the benzoxazine monomers readily polymerized by the cationic initiator disclosed later are monobenzoxazine and polybenzoxazine compounds generally having the general formula wherein n can be any integer from 1 to 20 and is preferably an integer from 1 to 4 and is most preferably 1 or 2 and r 1 can be hydrogen , one or more groups selected from hydroxyls , one or more linear or branched alkyls of 1 to 80 and more preferably 1 to 10 carbon atoms , aromatics , alkyl substituted aromatics , aromatic substituted alkyls of 6 or 20 carbon atoms , mono or poly fluorine substituted alkyls of 1 to 20 carbon atoms , mono or poly fluorine substituted compound having at least 1 aromatic ring and 6 to 20 carbon atoms , and phenolic compounds of 6 to 20 carbon atoms ( for thc purpose of this specification phenolic compounds may have more than one hydroxyl group as defined in chemical dictionaries ) including poly phenolic compounds having on average 6 to 20 carbon atoms per phenol group . when n is 2 , 3 or 4 , r 1 can be selected from the connecting groups below depending on whether phenolic or phenoxy repeat units are desired in said polybenzoxazine , it may be desirable that r 1 be ortho , meta or para to the oxygen atom of the benzoxazine monomer of formula a . further r 2 may be an alkyl of 1 to 40 carbon atoms , an aromatic , an alkyl substituted aromatic or aromatic substituted alkyl of 6 to 40 carbon atoms , mono or poly fluorine substituted alkyl of 1 to 20 carbon atoms , a mono or poly fluorine substituted compound having at least one aromatic ring and 6 to 20 carbon atoms or an amine of 1 to 40 carbon atoms including polyamines and aromatic , alkyl substituted aromatic , or aromatics substituted alkyls having 6 to 40 carbon atoms . furthermore , each benzene ring , as shown by ( r 3 ), where p is an integer from 0 to 3 and r 3 is as defined later , can have more than one substituent of the same structure or a mixture of the r 3 structures . the variable m can be an integer from 0 to 5 and r 3 can be h or r 2 . preferably r 3 is not the amine or polyamine components of r 2 . preferably r 3 is an alkyl of 1 to 9 carbon atoms such as ch 3 , c 2 h 5 , c 3 h 7 or c 4 h 9 , or a mono or poly fluorinated alkyl of 1 to 9 carbon atoms such as cf 3 , c 2 f 5 , c 3 f 7 . these r 1 compounds are well known to those familiar with phenolic compounds . generally r 1 can be any of the known connecting groups than interconnect two or more phenols . known connecting groups refers to those which are present in commercially available phenols , are in experimentally available phenols , and phenols whose synthesis are described in the published literature . examples of such phenols include as the cationically initiated ring opening polymerization of monofunctional benzoxazines generally results in linear polymers , it is desirable that at least 25 mole percent , more desirably at least 50 mole percent and preferably at least 75 mole percent or 90 mole percent of the r 1 groups are not an additional hydroxyl groups or a phenolic or polyphenolic compound and n in formula a is 1 . also desirably at least 25 mole percent , more desirably at least 50 percent , still more desirably at least 75 or 90 mole percent of the r 2 groups are neither polyamines nor include additional benzoxazine compounds . these limitations are desirable for thermoplastic polybenzoxazines but it is understood that if thermoset polybenzoxazines are desired the amount of difunctional or polyfunctional benzoxazine monomers ( those where n is 2 to 20 or r 2 is a polyamine or includes additional benzoxazine rings ) could be higher . when high molecular weight thermoplastic polybenzoxazines are desired , desirably the number average molecular weight of said polybenzoxazine is at least 5 , 000 and more desirably at least 10 , 000 . as is well known , benzoxazine monomers arc made from the reaction of three reactants , aldehydes , phenols , and primary amines by procedures using a solvent or known as solventless systems . u . s . pat . no . 5 , 543 , 516 , hereby incorporated by reference , sets forth a generally solventless method of forming benzoxazine monomers . an article by ning and ishida in journal of polymer science , chemistry edition , vol . 32 , page 1121 ( 1994 ) sets forth a procedure using a solvent which can be used to prepare benzoxazine monomers . the procedure using solvents is generally common to the literature of benzoxazine monomers . the preferred phenolic compounds are phenol or cresol but can include diphenols ( e . g . bisphenol - a ), triphenols , etc ., e . g . polyphenols , wherein each phenolic group in the phenolic compound has on average about 6 to about 20 carbon atoms per phenol group . the use of phenols with two or more hydroxyl groups reactive in forming benzoxazines may result in branched and / or crosslinked products . the groups connecting said phenolic groups into a phenol can be branch points or connecting groups in the polybenzoxazine . the aldehydes used to form the benzoxazine can be any aldehyde but preferably the aldehydes are those having from about 1 to about 10 carbon