 4 . further , that insulative blanket material 30 approaches the mold at right angles to and from below the heating chamber 4 . as such it does not take a path adjacent the hot parts of the heating chamber 4 , as is the case in the apparatus of the sawyer patent , supra . thus sintering of the insulative material at higher temperatures is avoided . insulative blanket material 30 is preferrably an alumina blanket fiber material . one such alumina blanket material is distributed by the babcock and wilcox company under the name saffil , a registered trademark of imperial chemicl industries limited for inorganic fiber . it is noteworthy that at 2400 degrees f ., the saffil blanket possesses an approximate four times insulation advantage over the alumina bubbles used in the prior art sawyer device . fig3 illustrates a later stage in the process . as mold 20 is lowered by the downward motion of pull rod 38 , there is also motion of the insulative blanket material 30 downward and about the surface of mold 20 at the critical area adjacent base plates 8 where mold 20 leaves the furnace assembly . an improved optical density is achieved since the insulation blanket material 30 completely engulfs mold 20 . this may not occur in other systems if mold dimensions change drastically , as in the platform areas of turbine blades . it will be appreciated that the invention is not limited to the specific details shown in the illustrations and that modifications may be made within the ordinary skill in the art without departing from the spirit and scope of the invention .