before the present technology is described in greater detail below with reference to fig2 through 7 , the present state of the art is presented with reference to fig1 . fig1 illustrates a known wear - resistant coating 10 , which is applied to an outer surface of a gas turbine component 11 . the wear - resistant coating 10 in fig1 has a multilayered structure , and consequently is horizontally segmented . the multilayered or horizontally segmented wear - resistant coating 10 has multiple relatively hard ceramic layers 12 , 13 , 14 , 15 , and 16 , as well as multiple relatively soft metallic layers 17 , 18 , 19 , 20 , and 21 . the ceramic layers 12 through 16 and the metallic layers 17 through 21 are each alternatingly positioned on top of one another in such a way that a metallic layer 18 or 19 or 20 or 21 is respectively provided between adjacent ceramic layers 12 and 13 , or 13 and 14 , or 14 and 15 , or 15 and 16 . an external layer 16 of the wear - resistant coating 10 , which forms an outer surface of the wear - resistant coating , is designed as a ceramic layer . in contrast , an internal layer 17 of the wear - resistant coating which is applied to the surface of the gas turbine component 11 is designed as a metallic layer . in the wear - resistant coating 10 , according to fig1 known from the current state of the art , all relatively hard ceramic layers 12 through 16 as well as all relatively soft metallic layers 17 through 21 are designed as compact or dense self - contained layers . such wear - resistant coatings known from the current state of the art are relatively sensitive to erosion because they are not able to easily absorb the energy acting thereon during , for example , particle erosion attack . instead , such wear - resistant coatings form cracks over large surface areas , such that after a relatively brief initiation phase , the wear - resistant coating known from the current state of the art begins to flake off over a large surface area . fig2 shows a first exemplary embodiment of a wear - resistant coating 22 according to the present technology which is applied to a gas turbine component 23 . the wear - resistant coating 22 in fig2 once again has multiple relatively hard ceramic layers 24 , 25 , 26 , and 27 as well as multiple relatively soft metallic layers 28 , 29 , 30 , and 31 . the relatively hard ceramic layers 24 through 27 and the relatively soft metallic layers 28 through 31 are applied to the gas turbine component 23 in alternation on top of one another , specifically in such a way that a metallic layer 29 or 30 or 31 is respectively provided between two adjacent ceramic layers 24 and 25 , or 25 and 26 , or 26 and 27 . an external layer 27 which forms an outer surface of the wear - resistant coating 22 is designed as a ceramic layer . an internal layer 28 which is applied directly to the gas turbine component 23 is designed as a metallic layer . in the wear - resistant coating 22 according to the presently described technology , at least the external ceramic layer 27 which forms the outer surface of the wear - resistant coating is vertically segmented in the manner of a column . in the exemplary embodiment of fig2 , all of the ceramic layers 24 , 25 , 26 , and 27 , including the external ceramic layer 27 , are vertically segmented in the manner of a column . columns 32 which are separated from one another by interfaces 33 are thus formed inside each of the ceramic layers 24 through 27 . in the exemplary embodiment of fig2 , the interfaces 33 extend between the columns 32 of all the ceramic layers 24 through 27 which are vertically segmented in the manner of a column , approximately perpendicular to the surface of the gas turbine component . thus , in the exemplary embodiment of fig2 the columns 32 of all ceramic layers 24 through 27 which are segmented in the manner of a column have the same orientation , with the columns 32 of all ceramic layers 24 through 27 which are segmented in the manner of a column extending perpendicular to the surface of the gas turbine component 23 , and therefore not being inclined relative to the surface of the gas turbine component 23 . as a result of the above - described columnar segmentation of at least the external ceramic layer 27 of the wear - resistant coating 22 , the forces acting on the wear - resistant coating 22 during particle erosion attack , for example , may be easily absorbed . spreading of microcracks produced by particle erosion attack , for example , is hindered by the interfaces 33 . in this manner , any flaking of the external layer 27 of the wear - resistant coating 22 is limited to very small spatial areas , such that the wear - resistant coating 22 according to the presently described technology has good erosion resistance . fig3 shows in additional detail the wear - resistant coating 22 in the region of the external ceramic layer 27 , which forms the outer surface of the wear - resistant coating 22 and is vertically segmented in the manner of a column . thus , the layer 27 according to fig3 is structured as a columnar pillar . alternatively , the external ceramic layer as well as any other layer that is segmented in the manner of a column may be structured as , for example , a columnar rod or as a columnar fiber . fig4 shows a layer 27 a structured as a columnar rod . fig5 shows a layer 27 b structured as a columnar fiber . in the exemplary embodiment of fig2 , the relatively soft metallic layers 28 , 29 , 30 , and 31 are designed as compact , dense layers which are therefore vertically unsegmented . the metallic layers 28 through 31 may also optionally be segmented in the manner of a column . in addition , it is possible for only a portion of the metallic layers to be segmented in the manner of a column . fig6 shows a further exemplary embodiment of a wear - resistant coating 34 according to the present technology which is applied to a gas turbine component 35 . the wear - resistant coating 34 of the exemplary embodiment of fig6 has multiple relatively hard ceramic layers 36 , 37 , 38 , and 39 as well as multiple relatively soft metallic layers 40 , 41 , 42 , and 43 , which once again , are applied to the gas turbine component 35 in alternation on top