atoms with formaldehyde being highly preferred . the amine used to form the benzoxazine can be an aromatic amine aliphatic amine , alkyl substituted aromatic or aromatic substituted alkyl amine . the amine can also be a polyamine , although the use of polyamines will , under some circumstances , yield polyfunctional benzoxazine monomers . polyfunctional benzoxazine monomers are more likely to result in branched and / or crosslinked polybenzoxazines than monofunctional benzoxazines , which would be anticipated to yield thermoplastic polybenzoxazines . the amines generally have from about 1 to abut 40 carbon atoms unless they include aromatic rings and then the may have from about 6 to about 40 carbon atoms . the amine of di or polyfunctional may also serve as a branch point to connect one polybenzoxazine to another . in the past , thermal polymerization has been the preferred method for polymerizing benzoxazine monomers . the temperature to induce thermal polymerization is typically varied from about 150 to about 300 ° c . the polymerization is typically done in bulk but could be done from solution or otherwise . catalyst , such as carboxylic acids , have been known to slightly lower the polymerization temperature or accelerate the polymerization rate at the same temperature . cationic polymerization initiators described in this invention have been found to result in polymerization of benzoxazine monomers at temperatures as low as cryogenic temperatures . preferred temperatures are from about − 100 ° c . to about 200 ° c . and m - ost preferably between about − 60 and 150 ° c . for ease of handling the reactants and products . some of the cationic initiators , e . g . pcl 5 , form repeating units , from the benzoxazine monomers , that include a salt of the amine . these repeating units have better solubility in polar solvents , e . g . water than similar repeating units without the amine salt . the initiators of the current invention can be used either in the benzoxazine melt or in the presence of solvent , allowing the solvent content to be from 0 % to nearly 100 %. many solvents can be used in cationic polymerizations and its selection is known by those skilled in the art of cationic polymerization . the polymers from the cationically initiated polymerization of benzoxazine are useful as molded articles with good thermal stability and / or flame resistance such as molded circuit boards , flame resistant laminates , other molded articles and is a source of precursor to high temperature resistant chars . the common uses for high temperature resistant chars include aircraft brake discs , equipment for sintering reactions , and heat shields or heat shielding material . the polymers which include repeating units having amine salts can be used in applications for partially or fully water soluble polymers such as viscosity control agents . generally given optimal reaction conditions , cationic initiators can polymerize benzoxazine monomers or oligomers . these include h 2 so 4 , hclo 4 , bf 3 , alcl 3 , t - bucl / et 2 alcl , cl 2 / bcl 3 , albr 3 , albr 3 . ticl 4 , i 2 , sncl 4 , wcl 6 , alet 2 cl , pf 5 , vcl 4 , aletcl 2 , and bf 3 et 2 o . preferred initiators include pcl 5 , pcl 3 , pocl 3 , ticl 5 , sbcl 5 , ( c 6 h 5 ) 3 c + ( sbcl 6 ) − , metallophorphyrin compounds such as aluminum phthalocyanine chloride which are all known to result in similar polymers from cationically initiated polymerization of unsaturated monomers . methyl iodide ( a covalent initiator ), butyl lithium ( an ionic initiator ), and benzoyl peroxide ( a radical initiator ) were not effective at polymerizing experimental benzoxazine monomers . methyl tosylate , methyl triflate and triflic acid appear to cationically polymerize the experimental benzoxazine monomers , although the polymers did not precipitate from solution . typically each initiator initiates a polymer with from about 3 to about 1 , 000 to 3 , 000 repeat units so the amount of initiator needed on a mole percent basis relative to the monomer is small . however , additional initiator is needed to compensate for loss due to adventitious moisture and other reactants that deactivate cations , that may be present in the monomers solvents , etc . desirably about 0 . 001 to about 50 mole percent initiator based upon the monomer and more desirably from about 0 . 