in the preferred practice of the method of the present invention , polysulfur in the rubbery state is blended with the compatible diluent , which is rubber , by mixing the rubbery polysulfur and the diluent on a two roll rubber mill and continuing the blending or mastication until a uniform blend is obtained . the amount of the rubbery polysulfur which is used is preferably enough to produce a uniform blend which contains about 40 % to about 80 % of the polysulfur as based on the total weight of the blend . the rubbery polysulfur can be prepared by any known manner . it is known that at about 113 degrees c . and above , sulfur melts . the molten sulfur begins to polymerize as the temperature is raised to about 159 degrees c . this is evidenced by a pronounced increase in viscosity . as the temperature is further increased , the viscosity increases sharply to a maximum in a rise of only a few degrees . it then drops off at a fairly steady rate as the temperature is still further increased . it is believed that the mean chain length is at its maximum at the point of maximum viscosity , and that the mean chain length decreases as the temperature rises further . the higher viscosities apparently have not been shown to inversely correlate with the percent of unpolymerized sulfur present . the purer the sulfur , the higher is the maximum viscosity . the curve of the viscosity versus temperature of pure sulfur is reversible if the temperature changes are gradual . this reversibility does not necessarily hold true when other substances , such as certain organic compounds or halogens , are present in small amounts . in pure sulfur , the end of the polymer chain is a free radical . when these other substances are present , either purposefully or accidentally , the free radical is probably “ capped ” by the other substances . however , for purposes of this application the term “ polysulfur ” is intended to cover the just - described capped polymers . if the molten sulfur is cooled gradually from the temperature of maximum viscosity , the drop in viscosity is attributed to the reversion of the polysulfur to predominantly s 8 . other sulfur molecules , notably s 6 , but others from s 2 to s 23 have been identified . when the molten sulfur is cooled rapidly from temperatures whereat a significant portion of the sulfur is polymeric , the polymeric form survives to a metastable form , which is rubbery , at room temperature . in pure sulfur , the polymer reverts to predominantly s 8 in a relatively short time . this reversion is hindered by the presence of halogens or certain other substances , and seems to be accelerated by the presence of moisture , or alkalinity . upon rapid cooling , the molten polysulfur forms a rubbery mass of rubbery polysulfur , which hardens by itself upon standing . this hardening does not necessarily indicate de - polymerization , or reversion . certain treatments can accelerate this hardening . the compatible diluent which is blended with the rubbery polysulfur to form the blends of the present invention can be any substance which is compatible with both the rubbery polysulfur and the polymer which is to be vulcanized with the blend . representative diluents include natural and synthetic rubbers , soaps , petroleum fractions , waxes , wood tar products and plasticizers , such as ethers and esters and their polymers . the method of preparing the blends can be any of those described herein , as well as other methods which can be used to form sufficiently uniform blends . in the following examples 1 to 6 , several techniques are described which demonstrate the wide variety of sulfur conversion processes that can be used in the practice of this invention . one part of bromine is added to one hundred parts of sulfur in a glass retort . heat is applied to melt and is then vaporize the sulfur . when the distillate runs in a steady stream , which must be a very thin stream , it is run into a pot of ice water which is rotating at forty - five rpm . it is collected until the stream becomes unsteady , which indicates that it will soon break . the sulfur forms a rubbery mass of strings in the ice water . it is removed from the ice water , and shook to remove most of the water . the remaining water is blown off with compressed air . the rubbery polymeric sulfur is then blended with an equal amount of natural rubber , the compatible diluent , on a two roll mill . an excellent uniform blend of the polysulfur and the rubber is obtained . the procedure of example 1 is repeated except in place of 1 part bromine , 0 . 8 parts of bromine and 0 . 2 parts of iodine are used . an excellent uniform blend of the polysulfur and the rubber is obtained . the procedure of example 2 is repeated , but the distillate of polysulfur is run directly into the nip of a cooled two roll rubber mill upon which the rubber , the compatible polymer , has already been banded and has formed a rolling nip . an excellent uniform blend of the polysulfur and the rubber is obtained . one hundred parts of sulfur and 0 . 25 parts of bromine are melted in a beaker and heated to a point ( e . g . 200 degrees c .) above the maximum viscosity of the sulfur to form a liquid . the liquid is slowly poured into a rotating ice water bath to form rubbery polysulfur which after isolation is blended with rubber , the compatible diluent , as in example 1 . an excellent uniform blend of the polysulfur and the rubber is obtained . the procedure of example 4 is repeated except that the molten liquid sulfur is fed into the compatible diluent , rubber , in the nip of the rollers , as in example 3 . an excellent uniform blend of the polysulfur and the rubber is obtained . one hundred parts of sulfur and one part of iodine are melted in an aluminum dish on a hotplate and heated to spontaneous combustion . the molten sulfur is sprayed with a hot spray gun onto a cool aluminum sheet to form a thin coating of rubbery polysulfur . the coating is peeled from the aluminum sheet , and laminated with a thin sheet of broken down rubber , the compatible diluent . the laminate is rolled up and passed through the nip of a two roll rubber mill . the mixture is cross rolled several times and banded on the mill . an excellent uniform blend of the polysulfur and the rubber is obtained . the uniform blends prepared as described in examples 1 - 6 can be used as vulcanizing agents for sulfur vulcanizable polymers . the vulcanizing agents can be readily and uniformly dispersed in the polymer to be vulcanized . the resulting products are free of defects caused when sulfur is not uniformly dispersed in the compound . if it is desired to initially keep selected ingredients apart , such as the sulfur and accelerator , two or more intermediate batches could be mixed separately , and later blended together , to give the desired finished batch formulation . typical recipes for accomplishing this would be : batch a and batch b are each mixed . after cooling , they are blended in proportion to their batch weight to give the same finished batch as in the formula immediately above . 95 parts of sulfur and 5 parts of selenium are melted together and heated to 260 ° c . upon rapid cooling , a rubbery mass is formed . this is then blended with rubber . an excellent dispersion of this polysulfur , which contains selenium , is obtained . as previously described , the rubbery polysulfur used to make the blends may be prepared by any known method and it may or may not contain the atoms of the sulfur homologs of group vi b of the periodic table of the elements , notably selenium and tellurium . however , it also has been found that if rubbery polysulfur is treated , either after it is formed , or as it is formed , with a solvent for soluble sulfur , such as carbon disulfide , a chlorinated hydrocarbon , an aromatic hydrocarbon , or other suitable solvent , it is possible to dissolve out some or substantially all of the soluble sulfur present . as a result , the polysulfur content of the rubbery mass can thereby be increased on a percentage basis . as a result , blends prepared from polysulfur thus treated contain less soluble or normal sulfur . it will be apparent to those skilled in the art that a number of modifications and changes can be made without departing from the spirit and scope of the invention . therefore , the invention is not to be limited except by the claims .