of one another . in the exemplary embodiment of fig6 , only two ceramic layers are vertically segmented in the manner of a column , namely , the external layer 39 which forms the outer surface of the wear - resistant coating 34 , and the ceramic layer 38 adjoining the external layer 39 with introduction of the metallic interlayer 43 . in contrast , the two internal ceramic layers 36 and 37 are vertically unsegmented , but have a nanocrystalline structure . in the ceramic layers 38 and 39 , which are vertically segmented in the manner of a column , once again , multiple columns 44 are provided which are separated from one another by interfaces 45 . in the exemplary embodiment of fig6 , the columns 44 and therefore the interfaces 45 , the same as in the exemplary embodiment of fig2 , extend approximately perpendicular to the surface of the gas turbine component , and in the exemplary embodiment of fig6 , the columns 44 or interfaces 45 therefore , are not inclined relative to the gas turbine component . in the exemplary embodiment of fig6 , the external ceramic layer 39 , which is vertically segmented in the manner of a column , has a nanostructured design . detail x in fig6 shows that in the illustrated exemplary embodiment the external layer 39 has a nanostructured design . according to detail x , multiple nanolayers 46 are positioned on top of one another , with the nanolayers 46 extending essentially horizontally and having a thickness of & lt ; 1 μm . thus , for example , nanolayers 46 made of different materials may be alternatingly positioned on top of one another , so that the ceramic layer 39 itself , which is vertically segmented in the manner of a column , is also horizontally segmented by the nanolayers 46 . as an alternative or in addition to the nanolayered structuring of the external ceramic layer 39 , said layer may have a nanocrystalline design . the individual nanolayers 46 may also be produced from nanograded materials . fig7 shows a further exemplary embodiment of a wear - resistant coating according to the present technology , wherein in principle , the wear - resistant coating of fig7 has the design of the wear - resistant coating of fig2 . thus , to avoid unnecessary repetition in the exemplary embodiment of fig7 , the same reference numerals are used as for the exemplary embodiment of fig2 . therefore , the discussion below addresses only the details according to which the exemplary embodiment of fig7 differs from the exemplary embodiment of fig2 . the exemplary embodiment of fig7 differs from the exemplary embodiment of fig2 in that the ceramic layers 24 through 27 are vertically segmented in the manner of a column in such a way that , with introduction of a respective metallic interlayer 29 or 30 or 31 , successive ceramic layers 24 and 25 , or 25 and 26 , or 26 and 27 are vertically segmented with different orientations in the manner of a column . fig7 shows that the columns 32 and thus the interfaces 33 of the ceramic layer 27 which is segmented in the manner of a column are inclined relative to the surface of the gas turbine component 23 in a different direction than the columns 32 of the ceramic layer 26 which is also segmented in the manner of a column . thus , in the exemplary embodiment of fig7 , the columns of the ceramic layers which are successively positioned with the introduction of a metallic interlayer are inclined in different directions relative to the surface of the gas turbine component , this inclination being observed in three - dimensional space . the columns of adjacent layers which are segmented in the manner of a column may have a difference in orientation , i . e ., a difference in inclination , between 0 ° and 180 °, preferably between 5 ° and 120 °. for a difference in orientation of 0 °, the columns of adjacent layers which are segmented in the manner of a column extend with the same orientation with respect to the surface of the gas turbine component . in the exemplary embodiment of fig7 , the columns 32 may have practically any given angle relative to the surface of the gas turbine component 23 . successive ceramic layers which are separated from one another by a metallic layer are inclined in different directions . as a result of these differences in orientation , for a given external stress , the development of tension in the individual layers of the wear - resistant coating may be influenced in a targeted manner . this is another advantage of the presently described technology . finally , it is noted and will be appreciated by those familiar with the art that a bonding layer may be provided between the wear - resistant coating 22 or 34 according to the presently described technology and the gas turbine component 23 or 35 on which the wear - resistant coating 22 or 34 according to the present technology is applied . the wear - resistant coating according to the invention is preferably produced by the physical vapor deposition ( pvd ) sputtering technique . the present technology has now been described in such full , clear , concise and exact terms as to enable a person familiar in the art to which it pertains , to practice the same . it is to be understood that the foregoing describes preferred embodiments and examples of the present technology and that modifications may be made therein without departing from the spirit or scope of the invention as set forth in the claims . moreover , while particular elements , embodiments and applications of the present technology have been shown and described , it will be understood , of course , that the present technology is not limited thereto since modifications can be made by those familiar in the art without departing from the scope of the present disclosure , particularly in light of the foregoing teachings and appended claims . moreover , it is also understood that the embodiments shown in the drawings , if any , and as described above are merely for illustrative purposes and not intended to limit the scope of the invention , which is defined by the following claims as interpreted according to the principles of patent law , including the doctrine of equivalents . further , all references cited herein are incorporated in their entirety .