01 to about 10 mole percent initiator is used for these cationically initiated polymerizations . several factors have been found to change the structure of the benzoxazine polymers prepared by cationic polymerization . these factors include polymerization temperature , the particular cationic initiator and competing reactivity between the ortho - carbon of the benzene ring and the basic nitrogen atom of the oxazine ring . for example the following results were obtained with pcl 5 as the initiator at − 60 ° c . and 40 ° c . thus the formation of a phenolic repeating ) unit having an amine salt therein occurs preferentially to this kind of monomer ( monoparasubstituted benzene ring other than the two sites occupied by the oxazine ring ) at low temperatures ( e . g . − 60 ° c .) with a pcl 5 initiator . a phenoxy repeating unit occurs more frequently at 40 ° c . than at − 60 ° c . but still is not the exclusive repeating unit . the amine salt form of the phenolic repeating unit causes an increased water solubility . further at − 60 ° c . the availability or reactivity of a ortho ch position also affects the relative ratio of phenolic to phenoxy repeat units . steric hindrance around the ortho ch position or a substituent in the ortho cl position favors a phenoxy structure from the benzoxazine while the absence of steric hindrance and absence of an ortho substituent favors a phenolic structure . a unified theory to explain the above is that there is a competition between the reactivity of the aromatic carbon ( ortho with respect to the oxygen ) and the basic nitrogen atom of the ( o — ch 2 — n ( r 2 ) ch 2 ). when substitution on the aromatic ring is in such a way that it reduces the reactivity of the ring ortho carbon , the protonation or alkylation of the nitrogen dominates and a phenoxy structure results . however , if the ortho ch position ( with respect to the o ) is open and no bulky substituent offers steric hindrance ., the ring reactivity dominates and a phenolic structure at low temperatures is the result . in summary it is anticipated that at − 60 ° c . if i ) aromatic ring reactivity dominates then a phenolic repeating structure is obtained and if ii ) oxazine ring reactivity dominates then a phenoxy repeating structure is obtained and that monomers given below will result in an increased probability of the repeating structures given . as phenolic repeat units from benzoxazine are now available from lower temperature cationic polymerizations , it is desirable to distinguish the resulting polymer from thermally polymerized benzoxazine polymers . desirably the number average molecular weight of polymers from cationically polymerized monofunctional benzoxazine monomers are at least 2 , 000 or 5 , 000 . desirably the cationically polymerized benzoxazine when both phenolic and phenoxy structures result has at least 2 , 5 , 10 or 15 or at least 50 , 80 , or 90 mole % repeating units of the phenoxy structures . however , the pure phenolic structure when the molecular weight is above 2 , 000 or 5 , 000 is not excluded . five benzoxazine monomers were used for most of the experimentation on cationically initiated polymerization . they were ba - a monomer and c - m monomer . different chemical structures for two of the monomers are shown below . ba - a monomer is made from the reaction of bisphenol a , formaldehyde , and aniline . c - m monomer is made from the reaction of cresol , formaldehyde and methylamine . c - m monomer was prepared according to the procedure set forth by ning and ishida in journal of polymer science , chemistry edition , vol . 32 , page 1121 ( 1994 ). the polymerization solvents used were 1 , 2 - dichloroethane , 1 , 2 - dichlorobenzene , chloroform , or deuterated chloroform . all the solvents were dried by conventional methods and distilled under argon . the cationic initiators used in table 1 were purchased from aldrich chemical company and used without further purification . all solvents and reactants were stored in a dry box unless refrigeration was required . the moisture was usually less than 1 ppm in the dry box . table 1 below shows polymerizations , which were ran for about 20 - 80 hours using the specified variety of cationic and other initiators . table 1 sets forth the results of polymerizations of ba - a monomer . while run numbers 8 , 9 , and 11 did not yield any insoluble polymer , the solutions turned deep red and a tough red polymer was recovered when the solvent was evaporated . the initiator amount was typically about 5 mole percent based upon the amount of benzoxazine monomer . several of the polymers polymerized according to the condition set forth in table 1 were analyzed by thermogravimetric analysis ( tga ) or differential scanning calorimity ( dsc ). the glass transition temperature ( tg ) is used to characterize a particular polymer and microstructure . the char yield is affected by many factors , a high char yield is typically desired for precursors for char or for non - flammable polymers . as can be seen in table 2 the first four cationic initiators yielded polymers from benzoxazine having significantly higher tg &# 39 ; s than the last sample which was a control ( thermally cured ) polybenzoxazine from the same monomer . the char yield from the polymers initiated with the first four cationic initiators varied from about 44 or 49 to about 62 weight percent based upon the weight of the initial starting polybenzoxazine . this was significantly higher than the control which yielded only about 29 weight percent char under identical conditions . the next three cationic initiators ( 5 - 7 ) yielded polymers with slightly different tg &# 39 ; s than the control . the char yield from the fifth through the seventh cationic initiator was also different than that of the control although the difference from the control amount was not as significant as with the first four cationic initiators , it is to be noted that the polymer from the methyl tosylate , methyl triflate , and triflic acid had a different color ( red ) than the polymers from the first four cationic initiators . the polymers from the cationic polymerization of benzoxazine monomer ba - a were analyzed by fourier transform infrared spectroscopy along with a thermally cured polybenzoxazine from the same monomer . these results indicated substantially similar infrared spectra when bisphenol a based benzoxazine was used . the polymers compared to the monomer showed the dramatic change in the peaks in the region of 1 , 000 to 1 , 350 cm − 1 , arising from the ch 2 wagging ( 1327 cm − 1 and 1305 cm − 1 ), c — o — c asymmetric stretching ( 1233 cm − 1 ), c — n — c asymmetric stretching ( 1159 cm − 1 ), and c — o — c symmetric stretching ( 1031 cm − 1 ) of the oxazine ring , respectively , as well as the decrease of the peak resolution , indicate the opening of the oxazine ring and the polymerization of the monomer into oligomers and polymers . there are significant spectral differences between the thermally polymerized polybenzoxazine and the pcl 5 initiated polybenzoxazines . in the spectrum of ba - a monomer the peaks centered at 1500 cm − 1 and 949 cm − 1 are major characteristics of the tri - substituted benzene ring in the benzoxazine structure , corresponding to the in - plane c — c stretching and the out - of - plane c — h deformation of tri - substituted benzene ring , respectively . these two peaks almost disappear in the thermally polymerized polybenzoxazine spectrum , meanwhile a new peak centered at 1489cm − 1 , representing tetra - substituted benzene ring mode , appears . the results are in accordance with the well accepted thermal polybenzoxazine structure shown as below . however , with some cationic initiators , here pcl 5 has been chosen as an example , these two peaks at 1500 cm − 1 and 949 cm − 1 remain unaffected except for the peak broadening , which indicates that in the polybenzoxazine structure obtained , the majority of the benzene rings should still be trisubstituted instead of tetrasubstituted . further nmr results are in support of this hypothesis . polymers for size exclusion chromatographic ( sec ) analysis were cationically polymerized from the ba - a monomer using chloroform as a solvent at about 23 ° c . using pcl 5 initiator and a mole ratio of 1 : 100 initiator : monomer . portions of the reactants were withdrawn after 1 , 2 , 2 . 5 , 3 . 5 , 5 , and 7 hours of reactions and poured into an excess of methylol to cause precipitation . the precipitated material was recovered and analyzed by sec for differences in molecular weight as a function of reaction time . as is well known in sec analysis , short retention times indicate higher molecular weight while long retention times indicate lower molecular weight . a peak at 29 . 3 minutes was associated with the benzoxazine monomer . a new peak occurred between 21 and 29 minutes as the polymerization occurred . simultaneously the peak at 29 . 3 minutes decreased in size . this is consistent with theories on polymerization . an nmr experiment was conducted comparing polymer from a cationic polymerization , using pcl 5 as the initiator in deuterated chloroform as a solvent , to a thermally polymerized polymer . the reaction temperature for the cationic polymerization was 40 ° c ., the reactor was a sealed nmr tube , and the material was evaluated after 10 minutes , 30 minutes . i hour , and 2 hours to see which nmr peaks were being generated or depleted as the monomer was cationically polymerized . the monomer peaks at 2 . 6 , 3 . 9 , and 4 . 75 ppm gradually disappeared while new peaks at 1 . 95 , and 3 . 65 ppm appeared and a broadening of the peak at 2 . 2 ppm occurred indicating less molecular rearrangement occurred on going from monomer to polymer under cationic conditions . based on these results ( proton nmr ) along with carbon 13 nmr and ftir results the repeat structure of the thermally polymerized polymer in these studies is theorized to be predominantly tetrasubstituted phenolic structure , e . g . while the cationically polymerized samples is predominantly the phenoxy repeating units of the structure in conclusion the experimental data indicates the cationically initiated polymerization benzoxazine monomers can occur at substantially lower temperatures than thermal polymerization and produces polymers of different microstructure than thermal polymerizations . further these polymers can have substantially higher char yields 62 \ 29 or an increase of 200 percent over the char yield of the thermally polymerized polymers . the polymers from benzoxazines are useful as precursors for char yielding material ( e . g . precursors to aircraft brake pads ). they are also useful as temperature and flame resistant polymers for electrical components , planes , cars , buses , etc . while in accordance with the patent statutes the best mode and preferred embodiment has been set forth , the scope of the invention is not limited thereto , but rather by the scope of the attached claims .